EN 10163-2-2004 en Delivery requirements for surface condition of hot-rolled steel plates wide flats and sections - Part 2 Plate and wide flats《热轧钢板 宽钢带与型材表面状态交付要求 第2部 分板材和宽带材》.pdf

《EN 10163-2-2004 en Delivery requirements for surface condition of hot-rolled steel plates wide flats and sections - Part 2 Plate and wide flats《热轧钢板 宽钢带与型材表面状态交付要求 第2部 分板材和宽带材》.pdf》由会员分享，可在线阅读，更多相关《EN 10163-2-2004 en Delivery requirements for surface condition of hot-rolled steel plates wide flats and sections - Part 2 Plate and wide flats《热轧钢板 宽钢带与型材表面状态交付要求 第2部 分板材和宽带材》.pdf（14页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD BS EN 10163-2:2004 Delivery requirements for surface condition of hot-rolled steel plates, wide flats and sections Part 2: Plate and wide flats The European Standard EN 10163-2:2004 has the status of a British Standard ICS 77.140.50 BS EN 10163-2:2004 This British Standard was publi

2、shed under the authority of the Standards Policy and Strategy Committee on 16 December 2004 BSI 16 December 2004 ISBN 0 580 45120 8 National foreword This British Standard is the official English language version of EN 10163-2:2004. It supersedes BS EN 10163-2:1991 which is withdrawn. The UK partici

3、pation in its preparation was entrusted to Technical Committee ISE/12, Structural steels, which has the responsibility to: A list of organizations represented on this committee can be obtained on request to its secretary. Cross-references The British Standards which implement international or Europe

4、an publications referred to in this document may be found in the BSI Catalogue under the section entitled “International Standards Correspondence Index”, or by using the “Search” facility of the BSI Electronic Catalogue or of British Standards Online. This publication does not purport to include all

5、 the necessary provisions of a contract. Users are responsible for its correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. aid enquirers to understand the text; present to the responsible international/European committee any enquiries on

6、 the interpretation, or proposals for change, and keep the UK interests informed; monitor related international and European developments and promulgate them in the UK. Summary of pages This document comprises a front cover, an inside front cover, the EN title page, pages 2 to 10, an inside back cov

7、er and a back cover. The BSI copyright notice displayed in this document indicates when the document was last issued. Amendments issued since publication Amd. No. Date Comments EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 10163-2 December 2004 ICS 77.140.50 Supersedes EN 10163-2:1991 English

8、 version Delivery requirements for surface condition of hot-rolled steel plates, wide flats and sections - Part 2: Plate and wide flats Conditions de livraison relatives ltat de surface des tles, larges plats et profils en acier lamins chaud - Partie 2: Tles et larges plats Lieferbedingungen fr die

9、Oberflchenbeschaffenheit von warmgewalzten Stahlerzeugnissen (Blech, Breitflachstahl und Profile) - Teil 2: Blech und Breitflachstahl This European Standard was approved by CEN on 4 November 2004. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the condition

10、s for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the Central Secretariat or to any CEN member. This European Standard exists in three offi

11、cial versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the official versions. CEN members are the national standards bodies of Austria,

12、Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATIO

13、N COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: rue de Stassart, 36 B-1050 Brussels 2004 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 10163-2:2004: EEN 10163-2:2004 (E) 2 Contents Page Foreword

14、3 1 Scope 4 2 Normative references 4 3 Terms and definitions .4 4 General4 5 Classification4 6 Requirements.5 6.1 Depth and affected area of discontinuities .5 6.2 Repair requirements5 6.2.1 Class A5 6.2.2 Class B6 6.3 Repair procedures .6 6.3.1 General6 6.3.2 Grinding 7 6.3.3 Welding .8 Annex A (in

15、formative) Classes and subclasses for surface conditions with their respective requirements 10 EN 10163-2:2004 (E) 3 Foreword This document (EN 10163-2:2004) has been prepared by Technical Committee ECISS/TC 10 “Structural steels Grades and qualities”, the secretariat of which is held by NEN. This E

16、uropean Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by June 2005, and conflicting national standards shall be withdrawn at the latest by June 2005. This document supersedes EN 10163-2:1991, Delivery requiremen

17、ts for surface condition of hot-rolled steel plates, wide flats and sections Part 2: Plates and wide flats. This series of standards consists of the following parts, under the general title Delivery requirements for surface condition of hot-rolled steel plates, wide flats and sections: Part 1: Gener

18、al requirements Part 3: Sections. During the 5 year review of EN 10163-2:1991 the members of ECISS/TC 10 agreed to revise EN 10163-2:1991. It was asked to bring the text in line with ECISS DOCS N 809 “Iron and steel standardization Model for a product standard”. Also the range of dimensions from EN

19、10025-2, which is increased from 250 mm to 400 mm is incorporated in this new edition. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Cyprus, Czech Republic, Denmark,

20、Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EN 10163-2:2004 (E) 4 1 Scope In addition to EN 10163-1 this document specifies

21、 the delivery requirements which apply to the surface condition of hot-rolled plates and surface condition of the faces of wide flats with thicknesses of 3 mm t 400 mm. NOTE For plates with a thickness 400 mm special agreements should be made at the time of the order. 2 Normative references The foll

22、owing referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 10029, Hot rolled steel plates 3 mm thick or above - T

23、olerances on dimensions, shape and mass. EN 10051, Continuously hot-rolled uncoated plate, sheet and strip of non-alloy and alloy steels - Tolerances on dimensions and shape. EN 10163-1:2004, Delivery requirements for surface condition of hot-rolled steel plates, wide flats and sections Part 1: Gene

24、ral requirements. 3 Terms and definitions For the purposes of this document, the following terms and definitions apply. 3.1 imperfections for flat products surface discontinuities other than cracks, shell and seams with a depth and/or area equal to or less than a specified limiting value 3.2 defects

25、 for flat products surface discontinuities with a depth and/or area greater than a specified limiting value and all cracks, shell and seams irrespective of their depth or/and area 4 General In addition to the conditions stated in EN 10163-1, it applies that if the purchaser needs to be sure that all

26、 discontinuities visible to the naked eye have been identified, assessed and where necessary repaired before delivery, products should be ordered descaled (see Clause 4 of EN 10163-1:2004). 5 Classification The surface requirements and repair conditions are subdivided into 2 classes and each class i

27、s further subdivided into 3 subclasses: Class A The surface condition shall comply with the requirements of 6.2.1 and 6.3.2.2. The remaining thickness of the affected area under discontinuities and of repaired ground areas may be less than the minimum thickness as specified in the appropriate tolera

28、nce standard. EN 10163-2:2004 (E) 5 Class B The surface condition shall comply with the requirements of 6.2.2 and 6.3.2.3. The remaining thickness of the affected area under discontinuities and of repaired ground areas shall not be less than the minimum thickness as specified in the appropriate tole

29、rance standard. Subclass 1 Repair by chipping and/or grinding followed by welding is permitted in compliance with 6.3.3.2. Subclass 2 Repair by welding is only permitted if agreed at the time of the order and under agreed conditions (see 6.3.3.3). Subclass 3 Repair by welding is not allowed. The req

30、uired class and subclass is specified in the appropriate material or product standard. If this is not the case the class and subclass shall be class A and subclass 1 unless otherwise specified at the time of the order. 6 Requirements 6.1 Depth and affected area of discontinuities The requirements of

31、 EN 10163-1 apply. 6.2 Repair requirements 6.2.1 Class A 6.2.1.1 Imperfections 6.2.1.1.1 Discontinuities other than cracks, shell and seams (see 6.2.1.2.3) not exceeding the limits of Table 1 are regarded as being inherent of the manufacturing process and are permissible irrespective of their number

32、. A surface area with discontinuities within the limits of Table 1 but with a remaining thickness under the discontinuities less than the minimum thickness as specified in EN 10029 and EN 10051 is permissible with a maximum of 15 % of the inspected surface. Table 1 Maximum permissible depth of imper

33、fections Dimensions in millimetres Nominal thickness of the product t Maximum permissible depth of imperfections 3 t 8 0,2 8 t 25 0,3 25 t 40 0,4 40 t 80 0,5 80 t 250 0,7 250 t 400 1,3 EN 10163-2:2004 (E) 6 6.2.1.1.2 Discontinuities other than cracks, shell and seams (see 6.2.1.2.3) with a depth exc

34、eeding the limits of Table 1 but not exceeding the limits of Table 2 and of which the sum of the affected areas does not exceed 5 % of the inspected surface, may be left unrepaired. In this case is a surface area with a remaining thickness under the discontinuities less than the minimum thickness as

35、 specified in EN 10029 and EN 10051 permissible with a maximum of 2 % of the inspected surface. Table 2 Maximum permissible depth of discontinuities Dimensions in millimetres Nominal thickness of the product t Maximum permissible depth of discontinuities 3 t 8 0,4 8 t 25 0,5 25 t 40 0,6 40 t 80 0,8

36、80 t 150 0,9 150 t 250 1,2 250 t 400 1,5 6.2.1.2 Defects 6.2.1.2.1 Discontinuities with a depth exceeding the limits of Table 1 but not exceeding the limits of Table 2, but with an affected surface area of more than 5 % of the inspected surface shall be repaired. 6.2.1.2.2 Discontinuities with a dep

37、th exceeding the limits of Table 2 shall be repaired irrespective of their number. 6.2.1.2.3 Discontinuities such as cracks, shell and seams which are in general deep and sharp, and therefore impair the use of the products, shall always be repaired irrespective of their depth and number. 6.2.2 Class

38、 B The requirements of 6.2.1.1 and 6.2.1.2 apply except that the remaining thickness under the discontinuities and repair ground areas shall not be less than the minimum permissible thickness as specified in the appropriate European Standards specifying tolerances. 6.3 Repair procedures 6.3.1 Genera

39、l In addition to the requirements of EN 10163-1 the following apply. EN 10163-2:2004 (E) 7 6.3.2 Grinding 6.3.2.1 Introduction The producer shall be allowed to repair the entire surface by grinding to the minimum thickness specified in the appropriate European Standards specifying the dimensional re

40、quirements. Grinding of defects shall be carried out subject to the following conditions. 6.3.2.2 Class A 6.3.2.2.1 The maximum permissible depth of ground areas is given in Table 3 and 4 respectively. Table 3 Maximum permissible depth of ground areas with a maximum of 15 % of the inspected area Dim

41、ensions in millimetres Nominal thickness of the product t Permitted grinding depth allowances below the minimum thickness as specified in EN 10029 and EN 10051 3 t 8 0,3 8 t 15 0,4 15 t 25 0,5 25 t 40 0,6 40 t 60 0,7 60 t 80 0,8 80 t 150 1,0 150 t 250 1,2 250 t 400 1,4 EN 10163-2:2004 (E) 8 Table 4

42、Maximum permissible depth of ground areas not exceeding 2 % of the inspected area Dimensions in millimetres Nominal thickness of the product t Permitted grinding depth allowances below the minimum thickness as specified in EN 10029 and EN 10051 3 t 8 0,4 8 t 15 0,5 15 t 25 0,7 25 t 40 0,9 40 t 60 1,

43、1 60 t 80 1,3 80 t 150 1,6 150 t 250 1,9 250 t 400 2,2 6.3.2.2.2 When the depth of the ground area is less than indicated in Table 3, a surface area with a remaining thickness under the ground area less than the minimum thickness as specified in EN 10029 and EN 10051 is permissible with a maximum of

44、 15 % of the inspected surface. 6.3.2.2.3 When the depth of the ground area exceeds the limits given in Table 3 but is less than indicated in Table 4, the sum of all ground areas below the minimum permissible thickness of one side of the product shall not exceed 2 % of the inspected surface area. Fo

45、r products of surface area greater than 12,5 m 2the size of a single ground area below the minimum permissible thickness shall not exceed 0,25 m 2 . 6.3.2.2.4 For the remaining thickness of two ground areas lying opposite to each other on both sides of the product the requirements of Table 4 apply.

46、6.3.2.3 Class B The remaining thickness of the repaired ground area shall not be under the minimum permissible thickness as specified in the appropriate European Standards specifying tolerances. 6.3.3 Welding 6.3.3.1 General The following conditions apply for the repair by welding of defects which c

47、annot be repaired by grinding as stated under 6.3.2. 6.3.3.2 Subclass 1 A single welded area shall not exceed 0,125 m 2and the sum of the welded areas shall not exceed 0,125 m 2or 2 % of the surface area under inspection whichever is the greater. EN 10163-2:2004 (E) 9 Ground and welded areas which a

48、re separated by a distance less than their average width shall be treated as a single area for the purpose of determining the limiting area. 6.3.3.3 Subclass 2 Repair by welding is only allowed if agreed at the time of the order. In this case requirements different from 6.3.3.2 can be specified. 6.3

49、.3.4 Subclass 3 Repair by welding is not allowed. EN 10163-2:2004 (E) 10 Annex A (informative) Classes and subclasses for surface conditions with their respective requirements In Table A.1 the classes and subclasses for surface conditions are given with their respective requirements. Table A.1 Classes and subclasses for surface conditions with their respective requirements Remaining thickness of re