ARMY DOD-P-63981-1982 PROJECTILE 30MM HIGH EXPLOSIVE DUAL PURPOSE M789 METAL PARTS《M789型双重用途30 mm高爆榴弹用金属部件》.pdf

《ARMY DOD-P-63981-1982 PROJECTILE 30MM HIGH EXPLOSIVE DUAL PURPOSE M789 METAL PARTS《M789型双重用途30 mm高爆榴弹用金属部件》.pdf》由会员分享，可在线阅读，更多相关《ARMY DOD-P-63981-1982 PROJECTILE 30MM HIGH EXPLOSIVE DUAL PURPOSE M789 METAL PARTS《M789型双重用途30 mm高爆榴弹用金属部件》.pdf（17页珍藏版）》请在麦多课文档分享上搜索。

1、a. I DOD-P-b378L 13 W 7777706 0352327 T DOD-P-63981 (AR) 29 CIBER 1982 MILITARY SPECIFICATION PROJECTILE 30MM, HIGH EXPLOSIVE DUAL PURPOSE, M789 METAL PARTS This specification is approved for use by the U.S. Army Armament Research and Development Command and is available for use by all Departments a

2、nd Agencies of the Department of Defense. 1. SCOPE 1.1 This specification covers the metal parts, equipment, requirements, quality assurance provisions and packaging for the 30MM High Explosive Dual Purpose Projectile for use in the 30MM, EEDP, M789 Cartridge. 2. APPLICABLE DOCUMENTS 2.1 2.1.1 Qecif

3、ications and standards. Unless otherwise specified (See 6.2), the following specifications and standards of the issue listed in that issue of the Department of Defense Index of Specifications and Standards (DoDISS) specified in the solicitations, form a part of this specification to the extent speci

4、fied herein. SPECIFICATIONS Federal TT-C-490 I Cleaning Methods and Pretreatment of Ferrous Surfaces for Organic Coat i ng s Military MIL-A-48078 Ammunition, Standard Quality Assurance Provisions, General Specification for STANDARDS Sampling Procedures and Tables for Inspection by Attributes - MIL-S

5、TD-105 THIS DOCUMENT CONTAINS 17 PAGES. - E FS 1305 Aro. Beneficial comments (recommeiidations, additions, deletions) and any perdnent data which may be of UIX in improvin this dmument should be rddrersed to: Commander, US Army Armament .FI 8 8 Provided by IHSNot for ResaleNo reproduction or network

6、ing permitted without license from IHS-,-,-DOD-P-6398L 13 m 999970b 0352335 9 m E Y 3 Y Y n z 0 5 U ti t ri * m ri 4ririririrlri ririririrl m MMMMM mmm.mm . d e u m a Cu c U4 a, n 9) c O 2 a, u) Zl E I LI -4 u m U EI 2 W O QI *a, mu am UIW k cc11 c u). m X 9 Provided by IHSNot for ResaleNo reproduct

7、ion or networking permitted without license from IHS-,-,-h Y 2 4 Qo QI m io I pi I 8 a E c E Y 3 ti Y Y P 0 z 5 V DOD-P-63781 13 m 7774706 035233b O m 8 .u m Gd d u) 1 .Pl 5 Q & Y 10 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-DOD-P-b3981 13 m 79

8、999Ob 0352337 2 m z Y I pi CI w 3.1 d P VI VI 4 a C m al P C 04 4J m 4J O cf4 v C m k a O a L 8 m (v w * . . * .- Cu m w al . U di O 2 al m 0 n In di cv m w . a a cn w- 8 U m & m rl I-IrlrldiW m m mmmmm . .I. m rlrlm rl m mmm . . VI VI Q, c a C Il 8 u3.1 a. wo 11 Provided by IHSNot for ResaleNo repr

9、oduction or networking permitted without license from IHS-,-,-8 t rl a ccr DOD-P-63781 13 W 777770b 0352338 4 W rlcv o. 4w w IC mm m m *e e e orlo4orl *I II 111 rr( cv e 21 & u 12 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-rl b N s 5 DOD-P-6378L

10、 13 m 777770b 0352337 b m - gsg c dpdpdpdpdpdpdpdp oooou1ooo crcrcycrwcrcycy a. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-DOD-P-63781 13 m 7779706 0352340 2 DOD-P-63981 (AR) 4.4.3 Testinq. 4.4.3.1 Sand fill. Projectile assemblies shall be secti

11、oned through the longitudinal axis to expose the band fill in the undercut areas. Each undercut area so exposed shall as a minimum be 50% filled by the rotating band material. 4.4.3.2 Inspection verification. Inspection verification by soundness inspection shall be performed by utilization of Govern

12、ment approved machine standards. units of the sample by the flow detector in the test for body metal soundness shall be cause for rejection of the lot. MIL-STD-105 shall be used to determine sample size (minimun sample size = 315), except for First Article Testing. Rejection of one or more 4.4.3.3 M

13、etal parts security. The occurrence of one or more .- - y- of the following casualties, as witnessed by hole(s) in the fragmentation screen(s) I or recovery of the part(s) or fragment(s) shall be cause for rejection of lot, except as otherwise provided: a. Body breakup. b. Complete rotating band sep

14、aration. This is defined as detachment of all of the band having band seat knurling imprint. c. Partial rotating band separation. This is defined as detachment of part of the band having band seat knurling imprint. d. The following acceptance criteria shall apply to thrown band fragments having no e

15、vidence of band seat knurling imprint: (1) The lot will be accepted if two or less assemblies throw band fragments having a length not greater than 13mm. (2) The lot will be rejected if any assembly throws a band fragment having a length greater than 13mm (indicative of deep-seated band lamination).

16、 (3) The lot will not be penalized for band particles thrown as a result of normal band fringing or slivering. 4.4.3.4 - Phosphate - coating. Failure of the phosphate coating on the standard panels or sample body assemblies to comply with the applicable requirements shall be cause for rejection of a

17、ll projectiles phosphated since the preceding test. 14 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-* DOD-P-63981 13 m 9999906 0352343 4 m DOD-P-63981 (AR) 4.4.3.5 -I RotatfnLband - blank. A rotating band blank which is deformed or judged to lack

18、sufficient metal in any part of its width or thickness to provide for complete band sak fill and minimum rotating band profile dimensions shall be classed defective. 4.4.3.6 9. A .254MM feeler gage shall not enter the gap between rotating band and projectile body, both forward and aft 360. r i 4.4.4

19、 Inspection equipment. The inspection equipment in the tables starting with paragraph 4.4.2.1. The contractor shall submit for approval inspection equipment designs in accordance with the terms of the contract. See section 6 of MIL-A-48078 and 6.3 herein. equired to perform the examinations and test

20、s prescribed herein s described in the “Paragraph Reference/Inspection Method“ column 45 Test methods and procedures. 4.5.1 Band tiqhtness. After sectioning along the -1-1-1- - longitudinal axis, one half of the sectioned projectile body shall be examined for rotating band fill in the undercut areas

21、. Failure of either of the exposed sections to comply with the. 50% fill requirements shall be considered a defect. 4.5.2 -II- Soundness. The procedures for conducting the soundness inspection shall be prepared by the contractor and submitted to the contracting officer for approval. The procedure sh

22、all make provision for the use of defect standards. used in the soundness test will be cycled through the soundness test equipment every shift. Failure of the test equipment to reject the defect standards shall be cause for rejection of assemblies inspected for soundness since the preceding test of

23、the defect standards. 4.5.2.1 -y- Defect standards. As a minimum, the defect standards 4.5.3 - verification. through the soundness inspection equipment at the start and completion of each shift as well as after any adjustment or shutdown of the soundness inspection equipment. Failure of the equipmen

24、t to reject standards shall be cause for rejection of assemblies tested for soundness since the preceding satisfactory test for defect standards. Automatic - inspection - equipment calibration The defect standards for soundness shall be cycled 4.5.4 Phosphate coating. The method of test shall be as

25、prescribed by TT-C-490 for the type of coating used (see Dwg. 9349963). The prescribed panels shall be processed, with the projectiles to be represented, at the start of daily production and at 4-hour intervals, maximum, thereafter. Appearance and weight of the coating shall be recorded. Provided by

26、 IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-DOD-P-63781 13 7777706 0352342 6 M DOD-P-63981 (AR) 4.5.5 Paint adhesion. The method of test shall be prescribed -I- by TT-C-490. The test shall be made on the painted bourrelet of each unit of the sample, forward

27、 of the rotating band. Visible exposure of underlying phosphate coating or ferrous metal of any unit of the sample, as a result of the test, shall be recorded as a defect. 4.5.6 Corrosion resistance. The method of test shall be prescribed in American Society of Testing and Materials (ACTM), ASTM B11

28、7. The Salt spray solution and exposure time shall be as specified in 3.6.3. The method of test shall be as prescribed in AMCR-715-505, Volume 8, as applicable. The target shall be 8 by 8 1“ thick plywood with 1/2“ thick celotex facing. Target shall be located 5 meters + 1 meter from the muzzle. The

29、 test sample shall be assembled to comply with requirements of Dwg. 11823954, Cartridge, 30MM, for projectile metal parts test. The test cartridges shall be fired at ambient temperature in bursts of 25 shots. The gun barrel may be cooled to ambient temperature after each 100 rounds. The cyclic rate

30、of each burst shall be the design cyclic rate. defect is found to have been caused by a defective test weapon, the firing defect shall not be classed as a failure. In such case, the defective test weapons shall be corrected or replaced and the test repeated in whole or in part, as appropriate. If su

31、ch firing defect is not found to have been caused by a defective weapon, it shall be classed as a failure. -I_- 4.5.7 Metal - parts I- security, 4.5.7.1 - Defective weaEons. - If any sample projectile firing 4.5.8 -I- Test gun. - Unless otherwise directed by the Contracting Officer, the metal parts

32、security firing tests shall be conducted in the 30MM, XM230 Gun. 5. PRESERVATION, PACKAGING AND PACKING 5.1 - Packagineand - e- packing - Le- level C. Each lot of projectile metal parts shall be packed using best commercial packaging and packing as approved by the procuring agency. 5.2 Marking - - a

33、nd labeliz. Marking or labeling of packed cartons or containers shall cmply with applicable requirements of MIL-CTD-1169 . 5.3 - Packaqins, packing and marking inspection. Inspection for packaging, packing and container marking shall be in accordance with the quality assurance provisions of MIL-STD-

34、1169. 5.4 - Chippinq. When shipments of more than one lot are made at one time, such as in a carload, each lot shall be kept separate and the division between lots clearly indicted to prevent mixing of the lots in transit. 16 Provided by IHSNot for ResaleNo reproduction or networking permitted witho

35、ut license from IHS-,-,- DOD-P-63981 (AR) 6. NOTES 6.1 -II- Intended use. This specification covers projectile, metal parts and packing for Projectile, 30MM, HEDP, M789. ( 6.2 Ordering data. See MIL-A-48078. P 6.3 Submission of insEection eguiEment design for =proval. - - - - - - See MIL-A-48078. Su

36、bmit equipment design as required to: Commander, ARRADCOM, ATTN: DRDAR-QAF-I, Dover, NJ 07801. Request letter of submittal, state contractor, contractor number, specification number, item nomenclature and classification of defects or test paragraph. 6.4 Submission of results of contractor-conducted

37、examinations and test. Unless otherwise specified by the Contracting Officer, the contractor shall forward requested records of examinations or tests to: Commmander, ARRADCOM, ATTN: DRDAR-QAF-S, Dover, NJ 07801. -I- - 6.5 Submission of test data. In addition to the normal distribution of records, wh

38、en Lhe cartridges are procured by ARRADCOM, one (1) copy of all ballistic data and ammunition data cards shall be forwrded to: Commander, ARRADCOM, ATTN: I- DRDAR-QAF-S , Dover, NJ 07801. 6.6 - First article. When a first article inspection is required, the contracting officer should include specifi

39、c instructions in acquisition documents regarding arrangement for examinations, test and approval of the documents for first article. ! 6.7 I- Process deviation. A process deviation is defined as a change in the approved basic method of manufacture or an operational change which alters the metallurg

40、ical or physical properties of the item of contract. 6.8 _ Projectile - coating - defect criteria. Projectiles indicating exposure of bare metal or underlying phosphate or organic pre-treatment shall be considered unsatisfactory if any of the following conditions exist. a. Any area exceeding 60 squa

41、re millimeters. b. More than one area exceeding 30 square millimeters. c. More than five areas of 15 square millimeters or less. Custodian: Army-AR Preparing activity: Army-AR (Project 1305-A889) 17 *V.S. GOVERNEMNT PRINTING OFFICE: 1982-605-03415642 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-