ISO 6363-2-2012 Wrought aluminium and aluminium alloys - Cold-drawn rods bars and tubes and wires - Part 2 Mechanical properties《加工铝和铝合金冷拉棒 条材和管材 第2部分 力学性能》.pdf

《ISO 6363-2-2012 Wrought aluminium and aluminium alloys - Cold-drawn rods bars and tubes and wires - Part 2 Mechanical properties《加工铝和铝合金冷拉棒 条材和管材 第2部分 力学性能》.pdf》由会员分享，可在线阅读，更多相关《ISO 6363-2-2012 Wrought aluminium and aluminium alloys - Cold-drawn rods bars and tubes and wires - Part 2 Mechanical properties《加工铝和铝合金冷拉棒 条材和管材 第2部分 力学性能》.pdf（24页珍藏版）》请在麦多课文档分享上搜索。

1、 ISO 2012 Wrought aluminium and aluminium alloys Cold-drawn rods/bars and tubes and wires Part 2: Mechanical properties Aluminium et alliages daluminium corroys Barres, tubes et fils tirs froid Partie 2: Caractristiques mcaniques INTERNATIONAL STANDARD ISO 6363-2 Second edition 2012-07-15 Reference

2、number ISO 6363-2:2012(E) ISO 6363-2:2012(E) ii ISO 2012 All rights reserved COPYRIGHT PROTECTED DOCUMENT ISO 2012 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying

3、and microfilm, without permission in writing from either ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland

4、ISO 6363-2:2012(E) ISO 2012 All rights reserved iii Contents Page Foreword iv 1 Scope 1 2 Normative references . 1 3 T erms and definitions . 1 4 Tensile testing 1 5 Mechanical properties 1 Annex A (normative) Rules for rounding .15 Annex B (normative) List of tempers used in Tables 1 and 2 .16 Bibl

5、iography .18 ISO 6363-2:2012(E) Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body inter

6、ested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and nongovernmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical

7、Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the tec

8、hnical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO

9、 shall not be held responsible for identifying any or all such patent rights. ISO 6363-2 was prepared by Technical Committee ISO/TC 79, Light metals and their alloys, Subcommittee SC 6, Wrought aluminium and aluminium alloys. This second edition cancels and replaces the first edition (ISO 6363-2:199

10、3) which has been technically revised. ISO 6363 consists of the following parts, under the general title Wrought aluminium and aluminium alloys Cold-drawn rods/bars, tubes and wires: Part 1: Technical conditions for inspection and delivery Part 2: Mechanical properties Part 3: Drawn round bars and w

11、ires Tolerances on form and dimensions (symmetric plus and minus tolerances on diameter) Part 4: Drawn rectangular bars and wires Tolerances on form and dimensions Part 5: Drawn square and hexagonal bars and wires Tolerances on form and dimensions Part 6: Drawn round tubes Tolerances on form and dim

12、ensions iv ISO 2012 All rights reserved INTERNATIONAL STANDARD ISO 6363-2:2012(E) Wrought aluminium and aluminium alloys Cold-drawn rods/ bars and tubes and wires Part 2: Mechanical properties 1 Scope This part of ISO 6363 specifies the mechanical properties of wrought aluminium and aluminium alloy

13、rods/bars, tubes and wires for general engineering applications (except aeronautical rivets). It applies to products which are extruded and then cold drawn. It does not apply to: products which are rolled and then cold drawn, including seam-welded tubes; forging stock, wire for drawing stock; drawn

14、wires for aeronautical application, electrical or welding purposes. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced doc

15、ument (including any amendments) applies. ISO 6363-1, Wrought aluminium and aluminium alloys Cold-drawn rods/bars, tubes and wires Part 1: Technical conditions for inspection and delivery ISO 6892-1, Metallic materials Tensile testing Part 1: Method of test at room temperature ASTM B557M, Standard T

16、est Methods for Tension Testing Wrought and Cast Aluminum- and Magnesium- Alloy Products 3 T erms and definitio ns For the purposes of this document, the terms and definitions given in ISO 6363-1 apply. 4 Tensile testing For the selection of the specimens and tensile testing, use ISO 6892-1 or ASTM

17、B557M. 5 Mechanical properties Values for mechanical properties of aluminium and aluminium alloys are given in Tables 1 and 2. For elongation, two different gauge lengths are used. The choice of the gauge length for elongation measurements (A or A 50mm ) is at the discretion of the producer, unless

18、otherwise agreed. NOTE A is the percentage elongation on a gauge length of 5,65 S o A 50mmis the percentage elongation on a gauge length of 50 mm. ISO 2012 All rights reserved 1 ISO 6363-2:2012(E) Test results shall be rounded in accordance with the rules given in Annex A. Table 1 Mechanical propert

19、ies of rods/bars and wires Alloy Temper Dimensions a Tensile strength R mMPa 0,2 % proof stress R p0,2MPa Elongationmin. min. max. min. max. A % A 50mm% 1050 O D or S 3 60 100 3 D or S 100 60 100 20 25 H14 D or S 10 95 H18 D or S 10 125 1050A O D or S 30 60 20 25 H14 D or S 30 100 70 6 5 H16 D 15 or

20、 S 5 120 160 105 4 3 H18 D or S 10 130 110 3 1070 O D or S 3 55 95 3 D or S 100 55 95 15 25 H14 D or S 10 85 H18 D or S 10 120 1080A O D 20 80 H14 D 18 90 H18 D 10 120 1098 O D 20 70 H14 D 18 85 H18 D 10 115 1100 O D or S 3 75 110 3 D or S 100 75 110 20 22 25 H14 D or S 30 110 80 b 5 H18 D or S 10 1

21、50 130 b 3 1200 O D or S 3 75 110 3 D or S 30 75 110 30 20 25 30 D or S 100 75 110 20 25 H14 D or S 30 110 80 5 H16 D 15 or S 5 135 170 115 3 3 2007 T3 D or S 30 370 240 7 5 30 D or S 80 340 220 6 T351 D or S 80 370 240 5 3 2011 T3 3 D or S 38 310 260 9 10 38 D or S 50 295 235 10 12 50 D or S 80 280

22、 205 10 14 T8 3 D or S 80 370 270 8 10 H13 D 18 155 225 H18 D 10 240 2 ISO 2012 All rights reserved ISO 6363-2:2012(E) Alloy Temper Dimensions a Tensile strength R mMPa 0,2 % proof stress R p0,2MPa Elongationmin. min. max. min. max. A % A 50mm% 2011A T3 D or S 40 320 270 10 8 40 D or S 50 300 250 10

23、 50 D or S 80 280 210 10 T8 D or S 80 370 270 8 6 2014 O 3 D or S 100 245 12 T3 D or S 80 380 290 8 6 T351 D or S 80 380 290 6 4 T4 T42 c T451 3 D or S 100 380 220 10 16 T6 T62 d T651 3 D or S 100 450 380 7 8 2014A O H111 D or S 80 240 125 12 10 H13 e D 18 210 280 H18 D 10 295 T3 D or S 80 380 290 8

24、 6 T351 D or S 80 380 290 6 4 T4 T451 D or S 100 380 220 10 10 T6 D or S 50 440 360 7 8 T651 D or S 100 450 380 7 8 2017 O D or S 3 245 3 D or S 100 245 16 H13 3 D or S 10 205 275 T4 T42 c D or S 3 380 3 D or S 100 380 225 12 2017A O H111 D or S 80 240 125 12 10 H13 e D 18 210 300 H18 D 10 315 T3 D

25、or S 80 400 250 10 8 T351 D or S 80 400 250 8 6 T4 T451 D or S 50 380 220 10 50 D or S 100 390 235 10 Table 1 (continued) ISO 2012 All rights reserved 3 ISO 6363-2:2012(E) Alloy Temper Dimensions a Tensile strength R mMPa 0,2 % proof stress R p0,2MPa Elongationmin. min. max. min. max. A % A 50mm% 21

26、17 H13 e D or S 18 170 240 H15 3 D or S 10 195 245 H18 D 18 260 T4 3 D or S 10 265 125 18 2024 O f H111 D or S 3 245 3 D or S 100 245 16 H13 e D 18 230 300 H18 D 10 320 T3 D or S 10 425 310 10 8 10 D or S 80 425 290 9 7 T351 12,5 D or S 100 425 310 9 T4 T451 D or S 3 425 3 D or S 12 425 310 10 10 12

27、 D or S 100 425 290 9 10 T42 c D or S 3 430 3 D or S 100 430 275 10 T6 D or S 80 425 315 5 4 T651 D or S 80 425 315 4 3 T62 d D or S 3 410 3 D or S 100 410 315 5 T8 D or S 80 455 400 4 3 T851 D or S 80 455 400 3 2 2030 T3 D or S 50 370 250 7 50 D or S 100 340 210 7 T351 D or S 80 370 240 5 3 2219 T8

28、51 10 D or S 50 400 275 3 50 D or S 100 395 270 3 3003 O D or S 3 95 125 3 D or S 100 95 125 35 22 25 H12 D or S 10 115 80 b 7 b H14 D or S 10 135 110 b 6 b H16 D 15 or S 5 160 130 b 3 b H18 D or S 10 180 145 b 2 b 3103 O D or S 50 95 35 22 19 H14 D or S 30 130 90 6 4 H16 D 15 or S 5 160 195 130 4 3

29、 H18 D or S 10 160 130 4 3 Table 1 (continued) 4 ISO 2012 All rights reserved ISO 6363-2:2012(E) Alloy Temper Dimensions a Tensile strength R mMPa 0,2 % proof stress R p0,2MPa Elongationmin. min. max. min. max. A % A 50mm% 5005 O H111 D 80 or S 60 100 145 40 18 16 H14 D 40 or S 10 140 110 6 4 H18 D

30、15 or S 2 185 155 4 2 5005A O H111 D 80 or S 60 100 145 40 18 16 H14 D 40 or S 10 140 110 6 4 H18 D 15 or S 2 185 155 4 2 5019 O H111 D 80 or S 60 250 320 110 16 14 H12 H22 H32 D 40 or S 25 270 350 180 8 7 H14 H24 H34 D 25 or S 10 300 210 4 3 5041 O D or S 25 225 20 5050 O D or S 10 125 180 25 22 H3

31、2 D or S 10 150 H34 D or S 10 170 H36 D or S 10 185 H38 D or S 10 200 5051A O D 20 195 H12 D 18 170 220 H14 D 18 195 245 H18 D 10 245 5052 O H111 D or S 3 170 220 3 D or S 100 170 220 65 22 25 H32 3 D or S 10 215 255 H14 D or S 3 235 3 D or S 30 235 180 5 H34 D or S 3 235 3 D or S 30 235 180 6 b H16

32、 H26 H36 D or S 15 250 290 200 3 3 H18 D or S 10 270 220 2 H38 D or S 10 270 220 b 2 b Table 1 (continued) ISO 2012 All rights reserved 5 ISO 6363-2:2012(E) Alloy Temper Dimensions a Tensile strength R mMPa 0,2 % proof stress R p0,2MPa Elongationmin. min. max. min. max. A % A 50mm% 5056 O D or S 3 3

33、15 3 D or S 100 250 320 110 16 20 H12 H32 D or S 10 300 H34 D or S 10 345 H38 D or S 10 380 5083 O D or S 3 275 355 3 D or S 100 275 355 110 14 14 H111 D or S 50 270 140 12 H12 D or S 30 300 200 4 5086 O D or S 50 240 95 16 H12 D or S 25 270 190 4 H32 D or S 25 270 190 5 5154 O D or S 10 205 285 75

34、20 16 H32 D or S 10 250 H34 D or S 10 270 H36 D or S 10 290 H38 D or S 10 310 5251 O H111 D 80 or S 60 150 200 60 17 15 H14 H24 H34 D 30 or S 5 200 240 160 5 4 H18 H28 H38 D 20 or S 3 240 200 2 2 5754 O D or S 50 180 80 16 H14 D or S 30 250 180 4 H34 D or S 30 250 180 5 H18 D or S 10 280 240 2 H38 D

35、 or S 10 280 240 3 6012 T4 g D or S 80 200 100 10 8 T6 g D or S 80 310 260 8 6 6056 H13 d D 18 160 240 H18 D 10 240 T39 i D 6 400 T39 i D 6 360 T4 D 20 300 380 T6 D 20 400 T89 i D 6 420 Table 1 (continued) 6 ISO 2012 All rights reserved ISO 6363-2:2012(E) Alloy Temper Dimensions a Tensile strength R

36、 mMPa 0,2 % proof stress R p0,2MPa Elongationmin. min. max. min. max. A % A 50mm% 6060 T39 i D 6 220 T39 i D 6 270 T4 g D or S 80 130 65 15 13 T6 g D or S 80 215 160 12 10 T89 i D 6 260 6061 O f D or S 3 145 3 D or S 100 145 18 H13 h 3 D or S 10 155 205 H18 D 10 210 T39 D 6 310 6 D 260 T4 D or S 3 2

37、05 3 D or S 100 205 110 16 18 T42 c D or S 3 205 3 D or S 100 205 95 18 T6 T62 d D or S 3 290 3 D or S 100 290 240 9 10 T89 i D 6 300 6063 T39 i D 6 230 T39 i D 6 280 T4 g D or S 80 150 75 15 13 T6 g D or S 80 220 190 10 8 T66 g D or S 80 230 195 10 8 T89 i D 6 270 6063A O H111 D or S 80 140 15 13 T

38、4 g D or S 80 150 90 16 14 T6 g D or S 80 230 190 9 7 6065 T6 g D 120 or S 85 290 240 10 8 T8 g D 120 or S 85 345 315 4 3 T9 g D 120 or S 85 360 330 4 3 6082 O D or S 80 160 110 15 H13 h D 18 165 225 H18 D 10 220 T39 i D 6 360 T39 i 6 D 310 T4 D or S 80 205 110 14 T6 D or S 80 310 255 10 T8 D or S 8

39、0 310 260 8 T89 i D 6 340 Table 1 (continued) ISO 2012 All rights reserved 7 ISO 6363-2:2012(E) Alloy Temper Dimensions a Tensile strength R mMPa 0,2 % proof stress R p0,2MPa Elongationmin. min. max. min. max. A % A 50mm% 6181 T4 D or S 50 200 100 15 T6 D or S 50 280 240 8 6262 T6 D or S 100 290 240

40、 8 7 T8 g D or S 50 345 315 4 3 T9 D or S 50 360 330 4 5 50 D or S 80 345 315 4 6262A T6 g D 120 or S 85 290 240 10 8 T8 g D 120 or S 85 345 315 4 3 T9 g D 120 or S 85 360 330 4 3 7020 T5 T6 D or S 50 350 280 10 7022 T6 g D or S 80 460 380 8 6 7049A T6 D 80 590 500 7 7075 O f 3 D or S 100 275 10 H13

41、 h D 18 230 310 H18 D 10 285 T6 T62 d T651 3 D or S 100 520 460 6 7 T73 D or S 100 470 385 9 7 aD (mm) = diameter for round bar. S (mm) = width across flats for square and hexagonal bar, thickness for rectangular bar. bGuaranteed values agreed upon between the purchaser and the supplier where reques

42、ted by the purchaser. cThe mechanical properties of temper grade T42 shall be applied only where the material of temper grade O has been naturally age-hardened after solution treatment by the purchaser. If the material is cold or hot worked prior to solution treatment by the purchaser, its mechanica

43、l properties may be lower than the specified values. dThe mechanical properties of temper grade T62 shall be applied only where the material of temper grade O has been artificially age-hardened after solution treatment by the purchaser. If the material is cold or hot worked prior to solution treatment by the purchaser, its mechanical properties may be lower than the specified values. eMe