ASTM C926-2016b Standard Specification for Application of Portland Cement-Based Plaster《硅酸盐水泥基灰浆应用的标准规格》.pdf

《ASTM C926-2016b Standard Specification for Application of Portland Cement-Based Plaster《硅酸盐水泥基灰浆应用的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM C926-2016b Standard Specification for Application of Portland Cement-Based Plaster《硅酸盐水泥基灰浆应用的标准规格》.pdf（14页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C926 16bStandard Specification forApplication of Portland Cement-Based Plaster1This standard is issued under the fixed designation C926; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A numb

2、er in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers the requirements for the appli-cation of full thickness portland cement-based plaster forexterior (stucco) and i

3、nterior work.1.2 This specification sets forth tables for proportioning ofvarious plaster mixes and plaster thickness.NOTE 1General information will be found in Annex A1. Designconsiderations will be found in Annex A2.1.3 The values stated in inch-pound units are to be regardedas the standard. The S

4、I (metric) values given in parentheses areapproximate and are provided for information purposes only.1.4 The text of this specification references notes andfootnotes that provide explanatory material. These notes andfootnotes (excluding those in tables and figures) shall not beconsidered as requirem

5、ents of the specification.1.5 Details of construction for a specific assembly toachieve the required fire resistance shall be obtained fromreports of fire-resistance tests, engineering evaluations, orlistings from recognized fire testing laboratories.2. Referenced Documents2.1 ASTM Standards:2C11 Te

6、rminology Relating to Gypsum and Related BuildingMaterials and SystemsC25 Test Methods for Chemical Analysis of Limestone,Quicklime, and Hydrated LimeC35 Specification for Inorganic Aggregates for Use in Gyp-sum PlasterC91 Specification for Masonry CementC150 Specification for Portland CementC206 Sp

7、ecification for Finishing Hydrated LimeC207 Specification for Hydrated Lime for Masonry Pur-posesC219 Terminology Relating to Hydraulic CementC260 Specification for Air-Entraining Admixtures for Con-creteC578 Specification for Rigid, Cellular Polystyrene ThermalInsulationC595 Specification for Blend

8、ed Hydraulic CementsC631 Specification for Bonding Compounds for InteriorGypsum PlasteringC897 Specification for Aggregate for Job-Mixed PortlandCement-Based PlastersC932 Specification for Surface-Applied Bonding Com-pounds for Exterior PlasteringC1063 Specification for Installation of Lathing and F

9、urringto Receive Interior and Exterior Portland Cement-BasedPlasterC1116 Specification for Fiber-Reinforced Concrete andShotcreteC1328 Specification for Plastic (Stucco) CementC1787 Specification for Installation of Non Metallic PlasterBases (Lath) Used with Portland Cement Based Plaster inVertical

10、Wall ApplicationsE90 Test Method for Laboratory Measurement of AirborneSound Transmission Loss of Building Partitions andElementsE119 Test Methods for Fire Tests of Building Constructionand MaterialsE492 Test Method for Laboratory Measurement of ImpactSound Transmission Through Floor-Ceiling Assembl

11、iesUsing the Tapping Machine2.2 ANSI Standard:A108.1 Specification for Installation of Ceramic Tile33. Terminology3.1 Terms shall be defined as in Terminologies C11 andC219, except as modified herein.3.2 Definitions of Terms Specific to This Standard:3.2.1 accelerator, nan admixture that will shorte

12、n thesetting time of plaster.1This specification is under the jurisdiction of ASTM Committee C11 onGypsum and Related Building Materials and Systems and is the direct responsibilityof Subcommittee C11.03 on Specifications for theApplication of Gypsum and OtherProducts in Assemblies.Current edition a

13、pproved Sept. 1, 2016. Published September 2016. Originallyapproved in 1981. Last previous edition approved in 2016 as C926 16a. DOI:10.1520/C0926-16b.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStan

14、dards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr

15、 Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States13.2.2 admixture, na material other than water, aggregate,or basic cementitious material added to the batch before orduring job mixing.3.2.3 acid etching, nthe cleansing and controlled erosionof a solid surface, using an acid

16、 wash.3.2.4 air entrainment, nthe use of an air-entraining ad-mixture or air-entraining cementitious material in a plaster mixto yield a controlled quantity of minute (typically between 10and 1000 m in diameter) disconnected air bubbles in theplaster (see entrapped air).3.2.5 back wrap, na means of

17、terminating a polymer-modified, fabric reinforced cementitious base coat by wrappingthe reinforcing mesh, which has been affixed to the substrateonto the outboard surface of the foam plastic core to providecontinuity of the reinforced base coat and protection for thefoam plastic core.3.2.6 backplast

18、er, nplaster applied to the face of metallath opposite a previously applied plaster.3.2.7 barrier wall, ntype of wall system that is intended toblock or interrupt the movement of water to the interior.3.2.8 bond, nthe state of adhesion between plaster coats orbetween plaster and plaster base.3.2.9 b

19、onding compound or agent, ncompounds surfaceapplied or integrally mixed with plaster to improve the qualityof bond between plaster and plaster base or between plastercoats.3.2.10 cementitious material, na material that, whenmixed with water and with or without aggregate, provides theplasticity and t

20、he cohesive and adhesive properties necessaryfor placement and the formation of a rigid mass.3.2.11 coat, na thickness of plaster applied in a singleoperation.3.2.11.1 basecoat, nall plaster applied before the applica-tion of the finish coat.3.2.11.2 bedding coat, na plaster coat that receives aggre

21、-gate or other decorative material impinged into its surfacebefore it sets.3.2.11.3 brown coat, nin three-coat work, the second coat,applied over the scratch coat. In two-coat work, brown coatrefers to the double-up basecoat. In either use, the brown coatis the coat directly beneath the finish coat.

22、3.2.11.4 dash-bond coat, na thick wet mixture of portlandcement and water, with or without aggregate, dashed onto thesurface of a plaster base such as smooth monolithic concrete orconcrete block surfaces to improve the mechanical key forsubsequent plaster coats.3.2.11.5 double-up coat, nthe brown-co

23、at plaster appliedto the scratch coat plaster before the scratch-coat plaster hasset.3.2.11.6 finish coat, nthe final layer of plaster applied overbasecoat plaster.3.2.11.7 fog coat, na light coat of cement and water, withor without aggregate or color pigment, applied by machinespray to improve colo

24、r consistency.3.2.11.8 scratch coat, nthe first coat of plaster applied toa plaster base.3.2.11.9 skim coat, na thin finish coat applied to anexisting plaster surface or other substrate to improve appear-ance.3.2.11.10 three-coat work, napplication of plaster in threesuccessive coats with time betwe

25、en coats for setting or drying,or both.3.2.12 cold joint (“joining” or “jointing”), nthe junctureof fresh plaster application adjacent to set plaster, in the sameplane.3.2.13 curing, vthe act or processes of producing a mois-ture environment favorable to cement hydration, resulting inthe setting or

26、hardening of the plaster.3.2.14 drainage wall, na wall system in which the clad-ding provides a substantial barrier to water intrusion, andwhich also incorporates a concealed water-resistive barrierover which drainage will occur.3.2.15 entrapped air, nunintentional air voids in the plas-ter generall

27、y larger than 1 mm.3.2.16 factory prepared (“mill-mixed” or “ready mixed”),adjpertaining to material combinations that have been for-mulated and dry-blended by the manufacturer, requiring onlythe addition of and mixing with water to produce plaster.3.2.17 fiber, natural or synthetic, nan elongated f

28、iber orstrand admixture added to plaster mix to improve cohesivenessor pumpability, or both.3.2.18 floating, vact of compacting and leveling brown-coat plaster to a reasonably true surface plane using a float toolor the act of bringing the aggregate to the surface of finish-coatplaster.3.2.19 key (a

29、lso mechanical key), nplaster that physicallysurrounds, penetrates, or deforms to lock onto the perforationsor irregularities of the plaster base or previous coat of plaster.3.2.20 metal plaster base, nexpanded metal lath, orwelded or woven wire lath.3.2.21 plaster, nportland cement-based cementitio

30、us mix-ture (see stucco).3.2.22 polymer modified cementitious base coat, nA basecoat containing portland cement modified with chemical ad-mixtures (typically polymer latexes) to improve characteristicsof the finished product, such as workability, plasticity, waterresistance, and adhesion.3.2.23 requ

31、ired, adjpertaining to a mandatory obligationimposed by a force outside of this specification, such as abuilding code, project specification, contract, or purchaseorder.3.2.24 rustication (also “break”), nan interruption orchange in plane of a plastered surface.3.2.25 scoring (also known as “scratch

32、ing”), nthe groov-ing of the surface of an unset plaster coat to provide a key fora subsequent coat.3.2.26 set, nthe chemical and physical change in plaster asit goes from a plastic, workable state to a rigid state.C926 16b23.2.27 solid plaster bases, nsubstrates that do not requirea metal plaster b

33、ase, including cast in place and precastconcrete, concrete and stone masonry, clay brick, and tile.3.2.28 stucco, nportland cement-based plaster used onexterior locations.3.2.29 stucco finish, na factory-prepared, dry blend ofmaterials for finish coat applications.3.2.30 temper, vto mix or restore u

34、nset plaster with waterto a workable consistency.3.2.31 texture, nany surface appearance as contrasted to asmooth surface.4. Delivery and Storage of Materials4.1 Delivery:4.1.1 Packaged materials shall be delivered in factory-sealed, unopened, and unbroken packages, containers, orbundles.4.1.2 Bulk

35、materials shall be delivered in clean transportvessels, free of contaminates.4.2 Storage:4.2.1 Weather-sensitive materials shall be kept in a drycondition until ready for use. (See A2.4.)4.2.2 Bulk materials shall be stored to prevent subsequentcontamination and segregation.5. Materials5.1 Materials

36、 shall conform to the requirements of thereferenced specifications and standards and to the requirementsspecified herein.5.2 Cement:5.2.1 Portland CementSpecification C150, Type I, II, andIII, as specified. White where specified.5.2.2 Air-Entraining Portland CementSpecification C150,type as specifie

37、d. White where specified.5.2.3 Masonry CementSpecification C91, Types N, S, andM. White where specified.5.2.4 Blended Hydraulic CementSpecification C595,Type IP, IS(70), IL, and IT(S70), as specified.5.2.5 Air-Entraining Blended Hydraulic CementSpecification C595, Type IP-(A), IS(70)-(A), IL-(A), an

38、d IT(S70)-(A), as specified.5.2.6 Plastic CementPlastic Cement shall meet the re-quirements of Specification C1328, Standard Specification forPlastic (Stucco) Cement.NOTE 2Plastic cements are not available nationally.5.3 Type “S” Hydrated LimeAhydrated lime that containsnot more than 8 % unhydrated

39、oxides when tested in accor-dance with Test Methods C25. See Specifications C206 andC207 for a complete description of a Type “S” hydrated lime.5.4 Aggregates:5.4.1 Sand for Base CoatsSpecification C897. Aggregatefailing to meet gradation limits in Specification C897 shall bepermitted to be used, pr

40、ovided the plaster made with this sandhas an acceptable demonstrated performance record in similarconstruction and climate conditions.5.4.2 PerliteSpecification C35.5.4.3 Sand for Job-Mixed Finish CoatsSpecificationC897.5.5 WaterWater used in mixing, application, and finishingof plaster shall be cle

41、an, fresh, suitable for domestic waterconsumption, and free of such amounts of mineral or organicsubstances as would affect the set, the plaster, or any metal inthe system.5.6 AdmixturesSee 3.2.2 and A2.5.5.7 FibersSpecification C1116 on alkali-resistant fibers,glass fibers, nylon, polypropylene or

42、carbon fibers.5.8 Product MarkingPackaged materials shall be clearlymarked or labeled to indicate product, brand name, themanufacturer, and the weight of the material contained therein.Similar information shall be provided in the shipping advicesaccompanying the shipment of bulk materials.6. Require

43、ments for Bases to Receive Portland Cement-Based Plaster6.1 Metal bases and accessories used to receive plaster shallbe installed in conformance with Specification C1063, exceptas otherwise specified. Non-metallic bases used to receiveplaster shall be installed in conformance with SpecificationC1787

44、.NOTE 3All plaster bases and accessories shall be free of deleteriousamounts of rust, oil, or other foreign matter, which could cause bondfailure or unsightly discoloration.6.2 Surfaces of solid bases to receive plaster, such asmasonry, stone, cast-in-place or precast concrete shall bestraight and t

45、rue within14 in. (6 mm) in 10 ft (3 m) and shallbe free of form oil or other elements, which would interferewith bonding. Conditions where the surfaces are out oftolerance shall be corrected prior to the application of theplaster. Ferrous-containing form ties or other obstructions shallbe removed or

46、 receded a minimum 1/8 in. (3 mm) below thesurface of the solid base and treated with a corrosion-resistantcoating. Non-ferrous protuberances shall be permitted to betrimmed back even with the surface of the solid base.6.2.1 Solid surfaces shall have the suction (ability to absorbwater) or surface r

47、oughness, or both, to provide the bondrequired for the plaster.6.2.2 Smooth or nonabsorbent solid surfaces, such as cast-in-place or precast concrete, shall be prepared to receiveportland cement plaster by one of the following methods:6.2.2.1 Sandblasting, wire brushing, acid etching, or chip-ping o

48、r a combination thereof,6.2.2.2 Application of a dash-bond coat applied forcefullyagainst the surface, left untroweled, undisturbed, and moistcured for at least 24 h, or6.2.2.3 Application of a bonding compound suitable forexterior or interior exposure solid surfaces in accordance withthe manufactur

49、ers written directions.6.2.3 Where bond cannot be obtained by one or more of themethods in 6.2.2, a furred or self-furring plaster base shall beinstalled in accordance with Specification C1063 or C1787 asappropriate. Where plaster base is used in areas where bondcannot be obtained by one or more of the methods in 6.2.2,C926 16b3accessories shall be installed in accordance with SpecificationC1063 or C1787 as appropriate.7. Application7.1 Plaster Proportions:7.1.1 All portland cement plasters shall be mixed andproportioned