ISO 25902-2-2010 Titanium pipes and tubes - Non-destructive testing - Part 2 Ultrasonic testing for the detection of longitudinal imperfections《钛管 无损检验 第2部分 纵向缺.pdf

《ISO 25902-2-2010 Titanium pipes and tubes - Non-destructive testing - Part 2 Ultrasonic testing for the detection of longitudinal imperfections《钛管 无损检验 第2部分 纵向缺.pdf》由会员分享，可在线阅读，更多相关《ISO 25902-2-2010 Titanium pipes and tubes - Non-destructive testing - Part 2 Ultrasonic testing for the detection of longitudinal imperfections《钛管 无损检验 第2部分 纵向缺.pdf（12页珍藏版）》请在麦多课文档分享上搜索。

1、 Reference number ISO 25902-2:2010(E) ISO 2010INTERNATIONAL STANDARD ISO 25902-2 First edition 2010-03-01 Titanium pipes and tubes Non-destructive testing Part 2: Ultrasonic testing for the detection of longitudinal imperfections Canalisations et tubes en titane Essai non destructif Partie 2: Contrl

2、e par ultrason pour la dtection des dfauts longitudinaux ISO 25902-2:2010(E) PDF disclaimer This PDF file may contain embedded typefaces. In accordance with Adobes licensing policy, this file may be printed or viewed but shall not be edited unless the typefaces which are embedded are licensed to and

3、 installed on the computer performing the editing. In downloading this file, parties accept therein the responsibility of not infringing Adobes licensing policy. The ISO Central Secretariat accepts no liability in this area. Adobe is a trademark of Adobe Systems Incorporated. Details of the software

4、 products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event that a problem relating to it is fo

5、und, please inform the Central Secretariat at the address given below. COPYRIGHT PROTECTED DOCUMENT ISO 2010 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying and mi

6、crofilm, without permission in writing from either ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland ii ISO

7、 2010 All rights reservedISO 25902-2:2010(E) ISO 2010 All rights reserved iiiForeword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO

8、 technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates cl

9、osely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Dr

10、aft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this doc

11、ument may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. ISO 25902-2 was prepared by Technical Committee ISO/TC 79, Light metals and their alloys, Subcommittee SC 11, Titanium. ISO 25902 consists of the following parts, under the gen

12、eral title Titanium pipes and tubes Non-destructive testing: Part 1: Eddy-current examination Part 2: Ultrasonic testing for the detection of longitudinal imperfections INTERNATIONAL STANDARD ISO 25902-2:2010(E) ISO 2010 All rights reserved 1Titanium pipes and tubes Non-destructive testing Part 2: U

13、ltrasonic testing for the detection of longitudinal imperfections 1 Scope This part of ISO 25902 specifies an ultrasonic testing method for detecting longitudinal imperfections in titanium seamless tubes or welded tubes. This part of ISO 25902 also applies to titanium alloy tubes. In this part of IS

14、O 25902 a) the minimum wall thickness is 0,3 mm, b) only rectangular notches are permitted as reference reflectors, and c) the minimum notch depth is 0,08 mm. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only

15、the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 9712, Non-destructive testing Qualification and certification of personnel ISO 10375, Non-destructive testing Ultrasonic inspection Characterization of search unit

16、 and sound field ISO 18175, Non-destructive testing Evaluating performance characteristics of ultrasonic pulse-echo testing systems without the use of electronic measurement instruments 3 General 3.1 Applicable dimension range The range of the applicable dimensions of a tube shall be 10 mm to 150 mm

17、 outside diameter and 0,3 mm to 10 mm thickness. The ratio of thickness to outside diameter shall be less than or equal to 0,2 (20 %). 3.2 Testing technique The test shall be carried out using an ultrasonic angle beam technique, effected by rotating the ultrasonic transducer or the tube. The ultraso

18、nic testing system shall be an immersion technique (including a local immersion technique). ISO 25902-2:2010(E) 2 ISO 2010 All rights reserved3.3 Personnel This test shall be carried out by suitably trained operators qualified in accordance with ISO 9712 or equivalent and supervised by competent per

19、sonnel nominated by the manufacturer. In the case of third-party inspection, this shall be agreed between the purchaser and manufacturer. Non-destructive testing (NDT) operators shall be authorized by a level 3 NDT individual approved by the employer. 4 Apparatus 4.1 Ultrasonic system, composed of a

20、n ultrasonic instrument, at least one ultrasonic transducer, a tube-feeding device, a rotary device for transducers or tubes, and an automatic alarm and recording system. The performance of the transducer shall comply with ISO 10375. The whole test system, i.e. instrument, transducer, tube-feeding d

21、evice, automatic alarm and recording system, shall be capable of detecting the required reference reflector with a sufficient signal-to-noise ratio. 4.2 Ultrasonic instrument, whose amplitude linearity shall be measured in accordance with ISO 18175. The sum of the absolute values of the positive and

22、 negative maximum deviation shall be less than or equal to 8 %. 4.3 Ultrasonic transducer. 4.3.1 The nominal transducer diameter shall be between 5 mm and 20 mm (including a rectangular shape having almost the same area as it) and, if necessary, a focusing transducer shall be used. 4.3.2 The nominal

23、 frequency shall be 4 MHz to 10 MHz. 5 Reference tube 5.1 Purpose The reference tube shall be used for setting the test sensitivity and for periodical performance tests to demonstrate that the required test sensitivity is maintained. 5.2 Materials Materials to be used for a reference tube shall have

24、 the same material grade, nominal diameter, thickness, surface finish and heat-treatment condition as those of the tubes to be tested, and shall have similar acoustic properties (e.g. velocity, attenuation coefficient). 5.3 Reference reflectors 5.3.1 Classification and shapes of reference reflectors

25、. The reference reflectors shall be rectangular notches, as shown in Figure 1. ISO 25902-2:2010(E) ISO 2010 All rights reserved 3a) b) Key aWidth of notch. bDepth. cLength of notch. dThickness. eAt most 10 % of length. Figure 1 Shape of reference reflectors for sensitivity setting 5.3.2 Dimensions o

26、f reference reflectors and their tolerances shall be as given in Table 1. Table 1 Dimensions of reference reflectors and their tolerances Dimensions in millimetres Type of notch Depth Tolerance on depth Length l Width N-0,08 0,08 N-0,10 0,10 N-0,20 0,20 0,05 N-0,40 0,40 N-12,5 12,5 % of thickness N-

27、15 15,0 % of thickness N-20 20,0 % of thickness N-25 25,0 % of thickness 15 % (0,05 min.) 10 u l u 25 1,0 max. ISO 25902-2:2010(E) 4 ISO 2010 All rights reserved5.4 Fabrication of reference notches. The reference notches shall be fabricated as follows: a) for seamless tubes: by electric-discharge or

28、 mechanical machining; b) for welded tubes: by electric-discharge or mechanical machining in the parent material of the tube; c) axially on the inner and outer surface of the tube. However, for tubes with an inside diameter of less than 15 mm, only notches on the outer surface are required. 5.5 Dist

29、ance of reference reflectors. In order to obtain clearly distinguishable signal indications, the notches shall be sufficiently separated from the ends of the reference tubes and from each other. 5.6 Verification of reference reflectors. The dimensions and shape of reference reflectors shall be verif

30、ied by a suitable technique. 6 Test method 6.1 Ultrasonic test system During testing, the tubes and/or the transducer assembly shall be moved relative to each other so that the complete tube surface is scanned. During scanning, the tubes shall be tested in two opposing circumferential directions of

31、sound propagation, unless otherwise agreed between the purchaser and manufacturer. 6.2 Setting 6.2.1 Period for setting test sensitivity The test sensitivity shall be set before the start of the test. 6.2.2 Reference reflectors for setting test sensitivity The parameters of reference reflectors to b

32、e used for setting the test sensitivity according to the class, the usage, the manufacturing method, the finishing method, and the wall thickness of the tube to be tested are listed in Table 2. Table 2 Reference reflectors for setting test sensitivity Class Use Manufacturing method Finishing method

33、Thickness, mm Type of rectangular notch UA 0,3 u 0,5 N-0,08 0,5 u 0,8 N-0,10 Welded tube As-welded or cold drawing 0,8 u 3 N-12,5 1 u 1,6 N-0,20 UB For heat exchanger Seamless tube Cold drawing 1,6 u u 5 N-12,5 UC Welded tube As-welded or cold drawing 1 u u 10 N-15 UD Cold drawing 1 u u 10 N-20 For

34、piping Hot extrusion 3 u u 10 N-25 1 u 1,6 N-0,40 UE For heat exchanger and for piping Seamless tube Cold rolling 1,6 u u 10 N-25 ISO 25902-2:2010(E) ISO 2010 All rights reserved 56.2.3 Test procedure 6.2.3.1 The sensitivity of the ultrasonic instrument shall be set with the reference reflectors sel

35、ected from Table 2. 6.2.3.2 The sensitivity of the ultrasonic instrument shall be set so that the indication from the reference reflectors becomes from 50 % to 80 % of the screen height. 6.2.3.3 The automatic alarm system or the recorder shall be adjusted to operate within a normal operation range u

36、nder the same condition as actual testing. 7 Acceptance criteria Accept only those tubes where no signal with an amplitude higher than that from the reference reflectors in the reference tube has been detected. Reject all other tubes. 8 Periodical confirmation of correct setting It shall be confirme

37、d at least every 4 h that the sensitivity of the ultrasonic instrument is suitably maintained when the testing is continuously performed, and when the testing operation ends or is interrupted. Where an unacceptable deviation of the test sensitivity is discovered during testing, perform readjustment

38、and re-examine all the tubes tested in the abnormal period. 9 Verification of test system The performance of the complete test system shall be verified periodically. The system shall show the required performance in detecting and evaluating the relevant test reflectors. 10 Test report The test repor

39、t shall contain at least the following information: a) date of test; b) names of testing personnel; c) a reference to this part of ISO 25902 and details of any special agreements; d) symbol for the tube and material grade; e) dimensions of tube; f) complete list of equipment; g) reference tube and r

40、eference reflectors; h) identification of ultrasonic transducers; i) testing technique and conditions (linear and rotational testing speed, parameters of sensitivity calibration, etc.); j) test results. ISO 25902-2:2010(E) 6 ISO 2010 All rights reservedBibliography 1 ISO 5577, Non-destructive testing Ultrasonic inspection Vocabulary 2 ISO 12710, Non-destructive testing Ultrasonic inspection Evaluating electronic characteristics of ultrasonic test instruments ISO 25902-2:2010(E) ICS 77.040.20; 77.150.50 Price based on 6 pages ISO 2010 All rights reserved