API TR 6MET-2010 Metallic Material Limits for Wellhead Equipment Used in High Temperature for API 6A and 17D Applications (First Edition)《API 6A标准及API 17D标准高温用井口设备的金属材料限制》.pdf

《API TR 6MET-2010 Metallic Material Limits for Wellhead Equipment Used in High Temperature for API 6A and 17D Applications (First Edition)《API 6A标准及API 17D标准高温用井口设备的金属材料限制》.pdf》由会员分享，可在线阅读，更多相关《API TR 6MET-2010 Metallic Material Limits for Wellhead Equipment Used in High Temperature for API 6A and 17D Applications (First Edition)《API 6A标准及API 17D标准高温用井口设备的金属材料限制》.pdf（46页珍藏版）》请在麦多课文档分享上搜索。

1、Metallic Material Limits for Wellhead Equipment Used in High Temperature for API 6A and 17D ApplicationsAPI TECHNICAL REPORT 6MET FIRST EDITION, OCTOBER 2010Metallic Material Limits for Wellhead Equipment Used in High Temperature for API 6A and 17D ApplicationsUpstream SegmentAPI TECHNICAL REPORT 6M

2、ET FIRST EDITION, OCTOBER 2010Special NotesAPI publications necessarily address problems of a general nature. With respect to particular circumstances, local, state, and federal laws and regulations should be reviewed.Neither API nor any of APIs employees, subcontractors, consultants, committees, or

3、 other assignees make any warranty or representation, either express or implied, with respect to the accuracy, completeness, or usefulness of the information contained herein, or assume any liability or responsibility for any use, or the results of such use, of any information or process disclosed i

4、n this publication. Neither API nor any of APIs employees, subcontractors, consultants, or other assignees represent that use of this publication would not infringe upon privately owned rights.API publications may be used by anyone desiring to do so. Every effort has been made by the Institute to as

5、sure the accuracy and reliability of the data contained in them; however, the Institute makes no representation, warranty, or guarantee in connection with this publication and hereby expressly disclaims any liability or responsibility for loss or damage resulting from its use or for the violation of

6、 any authorities having jurisdiction with which this publication may conflict.API publications are published to facilitate the broad availability of proven, sound engineering and operating practices. These publications are not intended to obviate the need for applying sound engineering judgment rega

7、rding when and where these publications should be utilized. The formulation and publication of API publications is not intended in any way to inhibit anyone from using any other practices.Any manufacturer marking equipment or materials in conformance with the marking requirements of an API standard

8、is solely responsible for complying with all the applicable requirements of that standard. API does not represent, warrant, or guarantee that such products do in fact conform to the applicable API standard.Users of this Technical Report should not rely exclusively on the information contained in thi

9、s document. Sound busi-ness, scientific, engineering, and safety judgment should be used in employing the information contained herein. All rights reserved. No part of this work may be reproduced, translated, stored in a retrieval system, or transmitted by any means, electronic, mechanical, photocop

10、ying, recording, or otherwise, without prior written permission from the publisher. Contact the Publisher, API Publishing Services, 1220 L Street, NW, Washington, DC 20005.Copyright 2010 American Petroleum InstituteForewordNothing contained in any API publication is to be construed as granting any r

11、ight, by implication or otherwise, for the manufacture, sale, or use of any method, apparatus, or product covered by letters patent. Neither should anything contained in the publication be construed as insuring anyone against liability for infringement of letters patent.This document was produced un

12、der API standardization procedures that ensure appropriate notification and participation in the developmental process and is designated as an API standard. Questions concerning the interpretation of the content of this publication or comments and questions concerning the procedures under which this

13、 publication was developed should be directed in writing to the Director of Standards, American Petroleum Institute, 1220 L Street, NW, Washington, DC 20005. Requests for permission to reproduce or translate all or any part of the material published herein should also be addressed to the director.Su

14、ggested revisions are invited and should be submitted to the Standards Department, API, 1220 L Street, NW, Washington, DC 20005, standardsapi.org.iiiContentsPageIntroduction. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

15、 . . . . . . . . . . . . . . . . . . vi1 Scope . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 12 Procedure . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

16、. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 23 Results . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 23.1 Phase I Results . . . . . . . . . . . .

17、. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 23.2 Phase II Results . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 33.3 P

18、hase III Results . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 34 Conclusions . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

19、. . . . . . . . . . . . . . . . 45 Recommendations . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 5Annex A (informative) AISI 4130 Test Results . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

20、 . . . . . . . . . . . . . . . . . . . . . . 10Annex B (informative) AISI 8630 Test Results . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 12Annex C (informative) 21/4 Cr 1 Mo Test Results . . . . . . . . . . . . . . . . . . . . . . . . . .

21、. . . . . . . . . . . . . . . . . . . . . . . . . 14Annex D (informative) AISI 4140 Test Results . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 16Annex E (informative) 410 Stainless Steel Test Results . . . . . . . . . . . . . . . . . . . .

22、. . . . . . . . . . . . . . . . . . . . . . . . . 18Annex F (informative) F6NM Test Results. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 20Annex G (informative) 25 Chrome Super Duplex Test Results. . . . . . . . . . . . . . . . . .

23、. . . . . . . . . . . . . . . . . . . . . . 22Annex H (informative) ASTM A453 Gr. 660 Test Results. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 24Annex I (informative) 718 (per Spec 6A718) Test Results . . . . . . . . . . . . . . . . . . . . . . . . . . .

24、. . . . . . . . . . . . . . . . . 26Annex J (informative) 725/625 Plus Test Results. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 28Annex K (informative) 925 Test Results . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

25、. . . . . . . . . . . . . . . . . . . . . 30Bibliography . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 32Figure1 AISI 8630 Strength Reduction with Temperature. . . . . . . . . . . . . .

26、. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 3Tables1 List of Alloys Included in Phase I Testing . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 12 List of Alloys Included in Phase II Testing . . . . . . . . . . . . . . . .

27、 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 13 List of Alloys Included in Phase III Testing . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 14 Recommended Yield Strength Reduction Ratios in Percent by Temperature . .

28、. . . . . . . . . . . . . . . . . . . . . 45 Yield Strength Reduction Factors in Percent by Temperature (from Literature) . . . . . . . . . . . . . . . . . . . . . 46 Alloy Composition for AISI 4130 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

29、 . . . . . . . . . 57 Alloy Composition for 8630M. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 58 Alloy Composition for 21/4Cr-1Mo (F22). . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

30、. . . . . . . . . . . . 59 Alloy Composition for AISI 4140 Test Material. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 610 Alloy Composition for 410 Stainless Steel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

31、. . . . . . . . . . 611 Alloy Composition for F6NM Stainless Steel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 612 Alloy Composition for 25Cr Super Duplex . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

32、 . . . . . . . 713 Alloy Composition for ASTM A453 Gr 660 Precipitation Hardened Austenitic Stainless Steel . . . . . . . . . 714 Alloy Composition for Nickel Alloy 718 (per Spec 6A718) . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 8vContentsPage15 Alloy Composition f

33、or Nickel Alloys 725 and 625 Plus. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 816 Alloy Composition for Nickel Alloy 925 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 9A.1 AISI 4130 Test Results. . .

34、 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 10A.1 Plot of 4130 Test Results . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 11B.1 A

35、ISI 8630 Test Results. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 12B.1 Plot of 8630 Test Results . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

36、 . . . . . . . . . 13C.1 21/4 Cr 1 Mo Test Results . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 14C.1 Plot of 21/4 Cr 1 Mo Test Results. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

37、. . . . . . . . . . . . . . . . . . . 15D.1 AISI 4140 Test Results. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 16D.1 Plot of AISI 4140Test Results . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

38、. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 17E.1 AISI 410 Test Results. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 18E.1 Plot of AISI 410 Stainless Steel Test Results . . . . . . . . . . .

39、 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 19F.1 F6NM Test Results. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 20F.1 Plot of F6NM Test Results . . . . . . . . . . . . .

40、. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 21G.1 25 Chrome Super Duplex Test Results . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 22G.1 Plot of 25 Chrome Super Duplex Test Result

41、s. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 23H.1 ASTM A453 Gr. 660 Test Results . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 24H.1 Plot of ASTM A453 Gr. 660 Test Results . .

42、 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 25I.1 718 (per Spec 6A718) Test Results . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 26I.1 Plot of 718 (per Spec 6A718) Test Res

43、ults . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 27J.1 725/625 Plus Test Results. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 28J.1 Plot of 725/625 Plus Test

44、Results. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 29K.1 925 Test Results. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 30K.1 P

45、lot of 925 Test Results . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 31IntroductionThis API-funded project was conducted by a Task Group charged by the Association of Well Head Equipment Manufacturers (AWHEM). The

46、 Task Group examined mechanical properties of metallic materials used for API 6A and API 17D wellhead equipment for service above 250 F. A total of eleven different alloys meeting API 6A, PSL 3 conditions were supplied “in condition” by a variety of suppliers. Materials in this test program included

47、 alloys common to the oil and gas industry. The alloys tested included low alloy steels, martensitic, precipitation hardened and duplex stainless steels, and nickel alloys. Yield strength reduction ratios at temperatures of 300 F, 350 F, 400 F, and 450 F are reported. As a result of testing, yield s

48、trength reduction ratios at 300 F to 450 F ranged from 92 % to 87 % for the low alloy steels, 92% to 88% for the martensitic stainless steels 81 % to 73 % for super duplex, 99 % to 89 % for the precipitation hardened stainless steel and 94 % to 89 % for the nickel alloys. The reported results repres

49、ent an average over the different heats for each type of material. These results are intended to expand the data shown in API 6A, Annex G.vi1Metallic Material Limits for Wellhead Equipment Used in High Temperature for API 6A and 17D Applications1 ScopeTesting was performed in three phases, presented herein in chronological order as Phase I, II, and III. Initially, all testing was to be completed in two phases, but testing anomalies in Phase II prompted re-testing of some alloys in Phase III.Alloy candidates were recommended by AWHEM membership for analysis and confirmed by APIs ap