ISO 8336-2017 Fibre-cement flat sheets - Product specification and test methods《纤维水泥平板 产品规范和试验方法》.pdf

《ISO 8336-2017 Fibre-cement flat sheets - Product specification and test methods《纤维水泥平板 产品规范和试验方法》.pdf》由会员分享，可在线阅读，更多相关《ISO 8336-2017 Fibre-cement flat sheets - Product specification and test methods《纤维水泥平板 产品规范和试验方法》.pdf（54页珍藏版）》请在麦多课文档分享上搜索。

1、 ISO 2017 Fibre-cement flat sheets Product specification and test methods Plaques planes en fibres-ciment Spcification des produits et mthodes dessai INTERNATIONAL STANDARD ISO 8336 Third edition 2017-06 Reference number ISO 8336:2017(E) ISO 8336:2017(E)ii ISO 2017 All rights reserved COPYRIGHT PROT

2、ECTED DOCUMENT ISO 2017, Published in Switzerland All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without pri

3、or written permission. Permission can be requested from either ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Ch. de Blandonnet 8 CP 401 CH-1214 Vernier, Geneva, Switzerland Tel. +41 22 749 01 11 Fax +41 22 749 09 47 copyrightiso.org www.iso.org IS

4、O 8336:2017(E)Foreword v Introduction vi 1 Scope . 1 2 Normative references 1 3 Terms and definitions . 2 4 Symbols and abbreviated terms . 4 5 Requirements 5 5.1 General . 5 5.2 Sheet classifications 5 5.2.1 Category A . 5 5.2.2 Category B 6 5.2.3 Category C 6 5.3 Composition and manufacture 6 5.3.

5、1 General 6 5.3.2 Reinforcement fibre 6 5.3.3 Cement 6 5.3.4 Manufacture . 6 5.4 Appearance and finish 6 5.5 Dimensions and tolerances 6 5.5.1 Nominal length and width . 6 5.5.2 Thickness 7 5.5.3 Tolerances on nominal dimensions and shape 7 5.6 Physical requirements and characteristics . 8 5.6.1 Gen

6、eral 8 5.6.2 Modulus of rupture 9 5.6.3 Apparent density . 9 5.6.4 Moisture movement 9 5.6.5 Water permeability 9 5.6.6 Water vapour transmission .10 5.6.7 Thermal conductivity . .10 5.6.8 Freeze-thaw performance 10 5.6.9 Heat-rain performance 10 5.6.10 Warm water performance 10 5.6.11 Soak-dry perf

7、ormance .10 5.6.12 Resistance to mould growth .10 5.6.13 Resistance to nail head pull-through .11 5.6.14 Saturated shear bond performance 11 5.6.15 Surface burning characteristics .11 5.7 Fire properties . .11 5.8 Product performance .11 6 Evaluation of conformity .12 6.1 General 12 6.2 Type testing

8、 12 6.2.1 General.12 6.2.2 Initial type testing 13 6.2.3 Further type testing .13 6.3 Quality control system.14 6.3.1 General.14 6.3.2 Acceptance tests 14 6.3.3 Equipment 15 6.3.4 Raw materials and components 15 6.3.5 Product testing and evaluation .15 ISO 2017 All rights reserved iii Contents Page

9、ISO 8336:2017(E)6.3.6 Non-conforming products 15 6.4 Inspection of a consignment of finished products 15 7 Test requirements 15 7.1 General 15 7.2 Dimensional and geometrical tests 15 7.2.1 General.15 7.2.2 Number of measurements 16 7.3 Physical performance tests .16 7.3.1 Modulus of rupture .16 7.3

10、.2 Apparent density 17 7.3.3 Moisture movement test 17 7.3.4 Water permeability .18 7.3.5 Freeze-thaw test 18 7.3.6 Heat-rain test .18 7.3.7 Warm water test 19 7.3.8 Soak-dry test .19 7.3.9 Mould testing .19 7.3.10 Nail head pull-through .20 7.3.11 Saturated shear bond test .20 8 Marking .20 Annex A

11、 (normative) Consignment and inspection sampling .21 Annex B (normative) Statistical method for determining the corresponding wet values or revised dry specifications for the MOR when making the dry method of test or when tested prior to coating for quality control purposes .22 Annex C (normative) D

12、imensional measurement and geometrical testing procedure 26 Annex D (normative) Test method for the determination of fibre-cement sheet modulus of rupture (bending strength) 30 Annex E (normative) Test method for the determination of the apparent density of fibre- cement sheets .34 Annex F (normativ

13、e) Test method for the determination of moisture movement characteristic of fibre-cement sheets 36 Annex G (normative) Test method for the determination of water permeability of fibre- cement sheets .38 Annex H (normative) Test method for the evaluation of freeze-thaw performance of fibre- cement sh

14、eets .39 Annex I (normative) Test method for the evaluation of heat-rain performance of fibre- cement sheets .41 Annex J (normative) Test method for warm water evaluation of fibre-cement sheets .43 Annex K (normative) Test method for soak-dry evaluation test of fibre-cement sheets 45 Bibliography .4

15、7 iv ISO 2017 All rights reserved ISO 8336:2017(E) Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Eac

16、h member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the Internation

17、al Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. The procedures used to develop this document and those intended for its further maintenance are described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the differen

18、t types of ISO documents should be noted. This document was drafted in accordance with the editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/ directives). Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shal

19、l not be held responsible for identifying any or all such patent rights. Details of any patent rights identified during the development of the document will be in the Introduction and/or on the ISO list of patent declarations received (see www .iso .org/ patents). Any trade name used in this documen

20、t is information given for the convenience of users and does not constitute an endorsement. For an explanation on the voluntary nature of standards, the meaning of ISO specific terms and expressions related to conformity assessment, as well as information about ISOs adherence to the World Trade Orga

21、nization (WTO) principles in the Technical Barriers to Trade (TBT), see the following URL: w w w . i s o .org/ iso/ foreword .html. This document was prepared by Technical Committee ISO/TC 77, Products in fibre reinforced cement. This third edition cancels and replaces the second edition (ISO 8336:2

22、009), which has been technically revised. ISO 2017 All rights reserved v ISO 8336:2017(E) Introduction The purpose of this document is to provide manufacturers and purchasers with uniform requirements for fibre-cement flat sheet products. These requirements are performance-based and have been specif

23、ied with the objective of ensuring product quality, industry efficiency and the performance of the product in service. ISO/TC 77 aims to harmonize this document, where possible, with other national fibre-cement standards (CEN, ASTM and JIS) to facilitate and promote uniform performance benchmarks fo

24、r the global use of fibre-cement products.vi ISO 2017 All rights reserved Fibre-cement flat sheets Product specification and test methods 1 Scope This document specifies methods for the inspection and testing of fibre-cement flat sheets and provides the acceptance conditions for their use in one or

25、more of the following applications: external wall and ceiling finishes; internal wall and ceiling finishes; internal and external backing sheets. Products covered by this document can be used for other purposes, provided they comply with the appropriate national or international application code or

26、standard. NOTE 1 This document does not apply to sheets for fire protection purposes. NOTE 2 This document does not include calculations for installation design requirements, wind uplift or water proofing of the installed sheets. NOTE 3 This document does not apply to the following products: boards

27、of Portland or equivalent cement reinforced with fibrous wood particles; fibre-reinforced boards of calcium silicate or cement for thermal insulation or fire protection; sheets containing asbestos fibre reinforcement; sheets containing steel fibre reinforcement; fibre-cement roofing slates. 2 Normat

28、ive references The following documents are referred to in the text in such a way that some or all of their content constitutes requirements of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any ame

29、ndments) applies. ISO 390, Products in fibre-reinforced cement Sampling and inspection ISO 12572, Hygrothermal performance of building materials and products Determination of water vapour transmission properties Cup method ISO 13787, Thermal insulation products for building equipment and industrial

30、installations Determination of declared thermal conductivity ANSI A118.1, Specification for Dry-Set Portland Cement Mortar ANSI A118.4, Specification for Latex-Portland Cement Mortar ANSI A136.1, Organic Adhesives for Installation of Ceramic Tile A S T M G 2 1 : 2 0 15 , Standard Practice for determ

31、ining Resistance of Synthetic Polymeric Materials to Fungi ASTM D1037, Standard Test Methods for Evaluating Properties of Wood-Base Fiber and Particle Panel Materials INTERNATIONAL ST ANDARD ISO 8336:2017(E) ISO 2017 All rights reserved 1 ISO 8336:2017(E) ASTM E84, Standard Test Method for Surface B

32、urning Characteristics of Building Materials 3 Terms and definitions For the purposes of this document, the following terms and definitions apply. ISO and IEC maintain terminological databases for use in standardization at the following addresses: IEC Electropedia: available at h t t p :/ www .elect

33、ropedia .org/ ISO Online browsing platform: available at h t t p :/ www .iso .org/ obp 3.1 acceptance test test to establish whether a batch of sheets conforms to a specification Note 1 to entry: The test is performed on samples drawn from continuous production or from a consignment (see ISO 390). N

34、ote 2 to entry: Test methods, specifications and limit values are specified in this document. Sampling levels and acceptance criteria are specified in Clause 6. 3.2 type test test carried out to demonstrate conformity with the requirements of this document or for the approval of a new product and/or

35、 when a fundamental change is made in formulation and/or method of manufacture, the effects of which cannot be predicted on the basis of previous experience Note 1 to entry: The test is performed on the as-delivered product, but is not required for each production batch. 3.3 acceptable quality level

36、 AQL maximum percent defective (or maximum number of defects per 100 units) which can be considered satisfactory as a long-term average quality level in a sampling plan Note 1 to entry: When a manufacturers process satisfies a sampling scheme with an AQL of 4 %, this indicates that 96 % of the inspe

37、cted product exceeds the specification. This type of specification provides the consumer with a clearly defined lower quality boundary; this does not occur if acceptance is based solely on the average value of the measured property. Examples of sampling schemes can be found in ISO 390, ISO 2859-1, o

38、r ISO 3951 (all parts). 3.4 apparent density dry weight/unit volume based upon the volume of the sample determined by water displacement or equivalent Note 1 to entry: This is an average density of the material as-delivered coated or uncoated. 3.5 as delivered same condition as the producer intends

39、to supply the product after completing all aspects of the process including maturing and, when appropriate, painting 3.6 upper face face normally exposed 3.7 under face reverse of the upper face (3.6)2 ISO 2017 All rights reserved ISO 8336:2017(E) 3.8 textured sheet sheet that has a relief pattern w

40、hich is either embossed on or applied to the upper face (3.6) as a coating 3.9 reinforcement fibre discrete randomly dispersed elements or continuous strands of cellulose fibre, synthetic organic, inorganic fibre or glass fibre, used in the manufacture of fibre-cement sheets 3.10 small-sized sheet s

41、heet for which the method of installation includes horizontal overlap Note 1 to entry: Their dimensions are generally such that they have an area of 7 normally used as horizontal overlapping wall covering 3.13 aspect ratio ratio of the sheet length to the sheet width 3.14 modulus of rupture MOR maxi

42、mum load/unit area of cross section at breaking, under flexural loading conditions Note 1 to entry: The modulus of rupture is referred to as the bending strength or flexural strength in some countries. 3.15 quality controlpart of quality management to ensure the product being manufactured meets stat

43、ed requirements Note 1 to entry: This is referred to as factory production control (FPC) in some countries. 3.16 ambient laboratory condition laboratory condition where the temperature is at (23 10) C and (50 20) % relative humidity ISO 2017 All rights reserved 3 ISO 8336:2017(E) 4 Symbols and abbre

44、viated terms a nominal length or width of sheet, in mm b a) dimension of the specimen (length or width) measured parallel to the test machine supports, in mm b) one of the coefficients of the regression line (see Annex B) d apparent density of the sheet, in g/cm 3 e thickness of sheet, in mm F break

45、ing load, modulus of rupture test, in N l length, in mm L m length of moisture movement specimen, in mm l s span between support centres in modulus of rupture test, in mm m mass of the specimen after drying, in g MOR modulus of rupture, in MPa MOR fi modulus of rupture of i thexposed specimen after

46、the type test MOR fci modulus of rupture of i thunexposed reference specimen MOR i individual ratio of the modulus of rupture of the i thpair of exposed and unexposed specimens n number of paired specimens R average ratio of the modulus of rupture of exposed and unexposed specimens R L lower estimat

47、e of the mean of the ratios at 95 % confidence level of the modulus of rupture of exposed and unexposed specimens s standard deviation of the values in the appropriate calculation water vapour transmission value thermal conductivity V volume of specimen, in cm 3 w width, in mm x i individual value o

48、f the i thspecimen tested dry x std minimum value to be used as the specification for the dry test method of test. This value is calculated at the 97,5 % lower confidence level from the value specified for the wet method of test (see Annex B) x 0 actual result obtained when dry testing (see Annex B)

49、 x mean value of x ifor i = 1 to n y i individual value of the i thspecimen tested wet4 ISO 2017 All rights reserved ISO 8336:2017(E) y std minimum value specified in the standard for wet testing (see Annex B) y 0 value calculated from the value obtained from a specimen tested dry, which is the estimate at the 97,5 % lower confidence level of the value expected from a specimen tested wet (see Annex B) y mean value of y ifor i = 1 to n NT new technology (European term for asbestos-free fibre-cement produc