1、 ISO 2013 Ceramic tiles Grouts and adhesives Part 2: Test methods for adhesives Carreaux cramiques Mortiers de joints et colles Partie 2: Mthodes dessai pour les colles INTERNATIONAL STANDARD ISO 13007-2 Third edition 2013-11-01 Reference number ISO 13007-2:2013(E) ISO 13007-2:2013(E)ii ISO 2013 All

2、 rights reserved COPYRIGHT PROTECTED DOCUMENT ISO 2013 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, withou

3、t prior written permission. Permission can be requested from either ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in S

4、witzerland ISO 13007-2:2013(E) ISO 2013 All rights reserved iii Contents Page Foreword iv 1 Scope . 1 2 Normative references 1 3 General test conditions and procedures 1 3.1 Sampling . 1 3.2 Test conditions 1 3.3 Test materials . 2 3.4 Mixing procedures . 2 3.5 Test substrate . 3 3.6 Failure pattern

5、s 3 3.7 Test report . 3 4 Test methods . 4 4.1 Determination of open time 4 4.2 Determination of slip . 5 4.3 Determination of shear adhesion strength (D, R) . 7 4.4 Determination of tensile adhesion strength (C) . 9 4.5 Determination of transverse deformation .11 Annex A (informative) Concrete test

6、 slab .23 ISO 13007-2:2013(E) Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interes

7、ted in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical C

8、ommission (IEC) on all matters of electrotechnical standardization. The procedures used to develop this document and those intended for its further maintenance are described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the different types of ISO documen

9、ts should be noted. This document was drafted in accordance with the editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives). Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible

10、 for identifying any or all such patent rights. Details of any patent rights identified during the development of the document will be in the Introduction and/or on the ISO list of patent declarations received (see www.iso.org/patents). Any trade name used in this document is information given for t

11、he convenience of users and does not constitute an endorsement. For an explanation on the meaning of ISO specific terms and expressions related to conformity assessment, as well as information about ISOs adherence to the WTO principles in the Technical Barriers to Trade (TBT) see the following URL:

12、Foreword - Supplementary information. The committee responsible for this document is ISO/TC 189, Ceramic tile. This third edition cancels and replaces the second edition (ISO 13007-2:2010), of which it constitutes a minor revision. ISO 13007 consists of the following parts, under the general title C

13、eramic tiles Grouts and adhesives: Part 1: Terms, definitions and specifications for adhesives Part 2: Test methods for adhesives Part 3: Terms, definitions and specifications for grouts Part 4: Test methods for groutsiv ISO 2013 All rights reserved INTERNATIONAL ST ANDARD ISO 13007-2:2013(E) Cerami

14、c tiles Grouts and adhesives Part 2: Test methods for adhesives 1 Scope This part of ISO 13007 describes the methods for determining the characteristics for adhesives used in the installation of ceramic tiles. The following test methods are described: determination of open time (4.1); determination

15、of slip (4.2); determination of shear adhesion strength (4.3); determination of tensile adhesion strength (4.4); determination of transverse deformation (4.5). 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for i

16、ts application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 13006, Ceramic tiles Definitions, classification, characteristics and marking ISO 13007-1, C e r a m i c t i l e s G r o

17、 u t s a n d a d h e s i v e s Pa r t 1: Te r m s , d e f i n i t i o n s a n d s p e c i f i c a t i o n s f o r a d h e s i v e s 3 General test conditions and procedures 3.1 Sampling A representative sample of at least 2 kg shall be used. 3.2 Test conditions Standard conditions shall be (23 2) C

18、and (50 5) % relative humidity and the speed of air in the testing area shall be less than 0,2 m/s. Other test conditions may be specified in Clause 4. The tolerance in the time of conditioning for all test specimens shall be as shown in Table 1 below. ISO 2013 All rights reserved 1 ISO 13007-2:2013

19、(E) Table 1 Allowed tolerance in testing time for all samples requiring conditioning Sample conditioning time Allowed tolerance for testing 24 h 0,5 h 7 d 3 h 14 d 6 h 21 d 9 h 28 d 12 h NOTE Testing must be performed within the specified time window. 3.3 Test materials Condition all test materials,

20、 including water, for at least 24 h under standard conditions. The adhesive to be tested shall be within its shelf life, where this is specified. 3.3.1 Ceramic tiles The tiles shall be checked prior to conditioning to ensure that they are unused, clean, and dry. The type of tile shall be as specifie

21、d under the specific test procedures found in Clause 4. 3.4 Mixing procedures 3.4.1 Cementitious adhesives (C) The amount of water and/or liquid admix required for preparing the adhesive shall be as stated by the manufacturer in parts by weight, i.e. liquid to dry powder (in cases where a range of v

22、alues is given, the average shall be used). Using a minimum quantity of 2 kg of the powder and the recommended quantity of liquid, prepare the adhesive in a planetary mixer using the following slow speed settings: (140 5) rotations per minute and (62 5) rotations per minute planetary movement. See F

23、igures 1 and 2. Carry out the following procedure. 1) Pour the liquid into the pan. 2) Scatter the dry powder over the liquid. 3) Mix for 30 s. 4) Take out the mixing paddle. 5) Scrape down the paddle and pan within 1 min. 6) Replace the paddle and mix for 1 min. If required by the adhesive manufact

24、urers instructions, let the adhesive mature as specified and then mix for an additional 15 s. 3.4.2 Dispersion adhesive (D) and reaction resin adhesive (R) Where ready-to-use dispersion adhesives or reaction resin adhesives are to be used, the manufacturers instructions shall be followed.2 ISO 2013

25、All rights reserved ISO 13007-2:2013(E) 3.5 Test substrate 3.5.1 Concrete test substrate The mandatory concrete test substrate shall be (40 5) mm thick, have a moisture content of less than 3 % by mass, and have a surface water absorption in the range of 0,5 cm 3to 1,5 cm 3after 4 h of testing. The

26、cohesive strength as referenced in A.3.3 shall be at least 1,5 N/mm 2 . A method for manufacturing a suitable concrete test slab and the procedures for measuring the cohesive strength and surface water absorption is given in informative Annex A. 3.5.2 Other substrates Other substrates may be used up

27、on agreement if the substrate is recommended for ceramic tile application by the adhesive manufacturer. To demonstrate compatibility with other optional substrates, the adhesive shall be applied to the selected substrate in accordance with the open time test method (see 4.1). When a result of 0,5 N/

28、mm 2is achieved or cohesive failure occurs in the substrate, the requirement is considered satisfied. 3.6 Failure patterns 3.6.1 Adhesion failure (AF-S or AF-T) Failure occurs at the interface between the adhesive and the substrate (AF-S) see Figure 3, a) or bet ween the tile and the adhesive (AF-T)

29、 see Figure 3, b). The test value is equal to the adhesive strength. In some cases, failure may occur in the adhesive layer between the tile and the pull-head plate (BF) see Figure 3, c). In this case, the adhesive strength is greater than the test value and the test should be repeated. 3.6.2 Cohesi

30、ve failure within the adhesive (CF-A) Failure occurs within the adhesive layer see Figure 3, d). 3.6.3 Cohesive failure in the substrate or in the tile (CF-S or CF-T) Failure occurs within the substrate (CF-S) see Figure 3, e) or within the body of the tile (CF-T) see Figure 3, f). In this case, the

31、 strength of the adhesive is greater than the test value. The modes of failure may be a combination of any of the above. An approximate percentage of each shall be recorded. 3.7 Test report 3.7.1 General The test report shall specify the following: a) a reference to this part of ISO 13007 (i.e. ISO

32、13007-2:2013); b) the date of test; c) the type of adhesive, commercial designation, and manufacturers name; d) the source, date obtained, and complete identification of test sample; e) the handling and storage of samples before testing; f) the test conditions; g) the amount of water or liquid used

33、for preparing the adhesive; ISO 2013 All rights reserved 3 ISO 13007-2:2013(E) h) any other factor that could have affected the result; i) the test results (individual and mean values and mode of failure where required). 3.7.2 Test results of cementitious and dispersion adhesives The test report sha

34、ll specify the following: a) open time; b) slip; c) shear adhesion strength; d) adhesion strength; e) deformation. 3.7.3 Test results of chemical resistance The test report shall specify the following: a) test conditions; b) change in colour and surface appearance during the test; c) total duration

35、of the test and exposure periods. 4 Test methods 4.1 Determination of open time 4.1.1 General Open time shall be tested following the general test conditions and procedures given in Clause 3 and the specific instructions which follow. 4.1.2 Test materials 4.1.2.1 Ceramic tiles, Group BIII porous bod

36、y tile complying with ISO 13006, with a water absorption of (15 3) % by mass, facial dimensions of (50 1) mm (50 1) mm, thickness in the range of 7 mm to 10 mm, and a profile back pattern of less than 0,25 mm deep. 4.1.2.2 Test substrate, conforming to the requirements given in 3.5.1. 4.1.3 Apparatu

37、s 4.1.3.1 Test mass, less than 50 mm 50 mm cross-sectional area and capable of exerting a uniform force of (20 0,05) N. 4.1.3.2 Pull-head plates, square metallic plates with a dimension of (50 1) mm, a minimum thickness of 10 mm, and a suitable fitting for connection to the test machine. 4.1.3.3 Tes

38、t machine, for the direct pull tensile force test, with suitable capacity and sensitivity. The machine shall be capable of applying the load to the pull-head plate at the rate of (250 50) N/s through a suitable fitting that does not exert any bending force.4 ISO 2013 All rights reserved ISO 13007-2:

39、2013(E) 4.1.4 Procedure Apply a thin layer of the adhesive, mixed in accordance with 3.4.1, to the concrete slab using a straight edge trowel. Then, apply a thicker layer and comb using a notched trowel having 6 mm 6 mm notches at 12 mm centres. The trowel shall be held at an angle of approximately

40、60 to the substrate at a right angle to one edge of the slab and shall be drawn across the slab parallel to that edge (in a straight line). After 5 min, 10 min, 20 min, 30 min, or longer, place at least 10 test tiles 50 mm apart on the adhesive within 30 s. Tiles are placed on no more than four ribs

41、 for all adhesives. Load each tile with (20 0,05) N for 30 s. After storing for 27 d under standard conditions, bond the pull-head plates to the tiles with a suitable high-strength adhesive (e.g. epoxy adhesive). After a further 24 h storage under standard conditions, determine the tensile adhesion

42、strength of the adhesive by applying a force increasing at a constant rate of (250 50) N/s. 4.1.5 Evaluation and expression of results The individual tensile adhesion strengths are quoted to 0,1 N/mm 2using Formula (1): s (1) where A s is the individual tensile adhesion strength, in N/mm 2 ; L is th

43、e total tensile load, in N; A is the bonding area, in mm 2(2 500 mm 2 ). The tensile adhesion strength for each time interval is determined as follows. 1) Determine the mean of the 10 values. 2) Discard the values falling out of the range of 20 % of the mean value. 3) If five or more values remain,

44、determine the new mean. 4) If less than five values remain, repeat the test. 5) Determine the mode of failure of the test units (see 3.6). The open time, in minutes, is the maximum time interval at which the adhesive meets the tensile adhesion strength requirement defined in ISO 13007-1 for open tim

45、e. 4.1.6 Test report The information listed in 3.7.1, items a) to i), shall be provided as well as 3.7.2, item a) (open time in minutes). 4.2 Determination of slip 4.2.1 General Slip shall be tested following the general test conditions and procedures given in Clause 3 and the specific instructions

46、which follow. ISO 2013 All rights reserved 5 ISO 13007-2:2013(E) 4.2.2 Test materials 4.2.2.1 Ceramic tiles, Group BI afully vitrified tile in accordance with ISO 13006, with a water absorption of 0,5 % by mass, unglazed, with plain adhering surface, and with facial dimensions of (100 1) mm (100 1)

47、mm, mass of (200 10) g, and a thickness in the range of 8 mm to 10 mm. 4.2.2.2 Concrete test substrate, conforming to the requirements given in 3.5. 4.2.3 Apparatus 4.2.3.1 Steel straight edge 4.2.3.2 Clamps 4.2.3.3 Masking tape, 25 mm wide. 4.2.3.4 Spacers, two pieces, made from stainless steel, wi

48、th a thickness of (25 0,5) mm (25 0,5) mm (10 0,5) mm. 4.2.3.5 Mass, capable of exerting a force of (50 0,1) N, with a cross-sectional area of less than (100 1) mm (100 1) mm. 4.2.3.6 Vernier caliper, accurate to 0,01 mm. 4.2.4 Procedure Secure the steel straight edge at the top of the concrete subs

49、trate so that its bottom edge is horizontal when the slab is raised to its vertical position. Position a 25-mm-wide masking tape immediately below the steel straight edge and apply a thin layer of the adhesive to the concrete slab using a straight edge trowel. Then, apply a thicker layer of adhesive to the surface of the concrete substrate so that it just overlaps the bottom edge of the masking tape. Comb the adhesive at ri