SAE AMS-P-83461-1998 Packing Preformed Petroleum Hydralic Fluid Resistant Improved Performance at 275 Degrees F (135 Degrees C)《275F(135℃)时性能增强的耐石油液压液的可调节填充物》.pdf

《SAE AMS-P-83461-1998 Packing Preformed Petroleum Hydralic Fluid Resistant Improved Performance at 275 Degrees F (135 Degrees C)《275F(135℃)时性能增强的耐石油液压液的可调节填充物》.pdf》由会员分享，可在线阅读，更多相关《SAE AMS-P-83461-1998 Packing Preformed Petroleum Hydralic Fluid Resistant Improved Performance at 275 Degrees F (135 Degrees C)《275F(135℃)时性能增强的耐石油液压液的可调节填充物》.pdf（16页珍藏版）》请在麦多课文档分享上搜索。

1、SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and enginee ring sciences. The use of this report is entirelyvoluntary, and its applicability and suitability for any particular use, including any patent infringement arising therefr

2、om, is the sole responsibility of the user.”SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invit es your written comments and suggestions.Copyright 1998 Society of Automotive Engineers, Inc.All rights reserved. Printed in U.

3、S.A.QUESTIONS REGARDING THIS DOCUMENT: (724) 772-7161 FAX: (724) 776-0243TO PLACE A DOCUMENT ORDER: (724) 776-4970 FAX: (724) 776-0790SAE WEB ADDRESS: http:/www.sae.org400 Commonwealth Drive, Warrendale, PA 15096-0001AEROS PACE MATERIAL SPECIFIC ATIONSubmitted for recognition as an American National

4、 StandardAMS-P-83461Issued APR 1998Packing, Preformed, Petroleum Hydraulic Fluid Resistant,Improved Performance at 275F (135C)NOTICEThis document has been taken directly from U.S. Military Specification MIL-P-83461B, Amendment 3, and contains only minor editorial and format changes required to bring

5、 it into conformance with the publishing requirements of SAE technical standards. The initial release of this document is intended to replace MIL-P-83461B, Amendment 3. Any part numbers established by the original specification remain unchanged.The original Military Specification was adopted as an S

6、AE standard under the provisions of the SAE Technical Standards Board (TSB) Rules and Regulations (TSB 001) pertaining to accelerated adoption of government specifications and standards. TSB rules provide for (a) the publication of portions of unrevised government specifications and standards withou

7、t consensus voting at the SAE Committee level, and (b) the use of the existing government specification or standard format.Any material relating to qualified product lists has not been adopted by SAE. This material was part of the original military specification and is reprinted here for historic re

8、ference only.1. SCOPE:1.1 Scope: This specification covers O-ring packings for use with petroleum based hydraulic fluids conforming to MIL-H-5606 and MIL-H-83282 over the temperature range of -65 to 275F (-54 to 135C). This material gives improved high temperature performance over materials conformi

9、ng to MIL-P-25732.1.2 Sizes: The O-rings conform to sizes shown in MIL-P-83461/1.AMS-P-83461 SAE AMS-P-83461- 2 -2. APPLICABLE DOCUMENTS: The following documents, of the issue in effect on date of invitation for bids or request for proposal, form a part of this specification to the extent specified

10、herein. 2.1 U.S. Government Publications: Available from DODSSP, Subscription Services Desk, Building 4D, 700 Robbins Avenue, Philadelphia, PA 19111-5094.MIL-P-4861 Packing, Preformed, Rubber, Packaging of MIL-H-5440 Hydraulic Systems, Aircraft, Types I and II, Design, Installation, and Data Require

11、ments ForMIL-G-5514 Gland Design, Packings, Hydraulic, General Requirements forMIL-H-5606 Hydraulic Fluid, Petroleum Base, Aircraft, Missile, and OrdanceMIL-H-6083 Hydraulic Fluid, Petroleum Base for Preservation and OperationMIL-S-18729 Steel Plate, Sheet, and Strip, Alloy 4130, Aircraft QualityMIL

12、-P-25732 Packing, Preformed, Petroleum Hydraulic Fluid Resistant, Limited Service at275F (135C)MIL-H-83282 Hydraulic FLuid, Fire Resistant, Synthetic Hydrocarbon Base, AircraftMIL-P-83461/1 Packings, Preformed, Petroleum Hydraulic Fluid Resistant, Improved Performance at 275F (135C), Sizes and Toler

13、ancesMIL-P-83461/2 Packings, Preformed, Petroleum Hydraulic Fluid Resistant, Improved Performance at 275F (135C) for Use in Boss Fittings, Sizes and TolerancesMIL-STD-105 Sampling Procedures and Tables for Inspection by AttributesMIL-STD-413 Visual Inspection Guide for Rubber O-ringsQQ-A-250/4 Alumi

14、num Alloy 2024, Plate and SheetQQ-A-250/11 Aluminum Alloy 6061, Plate and SheetQQ-A-250/12 Aluminum Alloy 7075, Plate and Sheet2.2 SAE Publications: Available from SAE, 400 Commonwealth Drive, Warrendale, PA 15096-0001.AMS 3020 Oil, Reference, for “L” Stock Rubber TestingAMS 5513 Steel, Corrosion Re

15、sistant, Sheet, Strip, and Plate, 19Cr - 9.2Ni (SAE 30304), Solution Heat TreatedAMS 5630 Steel, Corrosion Resistant, Bars, Wire, and Forgings, 17Cr - 0.52Mo (0.95 - 1.20C) (SAE 51440C)2.3 ASTM Publications: Available from ASTM, 100 Barr Harbor Drive, West Conshohocken, PA 19428-2959.ASTM D 1414 Rub

16、ber O-ringsAMS-P-83461 SAE AMS-P-83461- 3 -2.4 ANSI Publications: Available from ANSI, 11 West 42nd Street, New York, NY 10036-8002.ANSI B46.1 Surface Tecture (Surface Roughness, Waviness and Lay)3. REQUIREMENTS: 3.1 Qualification: The packings furnished under this specification shall be a product w

17、hich has been tested and passed the qualification tests specified herein and has been listed on or approved for listing on the applicable qualified products list.3.2 Materials: This specification originally required a specific formulation which was developed under an Air Force Materials Laboratory c

18、ontract. This exact formulation is no longer required but the formulation shown below is recommended since it will meet the requirements of this specification when properly processed.1. Source: The Goodyear Tire and Rubber Company2. Source: Several3. Source: Uniroyal Chemical4. Source: Bayer5. Sourc

19、e: C. P. Hall6. Source: C. P. Hall7. Source: R. T. Vanderbilt Co., Inc.Ingredients Parts by WeightChemigum N917 1 100.0Magnesium Oxide 2 5.0Zinc Oxide 2 5.0N330 RAF 2 40.0N550 FEF 2 35.0Aminox 3 1.5Antioxidant ZMB 4 1.5Dibutyloxyethyl Sebacate 5 10.0Diethylhexyl Azelate 6 10.0Varox 7 3.5AMS-P-83461

20、SAE AMS-P-83461- 4 -3.2 (Continued):The cure shall be 4 minutes at 370F. This cure has been used successfully in molds which are attached to the plates of curing presses. If the molds are not attached to the platens other curing conditions will have to be used. The alternate cure must be equivalent

21、to the 4 minutes at 370F cure and the material must meet the physical property requirements of this specification.A very significant difference in the ability to withstand dynamic cycling has been noted between batches of this material. Physical property tests do not show significant differences. It

22、 appears that the age of the Varox may be a factor although this has not been proven. Work is continuing to attempt to find the exact causes of the differences in cycling. In the interim, fresh Varox should be used to make this compound. This is particularly important during production because cycli

23、ng tests are not conducted as a part of quality conformance inspection. Dynamic cycling tests shall be run on samples of production batches of this material at various intervals at the discretion of the qualifying agency.3.3 Dimensions and tolerances: The dimensions and tolerances of O-rings procure

24、d to this specification shall conform toMIL-P-83461/1 or MIL-P-83461/2.3.4 Physical properties: The physical properties of the rubber shall conform to the values given in Table I.AMS-P-83461 SAE AMS-P-83461- 5 -Table I. Physical PropertiesOriginal Properties RequirementsSpecific gravityHardness, Typ

25、e A, pointsTensile strength, psiElongation,%Tensile stress (modulus psi at100% elongation)Temperature Retraction, TR-1050% elongation and 10% return, FCorrosion and adhesionAs determined75 51350, minimum125, minimum650, minimum-49, maximumSlight corrosion allowed on4130 steel, none on other metalsAf

26、ter aging 70 hours at 275 5F in ARM 201 (AMS-3020) Hardness change, Type A, pointsTensile strength decrease,%Elongation decrease,%Volume change,%Compression set, 25% deflection % of original deflectionTemperature Retraction, TR-1050% elongation and 10% return, F+5,-1050, maximum35, maximum10 to 2035

27、, maximum-49, maximumAfter aging 70 hours at 275 5Fin MIL-H-83282Hardness change, Type A, pointsTensile strength decrease,%Elongation decrease,%Volume change,%Compression set, 25% deflection,% of original deflectionTemperature Retraction, TR-1050% elongation and 10% Return, F+5, 1040 maximum35 maxim

28、um0 to 1545 maximum-49 maximumAfter aging 70 hours at 275F 5F in airCompression set, 25% deflection,% of original deflection67, maximumAfter aging 60 days at 75 5Fin airCompression set, 25% deflection,% of original deflection25, maximumAfter aging 60 days at 75 5F in ARM 201, (AMS-3020)Compression s

29、et, 25% deflection,% of original deflection 20, maximumAMS-P-83461 SAE AMS-P-83461- 6 -3.4.1 Variations: The permissible variations in physical properties during actual production from those values obtained in the qualification tests shall be as follows:a. Specific gravity 0.02b. Tensile strength, p

30、ercent 20c. Elongation, percent 20In addition, all physical properties tested shall meet the requirement specified in Table I.3.5 Dynamic cycling: When tested in accordance with 4.7, the O-rings shall withstand a minimum of 110,000 cycled without failure. Failure is determined as the number of cycle

31、s at which a test ring leaks a total of 70 ml of hydraulic fluid. Each test consists of 2 test cells containing 2 test rings each. A minimum of 3 test runs shall be conducted making a total of 6 test cells to be treated. The number of cycles until failure shall be recorded. The highest number of cyc

32、les and the lowest number of cycles shall be discarded. The remaining 4 values shall be averaged and that value must be 110,000 minimum for the O-rings to pass the test.3.6 Identification: All O-rings shall be individually packaged. Each envelope shall have the following information printed on the o

33、utside:a. National Stock Number.b. Military Part Number.c. Material Specification.d. Manufacturers Name.e. Manufacturers Compound Number.f. Manufacturers Batch Number.g. Contract Number.h. Cure Date.4. QUALITY ASSURANCE PROVISIONS: 4.1 Responsibility for inspection: Unless otherwise specified in the

34、 contract or purchase order, the supplier is responsible for the performance of all inspection requirements as specified herein. Except as otherwise specified in the contract or order, the supplier may use his own or any other facility suitable for the performance of the inspection requirements spec

35、ified herein, unless disapproved by the Government. The Government reserves the right to perform any of the inspections set forth in the specification where such inspections are deemed necessary to assure supplies and services conform to prescribed requirements.AMS-P-83461 SAE AMS-P-83461- 7 -4.1.1

36、Responsibility for compliance: All items shall meet all requirements of sections 3 and 5. The inspection set forth in this specification shall become a part of the contractors overall inspection system or quality program. The absence of any inspection requirements in this specification shall not rel

37、ieve the contractor of the responsibility of ensuring that all products or supplies submitted to the Government for acceptance comply with all requirements of the contract. Sampling inspection, as part of the manufacturing operations, is an acceptable practice to ascertain conformance to requirement

38、s; however, this does not authorize submission of known defective material, either indicated or actual, nor does it commit the Government to accept defective material.4.2 Classification of tests: The inspection and testing of the rubber shall be classified as follows:a. Qualification tests (see 4.3)

39、.b. Quality conformance inspection (see 4.4).4.3 Qualification tests: 4.3.1 Samples: Test samples shall be O-rings conforming to Size -214 of MIL-P-83461/1. Size -218O-rings are also required for the dynamic cycling test (see 4.7). Hardness shall be determined on hardness discs of at least 1/4 inch

40、thickness.4.3.2 Tests: Qualification tests shall consist of all the tests specified in 4.6 and 4.7.4.4 Quality conformance inspection: 4.4.1 Sampling for inspection: Sampling for quality conformance inspection shall be in accordance with MIL-STD-105, except where otherwise indicated herein. Quality

41、conformance tests are required for all production batches of material.4.4.1.1 Batch: A batch shall be the quantity of material compounded on a mill or mixer at one time. A batch will always have to include M83461/1 -214 O-rings and hardness discs for quality conformance tests. A batch shall consist

42、of a maximum of 200 pounds. Quality conformance tests shall be conducted on each 200 pounds if the batch size is more than 200 pounds.4.4.2 Quality conformance test samples: The test samples shall be Size -214 O-rings conforming to MIL-P-83461/1. Hardness discs shall be used for hardness determinati

43、ons.4.4.3 Inspection of materials and components: The supplier is responsible for insuring that materials and components used were manufactured, tested, and inspected in accordance with referenced subsidiary specifications and standards to the extent specified or if none, in accordance with this spe

44、cification (see 4.1). In the event of conflict, this specification shall govern. Inspection records shall be kept complete and available to the procuring activity at all times.AMS-P-83461 SAE AMS-P-83461- 8 -4.4.4 Inspection of the end item: Examination of the end item shall be in accordance with th

45、e classification of defects and inspection levels set forth herein. The lot size, for the purpose of determining the sample size in accordance with MIL-STD-105, shall be expressed in units of O-rings.4.4.4.1 Examination for defects in appearance and workmanship: The examination shall be in accordanc

46、e with MIL-STD-413. The sample size shall be in accordance with inspection level II of MIL-STD-105.4.4.4.2 Examination for dimensional defects: The examination shall be made to the tolerances specified in MIL-P-83461/1. The sample size shall be in accordance with inspection level II ofMIL-STD-105.4.

47、4.4.3 Examination for defects in packaging: An examination shall be made to determine that the packaging, packing, and markings comply with Section 5. The sample unit for this examination shall be one shipping container fully packed, selected just prior to the closing operation. Shipping containers

48、fully prepared for delivery shall be examined for closure defects.The sample size shall be in accordance with inspection level II of MIL-STD-105.Examine DefectPackaging Not the level specified. Not packagedas specified or required. Packagingmaterial, closures not as specified.Packing Not level speci

49、fied; not in accordance contract requirements.Container not as specified, closuresnot accomplished by specified orrequired methods or materials.Any nonconforming component, componentmissing, damaged or otherwise defective,affecting serviceability.Inadequate application of components,such as incomplete closure of caseliners, containing flaps loose orinadequate strapping, bulged or distortedcontainers.Count Less than specified or indicated quantity.Weight Cross weight exceeds specified requirements.Markings Interior or exterior markin