ASTM A537 A537M-2013 Standard Specification for Pressure Vessel Plates Heat-Treated Carbon-Manganese-Silicon Steel《压力容器用经热处理的碳锰硅钢板的标准规格》.pdf
《ASTM A537 A537M-2013 Standard Specification for Pressure Vessel Plates Heat-Treated Carbon-Manganese-Silicon Steel《压力容器用经热处理的碳锰硅钢板的标准规格》.pdf》由会员分享,可在线阅读,更多相关《ASTM A537 A537M-2013 Standard Specification for Pressure Vessel Plates Heat-Treated Carbon-Manganese-Silicon Steel《压力容器用经热处理的碳锰硅钢板的标准规格》.pdf(4页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: A537/A537M 08A537/A537M 13Standard Specification forPressure Vessel Plates, Heat-Treated, Carbon-Manganese-Silicon Steel1This standard is issued under the fixed designation A537/A537M; the number immediately following the designation indicates the yearof original adoption or, in the cas
2、e of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 This spec
3、ification2 covers heat-treated carbon-manganese-silicon steel plates intended for fusion welded pressure vesselsand structures.1.2 Plates furnished under this specification are available in the following three classes:Yield TensileStrength, Strength,Heat Thickness, min, ksi min, ksiClass Treatment M
4、Pa MPa1 Normalized 212 in. andunder65 mm andunder5034570485Over 212 to 4 in.Over 65 to 100mm45310654502 Quenchedand tempered212 in. andunder65 mm andunder6041580550Over 212 to 4 in.Over 65 to 100mm5538075515Over 4 to 6 in.Over 100 to 150mm46315704853 Quenchedand tempered212 in. andunder65 mm andunde
5、r5538080550Over 212 to 4 in.Over 65 to 100mm5034575515Over 4 to 6 in.Over 100 to 150mm40275704851.3 The maximum thickness of plates furnished under this specification is 4 in. 100 mm for Class 1 and 6 in. 150 mm forClass 2 and Class 3.1.4 The values stated in either inch-pound units or SI units are
6、to be regarded separately as standard. Within the text, the SI unitsare shown in brackets. The values stated in each system are not exact equivalents; therefore, each system is to be usedindependently of the other without combining values in any way.1 This specification is under the jurisdiction ofA
7、STM Committee A01 on Steel, Stainless Steel and RelatedAlloys and is the direct responsibility of Subcommittee A01.11on Steel Plates for Boilers and Pressure Vessels.Current edition approved Sept. 1, 2008Oct. 1, 2013. Published September 2008October 2013. Originally approved in 1965. Last previous e
8、dition approved in 20062008as A537/A537M 06.A537/A537M 08. DOI: 10.1520/A0537_A0537M-08.10.1520/A0537_A0537M-13.2 For ASME Boiler and Pressure Vessel Code applications, see related Specification SA-537/SA-537M in Section II of that Code.This document is not an ASTM standard and is intended only to p
9、rovide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof t
10、he standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States12. Referenced Documents2.1 ASTM Standards:3A20
11、/A20M Specification for General Requirements for Steel Plates for Pressure VesselsA435/A435M Specification for Straight-Beam Ultrasonic Examination of Steel PlatesA577/A577M Specification for Ultrasonic Angle-Beam Examination of Steel PlatesA578/A578M Specification for Straight-Beam Ultrasonic Exami
12、nation of Rolled Steel Plates for Special Applications3. General Requirements and Ordering Information3.1 Plates furnished supplied to this material specification shall conform to Specification A20/A20M. These requirementsoutline the testing and retesting methods and procedures; permissible variatio
13、ns in dimensions; and mass, quality, and repair ofdefects, marking, loading, etc. and ordering information.3.2 Specification A20/A20M also establishes the rules for the ordering information which should be complied with whenpurchasing material to this specification.3.2 In addition to the basic requi
14、rements of this specification, certain supplementary requirements are available when additionalcontrol, testing, or examination is required to meet end use requirements. These include: The purchaser is referred to the listedsupplementary requirements in this specification and to the detailed require
15、ments in Specification A20/A20M.3.3.1 Vacuum treatment,3.3.2 Additional or special tension testing,3.3.3 Impact testing, and3.3.4 Nondestructive examination.3.4 The purchaser is referred to the listed supplementary requirements in this specification and to the detailed requirements inSpecification A
16、20/A20M.3.3 If the requirements of this specification are in conflict with the requirements of Specification A20/A20M, the requirementsof this specification shall prevail.4. Manufacture4.1 Steelmaking PracticeThe steel shall be killed and conform to the fine austenitic grain size requirement of Spec
17、ificationA20/A20M.5. Heat Treatment5.1 All plates shall be thermally treated as follows:5.1.1 Class 1 plates shall be normalized.5.1.2 Class 2 and Class 3 plates shall be quenched and tempered. The tempering temperature for Class 2 plates shall not be lessthan 1100F 595C and not less than 1150F 620C
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMA537A537M2013STANDARDSPECIFICATIONFORPRESSUREVESSELPLATESHEATTREATEDCARBONMANGANESESILICONSTEEL 压力容器

链接地址:http://www.mydoc123.com/p-458718.html