SAE J 1553-1995 Cross Peel Test for Automotive-Type Adhesives for Fiber reinforced plastic (FRP) Bonding《粘合纤维增强塑料(FRP)用的车用胶粘剂的交叉剥离试验》.pdf
《SAE J 1553-1995 Cross Peel Test for Automotive-Type Adhesives for Fiber reinforced plastic (FRP) Bonding《粘合纤维增强塑料(FRP)用的车用胶粘剂的交叉剥离试验》.pdf》由会员分享,可在线阅读,更多相关《SAE J 1553-1995 Cross Peel Test for Automotive-Type Adhesives for Fiber reinforced plastic (FRP) Bonding《粘合纤维增强塑料(FRP)用的车用胶粘剂的交叉剥离试验》.pdf(6页珍藏版)》请在麦多课文档分享上搜索。
1、SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirelyvoluntary, and its applicability and suitability for any particular use, including any patent infringement arising therefro
2、m, is the sole responsibility of the user.”SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions.QUESTIONS REGARDING THIS DOCUMENT: (724) 772-8512 FAX: (724) 776-0243TO PLACE A DOCUMENT
3、 ORDER; (724) 776-4970 FAX: (724) 776-0790SAE WEB ADDRESS http:/www.sae.orgCopyright 1995 Society of Automotive Engineers, Inc.All rights reserved. Printed in U.S.A.SURFACEVEHICLE400 Commonwealth Drive, Warrendale, PA 15096-0001STANDARDSubmitted for recognition as an American National StandardJ1553R
4、EV.APR95Issued 1986-05Revised 1995-04Superseding J1553 MAY86(R) CROSS PEEL TEST FOR AUTOMOTIVE TYPE ADHESIVES FOR FIBER-REINFORCED PLASTIC (FRP) BONDING1. ScopeThis SAE Recommended Practice describes a cross peel test method for use in measuring thebonding characteristics of automotive-type adhesive
5、s for joining fiber-reinforced plastics to themselves and tometals.2. References2.1 Applicable PublicationsThe following publications form a part of the specification to the extent specifiedherein. Unless otherwise indicated the latest revision of SAE publications shall apply.2.1.1 ASTM PUBLICATIONS
6、Available from ASTM, 100 Barr Harbor Drive, West Conshohocken, PA 19428-2959.ASTMD1002Test Method for Strength Properties of Adhesives in Shear by Tension Loading (Metal-to-Metal)ASTM D 55733. Test Substrate3.1 SubstratesFiber-reinforced plastic as specified. Metal composition and roughness as speci
7、fied.3.2 DimensionsFiber-reinforced plastic parts shall be cut into flat coupons 25.4 mm x 75 mm (1.0 in x 3.0 in) ata nominal thickness of 2.5 mm (0.1 in). In the case of FRP to metal bonding, metal thickness will be nominally1.5 mm (0.060 in) or as agreed upon by the automotive engineer. Shearing
8、the FRP coupons is notrecommended.NOTEIf samples are cut with a diamond saw which is water cooled, the samples must be dry prior tobonding.3.3 Surface PreparationSurface preparation of FRP will be in accordance with the adhesives suppliersrecommendations. Surface roughening, solvent cleaning, and su
9、rface primers are acceptable provided theydo not reduce FRP bulk properties. Any surface preparation must be adaptable to actual productionsituations. Metals will be machined to eliminate burrs or bevels. They will be clean and dry, or surface treatedprior to bonding according to procedures prescrib
10、ed by the adhesive manufacturer.COPYRIGHT Society of Automotive Engineers, Inc.Licensed by Information Handling ServicesSAE J1553 Revised APR95-2-4. Preparation of Test Joints4.1 Application of AdhesiveAdhesive will be applied in accordance with the adhesive suppliersrecommendations. In the case of
11、two-part adhesives, mixing will be in accordance with suppliers suggestedprocedures.4.2 Adhesive CureAdhesive will be cured at room temperature or elevated temperature using prescribedconditions determined by the adhesive supplier, provided they can be reasonably adapted to productionsituations.4.3
12、Joint GeometryJoint geometry will be as shown in Figure 1. Joint geometry will be controlled byappropriate fixturing using glass beads or other suitable means to control a 0.76 mm (0.030 in) adhesivebondline thickness. The amount of glass beads in the bondline will be the minimum number needed to ho
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- SAEJ15531995CROSSPEELTESTFORAUTOMOTIVETYPEADHESIVESFORFIBERREINFORCEDPLASTICFRPBONDING 粘合 纤维 增强塑料 FRP
![提示](http://www.mydoc123.com/images/bang_tan.gif)
链接地址:http://www.mydoc123.com/p-1026389.html