ARMY MIL-C-44349-1988 CUP WATER CANTEEN COLD WEATHER CRS《耐蚀钢冬季水箱杯》.pdf

《ARMY MIL-C-44349-1988 CUP WATER CANTEEN COLD WEATHER CRS《耐蚀钢冬季水箱杯》.pdf》由会员分享，可在线阅读，更多相关《ARMY MIL-C-44349-1988 CUP WATER CANTEEN COLD WEATHER CRS《耐蚀钢冬季水箱杯》.pdf（11页珍藏版）》请在麦多课文档分享上搜索。

1、1 INCH-POUND 1 MIL-C-44349 ( GL) 9 December 1988 MILITARY SPECIFICATION CUP, WATER CANTEEN, COLD WEATHER, CRS This specification is approved for use by the U.S. Army Natick Research, Development, and Engineering Center, Department of the Army, and is available for use by all Departments and Agencies

2、 of the Department of Defense. 1. SCOPE 1.1 Scope. This specification covers one type and size of corrosion- resisting steel canteen cup with a folding wire handle having an 18 ounce capacity. 2. APPLICABLE DOCUMENTS 2.1 Government documents. 2.1.1 Specifications, standards, and handbooks. The follo

3、wing specifi- cations, standards, and handbooks form a part of this document to the extent specified herein. Unless otherwise specified, the issues of these documents are those listed in the issue of the Department of Defense Index of Specifications and Standards (DODISS) and supplement thereto, cit

4、ed in the solicitation (see 6.2). SPECIFICATIONS FEDERAL QQ-P-35 - Passivation Treatments for Corrosion-Resisting Stee 1 PPP-B-26 - Bag, Plastic, (General Purpose) PPP-B-636 - Boxes, Shipping, Fiberboard I Beneficial comments (recommendations, additions, deletions) and any pertinent data which may b

5、e of use in improving this document.should be addressed to: U. S. Army Natick Research, Development, and Engineering Center, Natick, MA 01760-5014 by using the self-addressed Standardization Document Improvement Proposal (DD Form 1426) appearing at the end of this document or by let ter. FSC 8465 DI

6、STRIBUTION STATEMENT A. Approved for public release; distribution is unlimited. 7- -, THIS DOCUMENT CONTAINS PAGES. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-C-44349( GL) 2 MIL-C-44349 4 799990b 0403541 5 W rb MILITARY O MIL-L-35078 - Loads

7、, Unit: Preparation of Semiperishable Subsistence Items; Clothing, Personal Equipment and Equipage; General Specification for STANDARDS MIL I TARY MIL-STD-105 - Sampling Procedures and Tables for Inspection by Attributes MLL-STD-129 - Marking for Shipment and Storage MIL-STD-147 - Palletized Unit Lo

8、ads MIL-STD-731 - Quality of Wood Members for Containers and Pallets (Unless otherwise indicated, copies of federal and military specifications, standards, and handbooks are available from the Naval Publications and Forms Center, (ATTN: NPODS), 5801 Tabor Avenue, Philadelphia, PA 19120-5099.) 2.1.2

9、Other Government documents, drawings, and publications. The following other Government documents, drawings, and publications form a part of this document to the extent specified herein. Unless otherwise specified, the issues are those cited in the solicitation. O DRAWINGS U. S. ARMY NATICK RESEARCH,

10、 DEVELOPMENT, AND ENGINEERING CENTER 2-10-450 - Cup, Canteen; Assembly (Canteen, Cold Weather, CRS) 2-10-451 - Cup, Canteen 2 -1 O -452 - Handle, Left Hand 2 -1 O -4 53 - Handle, Right Hand 2 -1 O -454 - Hinge, Handle (Copies of drawings required by contractors are available from the U.S. Army Natic

11、k Research, Development, and Engineering Center, Natick, MA 01760-5014.) 2.2 Non-Government publications. The following document(s) form a part of this document to the extent specified herein. Unless otherwise specified, the issues of the documents which are DOD adopted are those listed in the issue

12、 of the DODISS cited in the solicitation. Unless otherwise specified, the issues of documents not listed in the DODISS are the issues of the documents cited in the solicitation (see 6.2). Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-. MIL-C-44349(

13、GL) AMERICAN SOCIETY FOR TESTING AND MATERIALS (ASTM) D 3951 - Standard Practice for Commercial Packaging E 18 - Rockwell Hardness and Rockwell Superficihl Hardness of Metallic Materials (Application for copies should be addressed to the American Society for Testing and Materials, 1916 Race Street,

14、Philadelphia, PA 19103-1187.) (Nongovernment standards and other publications are normally available from the organizations that prepare or distribute the documents. These documents also may be available in or through libraries or other informational services.) 2.3 Order of precedence. In the event

15、of a conflict between the text of this document and the references cited herein, the text of this document takes precedence. Nothing in this document, however, supersedes applicable laws and regulations unless a specific exemption has been obtained. 3. REQUIREMENTS 3.1 First article. When specified

16、(see 6.21, a sample shall be subjected to first article inspection (see 6.3) in accordance with 4.3. 3.2 Guide samples. Guide samples, when furnished, are solely for guidance and information (see 6.4). the sample, in which case this specification shall govern. Variations from this specification may

17、appear in O 3.3 Materials and components. The materials shall be as specified herein and on Drawings 2-10-451 y 2-10-452, 2-10-453 y and 2-10-454. Materials and components not definitely specified .shall be of the quality normally used by the manufacturer provided the completed item complies with al

18、l the provisions of this specification. 3.3.1 Recycled materials. Recycled materials may be used in the fabrication of the cup provided that they meet the requirements of this specification. 3.4 Design and construction. The design and construction of the cup shall conform to Drawing 2-10-450 and the

19、 requirements specified herein. 3.4.1 Body. The body of the cup shall be fabricated of the corrosion- resisting steel specified on Drawing 2-10-451 and shall be of seamless construc- tion. The top edge shall be free of sharp edges, cracks, burrs, slivers, or rough surfaces. After forming, the vertic

20、al walls of the body shall have a minimum hardness of 46 on the 30N Rockwell scale when tested as specified in 4.5.5. 3 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-_ _ - - _ _I- - _ MIL-C-44347 154 W 7777706 0403543 7 W d I O MIL-C-4434 9 ( GL) 3

21、.4.2 Handles. The handles shall be fabricated of corrosion-resisting steel and welded in accordance with Drawings 2-10-452 and 2-10-453. The welds of the handle shall withstand a minimum total force of 235 pounds when tested as speci- fied in 4.5.4 The handle shall conform to the design, dimension,

22、and detail requirements of Drawings 2-10-452 and 2-10-453. The handle shall fit snugly against the cup within 1/8 inch when folded and the right handle shall nest and lock into the left handle when in use. 3.4.3 Hinge, The hinge shall be fabricated of corrosion-resisting steel and shall conform to t

23、he design, dimension, and details specified on Drawing 2-10-454. The hinge shall be attached by spot welds or projection welds, shall be located on the cup, and shall be attached as shown on Drawing 2-10-450, The welds shall be free of splatter, burn holes, cracks or fractures, and discolor- ation a

24、nd shall be tightly joined when tested as specified in 4.5.1, 4.5.2, or 4.5.3, as applicable. The hinge shall be a close fit to the contour of the body and there shall be no gaps between edge of hinge and body greater than 1/64 inch. * 3.5 Finish, The cup shall be given a uniform frosted lusterless

25、finish approximating a commercial 2D sheet finish and passivated in accordance with QQ-P-35, There shall be no evidence of rust, staining, pitting, or spotting when tested as specified in 4.5.6. 3.6 Markinq. The letters US, the year of manufacture, and the manu- m facturers name or trademark shall b

26、e stamped on the hinge as shown on Drawing 2-10-451. 3.7 Workmanship. The cup shall conform to the quality of product established by this specification and the occurrence of defects shall not exceed the applicable acceptable quality levels, The finished cup shall be clean and free of any dent or bei

27、ng bent out of shape, stain, ripple, fracture, or die or draw mark. The handles and hinge shall also be free of any sharp edge, burr, or sliver. Indentation on the inside of cup due to welding of the hinge is acceptable providing the indentation is smooth and free from sharp edges, weld splatter, bu

28、rr, crack, or burn through area, and does not exceed 0.005 inch in depth. 4. QUAJiIT ASSURANCE PROVISIONS 4.1 Responsibility for inspection. Unless otherwise specified in the contract or purchase order, the contractor is responsible for the performance of all inspection requirements (examinations an

29、d tests) as specified herein. Except as otherwise specified in the contract or purchase order, the contractor may use his own or any other facilities suitable for the performance of the inspection requirements specified herein, unless disapproved by the Government. The Government reserves the right

30、to perform any of the inspections set forth in this specification where such inspections are deemed necessary to ensure supplies and services conform to prescribed requirements. 4 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-4.1.1 Responsibility f

31、or compliance. All items shall meet all requirements of sections 3 and 5. become a part of the contractors overall inspection system or quality program. The absence of any inspection requirements in the specification shall not relieve the contractor of the responsibility of ensuring that all product

32、s or supplies submitted to the Government for acceptance comply with all requirements of the contract. Sampling inspection, as part of manufacturing operations, is an acceptable practice to ascertain conformance to requirements, however, this does not authorize submission of known defective material

33、, either indicated or actual, nor does it commit the Government to accept defective material, The inspection set forth in this specification shall 4.1.2 Responsibility for dimensional requirements. Unless otherwise speci- fied in the contract or purchase order, the contractor is responsible for ensu

34、ring that all specified dimensions have been met. When dimensions cannot be examined on the end item, inspection shaIl be made at any point, or at all points in the manufacturing process necessary to assure compliance with all dimensional requirements. 4.2 Classification of inspections. The inspecti

35、on requirements specified herein are classified as follows: a. First article inspection (see 4.3). b. Quality conformance inspection (see 4.4). 4.3 First article inspection. When a first article is required (see 6.2), it shall be examined for the defects specified in 4.4.3 and 4.4.4 and tested as sp

36、ecified in 4.5.2 through 4.5.6, as applicable. 4.4 Quality conformance inspection. Unless otherwise specified, sampling for inspection shall be performed in accordance with MIL-STD-105. 4.4.1 Component and material inspection. In accordance with 4.1, components and materials shall be inspected in ac

37、cordance with all the requirements of referenced documents unless otherwise excluded, amended, modified, or qualified in this specification or applicable purchase document. 4.4,2 In-process inspection. 4.4.2.1 In-process examination. In-process examination shall be made to establish conformance to t

38、he welding on wire handles requirements of Drawing 2-10-452 and 2-10-453. Whenever nonconformance is noted, correction shall be made to the applicable process and to all items processed. be corrected shall be removed from production. Items which cannot 5 Provided by IHSNot for ResaleNo reproduction

39、or networking permitted without license from IHS-,-,- I -_ _- MIL-C-44347 4 777740b 0403545 2 m b c O MIL-C-44349(GL) 4.4.2.2 In-process spot or projection weld testing. The spot or projection weld sample peel test shall be conducted on two test specimens per welding machine rather than sample cups.

40、 The spot or projection welding testing shall be performed as specified in 4.5.1 at the start of each days shifts production. Failure of test shall require correction of the welding process. 4.4.3 End item visual examination. The end items shall be examined for the defects listed in table I, The lot

41、 size shall be expressed in units of cups. The sample unit shall be one cup. The inspection level shall be II and the acceptable quality level (AQL), expressed in terms of defects per hundred units, shall be 2.5 for major defects and 6.5 for total (major and minor combined) defects. TABLE I. End ite

42、m visual defects Classif ication Examine Defect Major Minor Finish Not a uniform, frosted, lusterless finish approximating a commercial 2D sheet finish 201 Evidence of rust, staining,pitting, or spotting (slight water spotting, easily removed by washing shall not be considered a defect) 101 workman

43、chip or metal ripple 102 components and Component denfed 202 Construction and Seam, lap, lamination or crease, (applicable to all Any component missing 103 as s embl ies ) Component fractured 104 Component bent out of shape Rim of cup contains sharp edge, Evidence of die or draw mark I 204 203 burr,

44、 crack, sliver, or rough spot 105 Handle does not fold around cup within 1/8 inch as specified, or right handle does not nest and lock into left handle 106 Hinge plate is not close fit against body, i.e contains gap along edge greater than 1/64 inch (use feeler gage) Handle binds or requires force i

45、n Handle or hinge contains sharp edge, opening or folding burr, or sliver 6 107 205 206 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-C-44349( GL) TABLE I. End item visual defects (contd) Classification Examine Defect MaJor Minor We Ids Contain

46、s crack or fracture 108 Not in location shown on drawing 207 Contains burn hole, splatter, or Not number specified 109 discoloration 110 Evidence of poor fusion 111 Any missing weld 112 Weld on handle not neatly performed, i.e. contains rough or sharp projection or bead 20 8 Indentation in weld area

47、 on inside of cup (indentation on inside of the cup due to welding of the hinge is acceptable providing the indentation is smooth and free from sharp edges, weld splatter, burr, crack, bwn through area, and does not exceed 0.005 inch in depth) 20 9 Marking Missing, illegible, or incomplete 210 4.4.4

48、 End item dimensional examination. The end items shall be examined for conformance to the dimensions specified on drawings that can be determined on the end items without damaging or disassembling the end items. The .iot size shall be expressed in units of cups. The sample unit shall be one cup. The

49、 inspection level shall be S-2 and the AQL, expressed in terms of defects per hundred units, shall be 4.0. 4.4.5 End item testing. The end items shall be tested as specified in 4.5.2 or 4.5.3, 4.5.4, 4.5.5, and 4.5.6. The lot size shall be expressed in units of cups. The sample unit shall be one cup. The inspection level shall be S-1 and the AQL, expressed in terms of defects per hundred units, shall be 2.5. 4.4.6 Packaging examination. The fully pa