ISO 5002-2013 Hot-rolled and cold-reduced electrolytic zinc-coated carbon steel sheet of commercial and drawing qualities《商用和拉制性的热轧和冷缩电解锌镀层碳钢薄板材》.pdf

《ISO 5002-2013 Hot-rolled and cold-reduced electrolytic zinc-coated carbon steel sheet of commercial and drawing qualities《商用和拉制性的热轧和冷缩电解锌镀层碳钢薄板材》.pdf》由会员分享，可在线阅读，更多相关《ISO 5002-2013 Hot-rolled and cold-reduced electrolytic zinc-coated carbon steel sheet of commercial and drawing qualities《商用和拉制性的热轧和冷缩电解锌镀层碳钢薄板材》.pdf（20页珍藏版）》请在麦多课文档分享上搜索。

1、 ISO 2013 Hot-rolled and cold-reduced electrolytic zinc-coated carbon steel sheet of commercial and drawing qualities Tles en acier au carbone lamines chaud et froid, revtues par zingage lectrolytique (tles lectro-zingues) de qualit commerciale et pour emboutissage INTERNATIONAL STANDARD ISO 5002 Fo

2、urth edition 2013-11-15 Reference number ISO 5002:2013(E) ISO 5002:2013(E)ii ISO 2013 All rights reserved COPYRIGHT PROTECTED DOCUMENT ISO 2013 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form or by any means, electronic

3、 or mechanical, including photocopying, or posting on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41

4、22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland ISO 5002:2013(E) ISO 2013 All rights reserved iii Contents Page Foreword iv 1 Scope . 1 2 Normative references 1 3 T erms and definitions . 1 4 Dimensions . 2 5 Conditions of manufacture 2 5.1 Steelma

5、king . 2 5.2 Chemical composition 2 5.3 Chemical analysis 3 5.4 Coating . 4 5.5 Fabrication qualities. 5 5.6 Weldability 6 5.7 Application . 6 5.8 Mechanical properties 6 5.9 Strain ageing . 7 5.10 Surface treatment of electrolytic zinc-coated products . 8 5.11 Oiling 8 5.12 Painting 8 6 Dimensional

6、 and shape tolerances . 9 7 Sampling 9 7.1 Tensile sampling 9 7.2 Coating tests 9 8 Test methods . 9 8.1 Tensile test 9 8.2 Coating tests 9 9 Retests 10 10 Resubmission 10 11 Workmanship .10 12 Inspection and acceptance 10 13 Coil size 10 14 Marking .11 15 Designation .11 16 Information to be suppli

7、ed by the purchaser12 Annex A (normative) Specification of thickness as base metal alone .13 Bibliography .15 ISO 5002:2013(E) Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing Internati

8、onal Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with IS

9、O, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. The procedures used to develop this document and those intended for its further maintenance are described in the ISO/IEC Directives, Pa

10、rt 1. In particular the different approval criteria needed for the different types of ISO documents should be noted. This document was drafted in accordance with the editorial rules of the ISO/IEC Directives, Part 2. www.iso.org/directives Attention is drawn to the possibility that some of the eleme

11、nts of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of any patent rights identified during the development of the document will be in the Introduction and/or on the ISO list of patent declarations received

12、. www.iso.org/patents Any trade name used in this document is information given for the convenience of users and does not constitute an endorsement. The committee responsible for this document is ISO/TC 17, Steel, Subcommittee SC 12, Continuous mill flat rolled products. For an explanation on the me

13、aning of ISO specific terms and expressions related to conformity assessment, as well as information about ISOs adherence to the WTO principles in the Technical Barriers to Trade (TBT) see the following URL: http:/ /www.iso.org/iso/home/standards_development/resources-for- technical-work/foreword.ht

14、m This fourth edition cancels and replaces the third edition (ISO 5002:2008), of which it constitutes a minor revision.iv ISO 2013 All rights reserved INTERNATIONAL ST ANDARD ISO 5002:2013(E) Hot-rolled and cold-reduced electrolytic zinc-coated carbon steel sheet of commercial and drawing qualities

15、1 Scope This International Standard specifies the characteristics of carbon steel sheet of commercial and drawing qualities in cut length or coil form, zinc coated by electrolytic deposition. Electrolytic zinc-coated sheet is intended for the manufacture of formed or of miscellaneous parts, and can

16、be supplied chemically treated to render it more suitable for painting. The zinc coating is expressed in micrometres of thickness per side, for equally coated, differentially coated, or one-side-coated sheets. These sheets are generally produced with coatings, which are not intended to withstand out

17、door exposure without chemical treatment and painting. Electrolytic zinc-coated sheet can be produced in thicknesses of 0,36 mm and thicker (normally up to 4,0 mm) and in widths of 600 mm and over in coils or cut lengths. It is recognized that materials thinner than 0,36 mm or thicker than 4,0 mm ca

18、n be suitable for electrolytic zinc coating, and, if required, be the subject of agreement between the interested parties. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references,

19、 only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 6892-1, Metallic materials Tensile testing Part 1: Method of test at room temperature ISO 7438, Metallic materials Bend test ISO 16160, Hot-rolled steel shee

20、t products Dimensional and shape tolerances ISO 16162, Cold-rolled steel sheet products Dimensional and shape tolerances 3 T erms a nd definiti ons For the purposes of this document, the following terms and definitions apply. 3.1 electrolytic zinc-coated steel sheet product obtained by electrolytic

21、deposition of a zinc coating on steel sheet on a zinc coating line to produce either electrolytic zinc-coated coils or electrolytic zinc-coated cut lengths 3.2 skin pass light cold rolling of hot-rolled descaled sheet or of the cold-reduced and annealed steel sheet prior to zinc coating Note 1 to en

22、try: The purpose of the skin pass is to produce a higher degree of surface smoothness and thereby improve the surface appearance. The skin pass also temporarily minimizes the occurrence of a surface condition known as stretcher strain (Luders lines) or fluting during the fabrication of finished part

23、s. The skin pass also controls and improves flatness. Some increase in hardness and loss of ductility will result from skin passing. 3.3 stabilized interstitial free steel extra low carbon steel in which all interstitial elements are combined with titanium and/or equivalent elements ISO 2013 All rig

24、hts reserved 1 ISO 5002:2013(E) 3.4 grade substitution interstitial free steel (IF steel) may be applied on orders specifying CR4 Note 1 to entry: Deep drawing special killed, provided that the customer is informed of the substitution and related shipping documents reflecting the actual material shi

25、pped. 3.5 lot 50 t or less of sheet of the same designation rolled to the same thickness and condition 4 Dimensions 4.1 The thickness of zinc-coated sheet can be specified as a combination of the base metal and metallic coating, or as the base metal alone. The purchaser indicates on the order which

26、method of specifying thickness is required. In the event that the purchaser does not indicate any preference, the thickness as a combination of the base metal and coating will be provided. Annex A describes the requirement for specifying the thickness as base metal alone. 4.2 Electrolytic zinc-coate

27、d sheet less than 600 mm wide can be slit from wide sheet and will be considered as sheet. 5 Conditions of manufacture 5.1 Steelmaking The processes used in making the steel and in manufacturing electrolytic zinc-coated cold-reduced sheet and hot-rolled sheet are left to the discretion of the manufa

28、cturer. When requested, the purchaser shall be informed of the steelmaking process being used. 5.2 Chemical composition The chemical composition (heat analysis) shall not exceed the values given in Tables 1, 2, and 3. Table 1 Chemical composition (heat analysis) for hot-rolled electrolytic zinc-coat

29、ed carbon steel sheet Mass fractions in percent Quality C max. Mn max. P max. S max. Designation Name HR1 commercial 0,12 0,60 0,045 0,035 HR2 drawing 0,10 0,45 0,035 0,035 HR3 deep drawing 0,08 0,40 0,030 0,030 HR4 deep drawing aluminium killed 0,08 0,35 0,025 0,0302 ISO 2013 All rights reserved IS

30、O 5002:2013(E) Table 2 Chemical composition (heat analysis) for cold-rolled electrolytic zinc-coated carbon steel sheet Mass fractions in percent Quality C max. Mn max. P max. S max. Ti amax. Designation Name CR1 commercial 0,15 0,60 0,050 0,035 CR2 drawing c 0,10 0,50 0,040 0,035 CR3 deep drawing c

31、 0,08 0,45 0,030 0,03 CR4 deep drawing alumin- ium killed c(non-ageing) 0,06 0,45 0,030 0,03 CR5 extra deep drawing b(stabilized interstitial free) 0,02 0,25 0,020 0,02 0,15 a Titanium may be replaced totally or partially by niobium or vanadium. Carbon and nitrogen shall be completely stabilized. b

32、By agreement, the manganese, phosphorus, and sulfur maximums may be adjusted. c If IF steel is to be applied to CR1 or CR4 orders, the values of 0,15 % maximum Ti and 0,10 % maximum Nb and V are acceptable to ensure that carbon and nitrogen are fully stabilized. 5.3 Chemical analysis 5.3.1 Heat anal

33、ysis An analysis of each heat of steel shall be made by the manufacturer in order to determine compliance with the requirements given in Tables 1, 2 and 3. On request, at the time of ordering, this analysis shall be reported to the purchaser or his representative. Each of the elements listed in Tabl

34、es 1 and 2 shall be included in the report of the heat analysis. If one or more of the elements in Table 3 is/are specified, the analysis shall be reported. 5.3.2 Product analysis A product analysis may be made by the purchaser to verify the specified analysis of the semi-finished or finished steel,

35、 and shall take into consideration any normal heterogeneity. The sampling method and deviation limits shall be agreed upon between the manufacturer and the purchaser at the time of ordering. The product analysis tolerances shall be in accordance with Table 3 and Table 4. ISO 2013 All rights reserved

36、 3 ISO 5002:2013(E) Table 3 Limits on additional chemical elements Mass fractions in percent Elements Heat analysis max. Product analysis max. Cu a 0,20 0,23 Ni a 0,20 0,23 Cr a,b 0,15 0,19 Mo a,b 0,06 0,07 Nb c,d 0,008 0,018 V c,d 0,008 0,018 Ti c,d 0,008 0,018 a The sum of copper, nickel, chromium

37、, and molybdenum shall not exceed 0,50 % on heat analysis. When one or more of these elements are specified, the sum does not apply; in which case, only the individual limits on the remaining elements will apply. b The sum of chromium and molybdenum shall not exceed 0,16 % on heat analysis. When one

38、 or more of these elements are specified, the sum does not apply; in which case, only the individual limits on the remaining elements will apply. c An analysis greater than 0,008 % may be supplied after agreement between the producer and the consumer. d For IF steel, only the values of 0,15 % maximu

39、m Ti and 0,010 % maximum for Nb and V are acceptable to ensure that carbon and nitrogen are fully stabilized. Table 4 Product analysis tolerances Mass fractions in percent Element M a x i m u m of s p e c i f ie d e le m e n t Tolerance over maximum speci- f ie d C 0,15 0,03 Mn 0,60 0,03 P 0,05 0,01

40、 S 0,035 0,01 Ti 0,15 0,01 NOTE The maximum tolerance in this table is the allowable excess over the specified requirements and not the heat analysis. 5.4 Coating 5.4.1 Coating mass The amount of coating is expressed in micrometres of thickness per surface of sheet and shall conform to the requireme

41、nts of minimum thickness given in Table 5. 5.4.2 Coating adherence The zinc-coated sheet shall be capable of being bent in any direction, in accordance with the mandrel diameter requirements for the quality designations included in Table 6.4 ISO 2013 All rights reserved ISO 5002:2013(E) Table 5 Zinc

42、 coatings for electrolytic zinc-coated hot-rolled and cold-reduced steel sheet Coating designation a Nominal thickness per surface m Minimum thickness per surface m Nominal coating mass per surface bg/m 2 ZE 04 0,4 0,4 3 ZE 10 1,0 0,9 7 ZE 14 1,4 1,2 10 ZE 25 2,5 2,2 18 ZE 28 2,8 2,4 20 ZE 38 3,8 3,

43、4 27 ZE 42 4,2 3,6 30 ZE 50 5,0 4,5 36 ZE 56 5,6 4,8 40 ZE 70 7,0 6,0 50 ZE 75 7, 5 6,8 54 ZE 100 10,1 9,1 75 ZE 135 13,5 12,2 96 ZE 150 15,0 13,5 107 NOTE The density of zinc used is 7 100 kg/m 3 . a Equally coated material should be designated as ZE 10/10, for example. Differentially coated materi

44、al should be designated as ZE 50/10, for example. Single-surface-coated material should be designated as ZE 38/0, for example. b This is for information only. Table 6 Coating bend test requirements for electrolytic zinc-coated hot-rolled and cold- reduced steel sheet Designation 180 bend mandrel dia

45、meter e 3 e 3 HR1, HR2, HR3, HR4 0 1,0a CR1, CR2, CR3, CR4, CR5 0 0 NOTE 1 e is the thickness of the sheet in millimetres. NOTE 2 a is the thickness of bend test piece. 5.5 Fabrication qualities 5.5.1 Commercial quality electrolytic zinc-coated sheet (HR1 or CR1) is intended for general fabricating

46、purposes where sheet is used in the flat state or for bending or moderate forming. 5.5.2 Drawing quality electrolytic zinc-coated sheet (HR2, HR3, and HR4 or CR2, CR3, CR4, and CR5) is intended for drawing or severe forming. It is furnished according to all requirements of this International Standar

47、d or by agreement when ordered to fabricate an identified part, in which case the mechanical properties of Table 4 (for hot-rolled steel sheet) and Table 5 (for cold-reduced steel sheet) do not apply. Drawing qualities are identified as follows: HR2/CR2 (drawing quality); HR3/CR3 (deep drawing quali

48、ty); HR4/CR4 deep drawing quality aluminium killed (see 5.9); ISO 2013 All rights reserved 5 ISO 5002:2013(E) CR5 extra deep drawing quality (stabilized interstitial free). 5.6 Weldability The product is suitable for welding if appropriate conditions are selected. 5.7 Application It is desirable tha

49、t electrolytic zinc-coated steel sheet be identified for fabrication by the name of the part or by the intended application. Steel sheet of drawing qualities HR2, HR3, and HR4 and CR2, CR3, CR4, and CR5 may be produced to make an identified part within a properly established breakage allowance, which shall be previously agreed upon between the interested parties. In this case, the part name, the details of fabrication, and special requirements (i.e. exposed or unexposed, freedom from stretcher strai