BS HC 10-1974 Specification for nickel-chromium-molybdenum steel castings (1150-1300 MPa)《镍-铬-钼-钢铸件(1150-1300MPa)规范》.pdf

《BS HC 10-1974 Specification for nickel-chromium-molybdenum steel castings (1150-1300 MPa)《镍-铬-钼-钢铸件(1150-1300MPa)规范》.pdf》由会员分享，可在线阅读，更多相关《BS HC 10-1974 Specification for nickel-chromium-molybdenum steel castings (1150-1300 MPa)《镍-铬-钼-钢铸件(1150-1300MPa)规范》.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD AEROSPACE SERIES CONFIRMED JULY 1982 BSHC 10:1974 (Superseding, in part, Ministry of Defence specifications DTD705 and DTD5072) Incorporating Amendment No.1 Specification for Nickel-chromium- molybdenum steel castings (11501300MPa) UDC629.7:669.1524262814BSHC10:1974 This BritishStan

2、dard, having been approved by the AerospaceIndustry StandardsCommittee, waspublished under theauthoritythe ExecutiveBoard on 10May1974 BSI02-2000 The following BSI references relate to the work on this standard: Committee reference ACE/60 Draft for comment72/35126 DC ISBN 0 580 08402 7 A British Sta

3、ndard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front cover

4、, an inside front cover, pagesi andii, pages1 and2 and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside front cover. Amendments issued since publication Amd. No. Date of issue Comme

5、nts 3847 May 1982 Indicated by a sideline in the marginBSHC10:1974 BSI 02-2000 i Contents Page 1 Special foundry approval 1 2 Inspection and testing procedure 1 3 Chemical composition 1 4 Condition 1 5 Heat treatment 1 6 Mechanical properties 1 7 Rectification of defects 2ii blankBSHC10:1974 BSI 02-

6、2000 1 1 Special foundry approval Manufacture of castings to this specification may be restricted to foundries specially approved in accordance with the requirements of BSHC100, Section 1. 2 Inspection and testing procedure This BritishStandard shall be used in conjunction with the relevant sections

7、 of the latest issue of BSHC100 as follows: 3 Chemical composition The re-melting stock and the castings shall contain: 4 Condition Castings shall be supplied finally heat treated. 5 Heat treatment The final heat treatment shall be as follows. 5.1 Annealing. Heat uniformly at a temperature between88

8、0 C and960 C. 5.2 Hardening. Heat uniformly at a temperature between830 C and910 C and quench in oil. 5.3 Tempering. Heat uniformly at a temperature between450 C and560 C. 6 Mechanical properties 6.1 Tensile and impact. The tensile and impact properties obtained from test pieces representing casting

9、s, selected, prepared and tested in accordance with the relevant requirements of BSHC100, shall be: NOTEInformation on SI units is given in BS3763, “The International System of units (SI)”, and BS350, “Conversion factors and tables”. Re-melting stock Sections1 and2 Precision castings Sections1 and3

10、Sand castings Sections1 and4 Centrifugal castings Sections1 and5 Element % min. max. Carbon Silicon Manganese Phosphorus Sulphur Chromium Copper Molybdenum Nickel 0.22 0.3 0.3 0.5 0.2 0.5 0.34 0.6 0.8 0.025 0.025 1.3 0.4 0.7 3.0 0.2% proof stress Tensile strength Elongation Reduction of area Izod im

11、pact min. min. max. min. min. min. MPa (N/mm 2 ) MPa (N/mm 2 ) MPa (N/mm 2 ) % % ft lbf 940 1150 1300 5 14 10BSHC10:1974 2 BSI 02-2000 6.2 Hardness. The hardness of hardened and tempered castings and their representative test samples shall be: 7 Rectification of defects 7.1 Correction of distortion.

12、 When permitted in accordance with BSHC100 distortion shall be corrected after annealing and castings shall subsequently be hardened and tempered. 7.2 Repair of castings by welding. When repair by welding is permitted in accordance with BSHC100, this shall be carried out after annealing and castings

13、 shall subsequently be hardened and tempered. min. max. HB HV HRC 331 335 35 401 425 42blankBSHC 10:1974 BSI 389 Chiswick High Road London W4 4AL BSIBritishStandardsInstitution BSI is the independent national body responsible for preparing BritishStandards. It presents the UK view on standards in Eu

14、rope and at the international level. It is incorporated by Royal Charter. Revisions BritishStandards are updated by amendment or revision. Users of BritishStandards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality of our produ

15、cts and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using this BritishStandard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel:02089969000. Fax:02089967400. BSI offers members a

16、n individual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel:02089969001. Fax:02089967001. In respon

17、se to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as BritishStandards, unless otherwise requested. Information on standards BSI provides a wide range of information on national, European and international standards through i

18、ts Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel:02089967111. Fax:02089967048. Subscribing members of BSI are kept up to date with standards

19、developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel:02089967002. Fax:02089967001. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in the UK, of the public

20、ations of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or transmitted in any form or by any means electronic, photocopying, recording or otherwise without prior written permi

21、ssion from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. If permission is granted, the terms may include royalty payments or a licensing agreement. Details and advice can be obtained from the Copyright Manager. Tel:02089967070.