ISO 6362-3-2012 Wrought aluminium and aluminium alloys - Extruded rods bars tubes and profiles - Part 3 Extruded rectangular bars - Tolerances on shape and dime.pdf

《ISO 6362-3-2012 Wrought aluminium and aluminium alloys - Extruded rods bars tubes and profiles - Part 3 Extruded rectangular bars - Tolerances on shape and dime.pdf》由会员分享，可在线阅读，更多相关《ISO 6362-3-2012 Wrought aluminium and aluminium alloys - Extruded rods bars tubes and profiles - Part 3 Extruded rectangular bars - Tolerances on shape and dime.pdf（12页珍藏版）》请在麦多课文档分享上搜索。

1、 ISO 2012 Wrought aluminium and aluminium alloys Extruded rods/bars, tubes and profiles Part 3: Extruded rectangular bars Tolerances on shape and dimensions Aluminium et alliages daluminium corroys Barres, tubes et profils fils Partie 3: Barres rectangulaires files Tolrances sur forme et dimensions

2、INTERNATIONAL STANDARD ISO 6362-3 Third edition 2012-07-01 Reference number ISO 6362-3:2012(E) ISO 6362-3:2012(E) ii ISO 2012 All rights reserved COPYRIGHT PROTECTED DOCUMENT ISO 2012 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any fo

3、rm or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09

4、 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland ISO 6362-3:2012(E) ISO 2012 All rights reserved iii Contents Page Foreword iv 1 Scope 1 2 Normative references . 1 3 Terms and definitions . 1 4 Materials . 1 5 Tolerances on shape and dimensions . 2 5.1 Dimensional tolerances . 2

5、5.2 Shape tolerances . 3 ISO 6362-3:2012(E) Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each membe

6、r body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Elec

7、trotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopt

8、ed by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of paten

9、t rights. ISO shall not be held responsible for identifying any or all such patent rights. ISO 6362-3 was prepared by Technical Committee ISO/TC 79, Light metals and their alloys, Subcommittee SC 6, Wrought aluminium and aluminium alloys. This third edition cancels and replaces the second edition (I

10、SO 6362-3:2001), which has been technically revised. ISO 6362 consists of the following parts, under the general title Wrought aluminium and aluminium alloys Extruded rods/bars, tubes and profiles: Part 1: Technical conditions for inspection and delivery Part 2: Mechanical properties Part 3: Extrude

11、d rectangular bars Tolerances on shape and dimensions Part 4: Profiles Tolerances on shape and dimensions Part 5: Round, square and hexagonal bars Tolerances on shape and dimensions Part 6: Round, square, rectangular and hexagonal tubes Tolerances on shape and dimensions Part 7: Chemical composition

12、 iv ISO 2012 All rights reserved INTERNATIONAL STANDARD ISO 6362-3:2012(E) Wrought aluminium and aluminium alloys Extruded rods/ bars, tubes and profiles Part 3: Extruded rectangular bars Tolerances on shape and dimensions 1 Scope This part of ISO 6362 specifies the tolerances on dimensions and shap

13、e of wrought aluminium and aluminium alloy extruded rectangular bars, having thicknesses in the range from 2 mm up to 240 mm and widths in the range from 10 mm up to 600 mm. It applies to extruded rectangular bars. 2 Normative references The following referenced documents are indispensable for the a

14、pplication of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 6362-1, Wrought aluminium and aluminium alloys Extruded rods/bars, tubes and profiles Part 1: Technical con

15、ditions for inspection and delivery 3 Terms and definitions For the purposes of this document, the terms and definitions given in ISO 6362-1 apply. 4 Materials For the purposes of this part of ISO 6362, wrought aluminium and aluminium alloys are divided into two groups, which correspond to varying d

16、ifficulty when manufacturing the products. The division into Group I and Group II of the most commonly used general engineering alloys is specified in Table 1. Grouping of other alloys is subject to agreement between the purchaser and supplier. Table 1 Alloy group Group I 1070, 1070A, 1060, 1050, 10

17、50A, 1350, 1100, 1200 3102, 3003, 3103 5005, 5005A, 5051A, 5251 6101, 6101A, 6101B, 6005, 6005A, 6005C, 6110A, 6012, 6018, 6023, 6351, 6060, 6360, 6061, 6261, 6262, 6262A, 6063, 6063A, 6463, 6065, 6081, 6082, 6182 Group II 2007, 2011, 2011A, 2014, 2014A, 2017, 2017A, 2024, 2030 5019, 5049,5052, 5154

18、A, 5454, 5754, 5056, 5083, 5086 7003, 7204, 7005, 7108, 7108A, 7020, 7021, 7022, 7049A, 7050, 7075 NOTE The four-digit numbers listed are taken from the Registration of International Alloy Designations and Chemical Composition Limits for Wrought Aluminium Alloys, published by the Aluminum Associatio

19、n, 1525 Wilson Boulevard, Suite 600, Arlington, VA 22209, USA (known as “Teal Sheets”). ISO 2012 All rights reserved 1 ISO 6362-3:2012(E) 5 Tolerances on shape and dimensions 5.1 Dimensional tolerances 5.1.1 Tolerances on width and thickness Tolerances on width and thickness shall be in accordance w

20、ith Table 2 and Table 3. Table 2 Tolerances on width and thickness for alloy group I Dimensions in millimetres Width b Thickness t tolerances for thickness ranges Range Tolerances 2 t 6 6 t 10 10 t 18 18 t 30 30 t 50 50 t 80 80 t 120 120 t 180 180 t 240 10 b 18 0,25 0,20 0,25 0,25 18 b 30 0,30 0,20

21、0,25 0,30 0,30 30 b 50 0,40 0,25 0,25 0,30 0,35 0,40 50 b 80 0,60 0,25 0,30 0,35 0,40 0,50 0,60 80 b 120 0,80 0,30 0,35 0,40 0,45 0,60 0,70 0,80 120 b 180 1,0 0,40 0,45 0,50 0,55 0,60 0,70 0,90 1,0 180 b 240 1,4 0,55 0,60 0,65 0,70 0,80 1,0 1,2 1,4 240 b 350 1,8 0,65 0,70 0,75 0,80 0,90 1,1 1,3 1,5

22、350 b 450 2,2 0,80 0,85 0,90 1,0 1,2 1,4 1,6 450 b 600 3,0 0,90 1,0 1,4 When the tolerance is specified either all plus or minus side, the value in this table shall be doubled. Table 3 Tolerances on width and thickness for alloy group II Dimensions in millimetres Width b Thickness t tolerances for t

23、hickness ranges Range Tolerances 2 t 6 6 t 10 10 t 18 18 t 30 30 t 50 50 t 80 80 t 120 120 t 180 180 t 240 10 b 18 0,35 0,25 0,30 0,35 18 b 30 0,40 0,25 0,30 0,40 0,40 30 b 50 0,50 0,30 0,30 0,40 0,50 0,50 50 b 80 0,70 0,30 0,35 0,45 0,60 0,70 0,70 80 b 120 1,0 0,35 0,40 0,50 0,60 0,70 0,80 1,0 120

24、b 180 1,4 0,45 0,50 0,55 0,70 0,80 1,0 1,1 1,4 180 b 240 1,8 0,60 0,65 0,70 0,90 1,1 1,3 1,6 1,8 240 b 350 2,2 0,70 0,75 0,80 0,90 1,2 1,4 1,7 1,9 350 b 450 2,8 0,90 1,0 1,1 1,4 1,8 2,1 2,3 450 b 600 3,5 1,2 1,4 1,8 When the tolerance is specified either all plus or minus side, the value in this tab

25、le shall be doubled. 5.1.2 Corner radii Maximum corner radii shall be in accordance with Table 4. 2 ISO 2012 All rights reserved ISO 6362-3:2012(E) Table 4 Maximum value of corner radii Dimensions in millimetres Thickness t Maximum value of corner radii Alloy group I Alloy group II 2 t 10 0,6 1,0 10

26、 5 000 b 100 0 5 + 0 7 + 0 10 + 100 b 200 0 7 + 0 9 + 0 12 + 200 b 450 0 8 + 0 11 + 0 14 + 450 b 600 0 9 + 0 12 + 0 16 + 5.1.4 Squareness of cut ends The squareness of cut ends shall be within half of the fixed-length tolerance range specified in Table 5 for both fixed and random lengths. For exampl

27、e, for a fixed-length tolerance of 0 10 +mm, the squareness of cut ends shall be within 5 mm. 5.2 Shape tolerances 5.2.1 General The shape tolerances specified in 5.2.2 to 5.2.4 apply to all tempers, except tempers O and TX510 type tempers. The deviation shall be measured with the bar supported on a

28、 horizontal base plate, such that the deviation is minimized by the weight of the bar. 5.2.2 Flatness tolerances Flatness tolerances shall be in accordance with Table 6. The deviation from flatness e shall be measured in accordance with Figure 1. ISO 2012 All rights reserved 3 ISO 6362-3:2012(E) Tab

29、le 6 Flatness tolerances Dimensions in millimetres Width b Tolerances for convexity or concavity e 10 b 30 0,2 30 b 50 0,3 50 b 80 0,4 80 b 120 0,6 120 b 180 0,9 180 b 240 1,2 240 b 350 1,5 350 b 450 2,0 450 b 600 2,5 Key 1 base plate 2 thickness b width e ideviation from flatness Figure 1 Measureme

30、nt of deviation from flatness 5.2.3 Straightness tolerances For rectangular bars of thickness equal to or greater than 10 mm, the straightness tolerances shall be in accordance with Table 7. 4 ISO 2012 All rights reserved ISO 6362-3:2012(E) Table 7 Straightness tolerances Dimensions in millimetres W

31、idth b Thickness t Straightness tolerances Per 1 000 mm of total length (l 1 ) h 1 In any 300 mm (l 2 ) h 2 10 b 80 10 t 80 2 1 80 b 120 10 t 50 2 1 50 t 120 3 1,5 120 b 180 10 t 50 3 1,5 50 t 180 4 2 180 b 350 10 t 50 4 2 50 t 240 6 4 350 b 450 10 t 240 6 4 450 b 600 30 t 120 6 4 For rectangular ba

32、rs of thickness less than 10 mm, the straightness tolerances shall be agreed upon between the supplier and purchaser. The deviations from straightness h 1and h 2shall be measured as shown in Figure 2, with the bar placed on a horizontal base plate so that its mass decreases the deviation. Dimensions

33、 in millimetres Key 1 base plate Figure 2 Measurement of deviation from straightness 5.2.4 Twist tolerances Twist tolerances shall be in accordance with Table 8. The twist ishall be measured in accordance with Figure 3. ISO 2012 All rights reserved 5 ISO 6362-3:2012(E) Table 8 Twist tolerances Dimen

34、sions in millimetres Width b Tolerances on twist i Per 1 000 mm of length Over the total length 10 b 30 1 3 30 b 50 1,5 4 50 b 120 2 5 120 b 240 3 8 240 b 350 4 10 350 b 450 5 12 450 b 600 6 14 Key 1 base plate 2 thickness b width itwist Figure 3 Measurement of twist 5.2.5 Squareness tolerances Squa

35、reness tolerances are specified in Table 9. The deviation from square shall be measured as shown in Figure 4. Table 9 Squareness tolerances Dimensions in millimetres Thickness t Maximum deviation from square Z 2 t 10 0,1 10 t 100 0,01 t 100 t 180 1,0 180 t 240 1,5 6 ISO 2012 All rights reserved ISO 6362-3:2012(E) Key Z maximum deviation from square Figure 4 Measurement of deviation from square (cross-section) ISO 2012 All rights reserved 7ISO 6362-3:2012(E) ISO 2012 All rights reserved ICS 77.150.10 Price based on 7 pages