1、Designation: C325 07 (Reapproved 2014)Standard Guide forWet Sieve Analysis of Ceramic Whiteware Clays1This standard is issued under the fixed designation C325; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revisi

2、on. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This guide covers the wet sieve analysis of ceramicwhiteware clays. This guide is intended for use in testingshipments of clay as

3、 well as for plant control tests.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.3 This standard does not purport to address all of

4、 thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2C322 Practice for Sampli

5、ng Ceramic Whiteware ClaysE11 Specification for Woven Wire Test Sieve Cloth and TestSieves3. Apparatus3.1 Stirring DeviceA mechanical stirrer with a three-bladed propeller 2 in. (51 mm) in diameter and having a speedof approximately 1700 r/min, or the equivalent, shall beprovided.3.2 SievesThe sieve

6、s shall conform to Specification E11and shall include the No. 100 (150-m), No. 140 (106-m), No.200 (75-m) and No. 325 (45-m) sieves (Note 1). The wirecloth for these sieves shall be woven (not twilled) and shall bemounted in circular metal frames 8 in. (203 mm) in diameter,which shall be so construc

7、ted as to permit nesting of two ormore sieves. A pan and cover for the sieves shall be provided.NOTE 1Equivalent sieves from other standard series, such as the Tylerseries, may also be used. If results are to be compared with those obtainedwith sieves from the ASTM series, it is important that the o

8、penings of thesieves used fall within the tolerances specified in Specification E11 for thecorresponding ASTM sieves.4. Sampling4.1 The sample shall be obtained in accordance with Prac-tice C322.4.2 The sample as received shall be placed in a drying ovenat 100 to 110C for a period of not less than 5

9、 h prior to testing.5. Procedure5.1 Transfer duplicate portions, of approximately 250 g ofthe dried clay sample, weighed to the nearest 0.1 g, tocontainers of at least 2-L capacity. Wet the clay with 1 L ofwater and allow to slake for 2 h. If a free-flowing slurry is notproduced by this treatment, a

10、dd another 500 mL of water.5.2 To ensure complete separation of clay from nonplasticimpurities, agitate the slurry by means of a mechanical stirrer(3.1). Continue the stirring between 5 and 10 min.5.3 Transfer the slaked and stirred sample, without loss, tothe finest sieve to be employed in the test

11、, and wash by meansof a small jet of water from a14-in. (6.4-mm) soft rubber hoseattached to a water supply having a pressure not in excess ofthat of an ordinary city main. The force of the jet may becontrolled by compressing the end of the hose between thethumb and forefinger. Take care to avoid lo

12、ss of sample fromsplashing. Continue washing until water passing through thesieve shows only traces of sample. Should lumpy materialremain on the screen, return the residue to the stirrer containerby careful washing with a gentle jet of water, and agitate inapproximately 1 L of water for 10 min, the

13、n wash the slurry aspreviously described.5.4 Wash the residue remaining on the finest sieve into thepan. Thoroughly wet the remaining sieves to be used in the testwith clear water, and nest them in the proper sequence on thefinest sieve. Wash the residue in the pan quantitatively onto thetop sieve,

14、and give the stack a preliminary washing.5.5 Nest the top sieve on the pan, which shall contain about12 in. (12.7 mm) of clear water. Wash the residue by holdingthe pan and sieve firmly in the hands, and by a sidewisemovement, causing water to splash up through the sieve andinto the residue. This mo

15、vement, coupled with interspersed1This guide is under the jurisdiction of ASTM Committee C21 on CeramicWhitewares and Related Products and is the direct responsibility of SubcommitteeC21.04 on Raw Materials.Current edition approved Jan. 1, 2014. Published February 2014. Originallyapproved in 1953. L

16、ast previous edition approved in 2007 as C325 07. DOI:10.1520/C0325-07R14.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe

17、ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1circular motions, allows thorough washing. Wash the residueand water remaining in the pan onto the top sieve of the stack.5.6 Again fill the pan with the proper amount of wa

18、ter, nestthe top sieve and its residue on the pan, and repeat theoperation. Continue this until the finest sieve has been washed.Carefully blot each sieve on its underside with a soft, dampsponge, and place the sieve either in a drying oven at 100 to110C or under infrared lamps until thoroughly dry.

19、 Approxi-mately2hisrequired with a drying oven, but only about 30min with an infrared lamp set 12 in. (305 mm) above the sieve.5.7 Nest the dried residues and sieves in the proper order,with due care to prevent dusting of the residues. Close the stackof sieves with a dry pan and cover, and tap the a

20、ssembly lightlyfor 1 min on a table top.5.8 Separate the nested sieves and carefully brush theresidue from each onto a weighing paper. Weigh the residues tothe nearest 0.001 g on an analytical balance.6. Calculation and Report6.1 Calculate the sieve analysis for test sample on the dryweight basis, a

21、nd report the results to the nearest 0.01 % of thematerial retained on each sieve. Report the percentage passingthe finest sieve as the difference between 100 % and the sum ofthe percentages retained on the various sieves.7. Keywords7.1 clay; sieve analysis; wet sieveASTM International takes no posi

22、tion respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibili

23、ty.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to AST

24、M International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address

25、shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).C325 07 (2014)2