ISO 28279-2010 Sintered metal materials - Determination of the level of cleanliness of powder-metallurgy parts《烧结金属材料 粉末冶金部件洁净度的测定》.pdf

《ISO 28279-2010 Sintered metal materials - Determination of the level of cleanliness of powder-metallurgy parts《烧结金属材料 粉末冶金部件洁净度的测定》.pdf》由会员分享，可在线阅读，更多相关《ISO 28279-2010 Sintered metal materials - Determination of the level of cleanliness of powder-metallurgy parts《烧结金属材料 粉末冶金部件洁净度的测定》.pdf（10页珍藏版）》请在麦多课文档分享上搜索。

1、 Reference number ISO 28279:2010(E) ISO 2010INTERNATIONAL STANDARD ISO 28279 First edition 2010-10-01 Sintered metal materials Determination of the level of cleanliness of powder- metallurgy parts Matriaux mtalliques fritts Dtermination du niveau de propret des pices en poudres mtalliques ISO 28279:

2、2010(E) PDF disclaimer This PDF file may contain embedded typefaces. In accordance with Adobes licensing policy, this file may be printed or viewed but shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloading thi

3、s file, parties accept therein the responsibility of not infringing Adobes licensing policy. The ISO Central Secretariat accepts no liability in this area. Adobe is a trademark of Adobe Systems Incorporated. Details of the software products used to create this PDF file can be found in the General In

4、fo relative to the file; the PDF-creation parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below

5、. COPYRIGHT PROTECTED DOCUMENT ISO 2010 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address

6、 below or ISOs member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland ii ISO 2010 All rights reservedISO 28279:2010(E) ISO 2010 All rights reserv

7、ed iiiContents Page Foreword iv 1 Scope1 2 Symbols and units.1 3 Principle.1 4 Apparatus.1 5 Procedure.2 6 Expressions of results4 7 Test report4 ISO 28279:2010(E) iv ISO 2010 All rights reservedForeword ISO (the International Organization for Standardization) is a worldwide federation of national s

8、tandards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International

9、organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules gi

10、ven in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least

11、 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. ISO 28279 was prepared by Technical Committee ISO/TC 119,

12、Powder metallurgy, Subcommittee SC 3, Sampling and testing methods for sintered metal materials (excluding hardmetals). INTERNATIONAL STANDARD ISO 28279:2010(E) ISO 2010 All rights reserved 1Sintered metal materials Determination of the level of cleanliness of powder-metallurgy parts 1 Scope This In

13、ternational Standard specifies the determination of the amount and nature of the surface contamination of powder-metallurgy (PM) parts (i.e. the level of cleanliness of PM parts). 2 Symbols and units For the purposes of this document, the following symbols and units apply. Symbol Explanation Unit C

14、Amount of contaminant. mg/part m 1Mass of the as-received, dried 5 m filter (4.4). g m 2Mass of the dried 5 m filter (4.4) plus the contaminants. g N Number of parts taken for testing. 3 Principle PM parts are pressure-rinsed with a filtered solvent that is subsequently re-filtered in order to captu

15、re surface contaminants. The filtered residue is weighed and the contaminant particles are examined with a magnifying glass or stereomicroscope in order to determine their nature. 4 Apparatus 4.1 Filter funnel. 4.2 Filtering flask, with a minimum volume of 2 L. 4.3 Vacuum pump. 4.4 Filter, 5 m, made

16、 of polyester (preferred material) or polyamide of diameter 20 mm to 50 mm (type of filter depending on the solvent). 4.5 Filter, maximum 1 m, made of polyester (preferred material), polyamide or cellulose (type of filter material depending on the solvent) of diameter 20 mm to 50 mm. 4.6 Analytical

17、balance, of capacity at least 20 g and 0,000 1 g accuracy. 4.7 Petri-dish set, (only the bottom portion). ISO 28279:2010(E) 2 ISO 2010 All rights reserved4.8 Drying oven, with a capability of at least 100 C and 10 C accuracy. 4.9 Desiccator. 4.10 Pressure gun for liquids. 4.11 Solvent (white spirit)

18、. 4.12 Stereomicroscope (at least 10 magnification) or microscope. 4.13 Glass microscope slides. 4.14 Stainless-steel tongs, with flat tips. 4.15 Gloves, made of latex or another type of plastic depending on the solvent used. The gloves should be used in order to prevent contamination during handlin

19、g. 5 Procedure 5.1 Place the 5 m filter (4.4) on the Petri dish (see Figure 1), and dry it in an oven (4.8) at 100 C for at least 30 min. The recommended filter mesh is 5 m and other mesh should be agreed between the user and supplier. Key 1 filter 2 Petri dish Figure 1 Filter ready to be dried 5.2

20、Transfer the Petri dish and filter to the desiccator (4.9), and cool it to room temperature. 5.3 Weigh the dried filter to the nearest 0,000 1 g with an analytical balance (4.6), and record the mass m 1 . 5.4 Filter at least 2 L of white spirit solvent by using the filtering flask and the vacuum pum

21、p (see Figure 2), with the maximum 1 m filter (4.5) (see Figure 2). Keep this filtered solvent in a clean glass bottle previously cleaned with pure solvent. The recommended solvent is white spirit and any other solvent should be agreed between the user and supplier. ISO 28279:2010(E) ISO 2010 All ri

22、ghts reserved 3Key 1 filter funnel 5 filtered solvent 2 filter 6 filtering flask 3 porous plate 7 clips 4 vacuum-pump connection Figure 2 System for cleaning the solvent and/or filtering the contaminants 5.5 Take a number of parts so as to have a total surface area of at least 1 000 cm 2 , and note

23、the total number of parts N. Take care not to contaminate the PM parts during handling. In case of difficulty in reaching 1 000 cm 2of surface because the part is too big or too small, the surface area should be agreed between the user and supplier. 5.6 Rinse the parts with the pressure gun (4.10) b

24、y using 1 L of filtered solvent, at a pressure of (200 50) kPa, and save the solvent after rinsing. Ensure that the solvent wets all surfaces of the PM parts during this operation. NOTE Both parties can decide if a pressure gun should be used. In some cases, an extraction technique based on ultrasou

25、nd might be suitable. 5.7 Filter the contaminated solvent by using the glass filtering flask (4.2) and the vacuum pump (4.3) using the same system as shown in Figure 2, with the previously dried and weighed 5 m filter (4.4). The filter now has collected the contaminants from the PM parts. 5.8 Using

26、the same vacuum system, rinse the residues and the 5 m filter (4.4) with 200 ml of clean, filtered solvent (4.11) in order to remove any trapped oil. 5.9 Place the filter with residues on the Petri dish (4.7) and dry it in the oven (4.8) at 100 C for at least 30 min (same system as shown in Figure 1

27、). Then transfer the Petri dish and filter to the desiccator (4.9), and cool to room temperature. ISO 28279:2010(E) 4 ISO 2010 All rights reserved5.10 Weigh the filter with residues to the nearest 0,000 1 g in an analytical balance, and record the mass m 2 . 5.11 Place the filter with residues betwe

28、en two glass microscope slides (4.13) (see Figure 3), and visualize the particles by means of the stereomicrocope with at least 10 magnification power or a microscope (4.12). Note the nature of the contaminants and their size taken at maximum length/diameter. Figure 3 Filter ready to be observed by

29、means of a stereomicroscope or microscope 6 Expressions of results 6.1 The amount of contaminant, C, in milligrams per part, is calculated as follows: 21 1000 mm C N = 6.2 The nature of the contamination is expressed as the maximum size of each contaminant particle, in micrometres (m), and its natur

30、e. 7 Test report The test report should include the following information: a) a reference to this International Standard; i.e. ISO 28279:2010; b) the name or designation of the parts tested; c) the amount of contaminant, C, in milligrams per part; d) the size of the maximum particle of each type of

31、contaminant observed, in micrometres; e) the nature of the contaminant. This International Standard specifies a unique way for determining the contamination. Any variation regarding the filter mesh, the type of solvent, or the extraction method, should be agreed between the two parties. If the appli

32、cation of the part is in vacuum or under a pressure exceeding 10 hPa, an ultrasonic extraction technique can be used, except for material that can be chemically attacked by ultrasound (such as aluminium). In this case, both parties should agree to use the same type of ultrasonic device, and they should agree on the frequency of the ultrasound and the extraction time. ISO 28279:2010(E) ICS 77.160 Price based on 4 pages ISO 2010 All rights reserved