SAE AMS 7269B-1991 RINGS SEALING SILICONE (PVMQ) RUBBER Low Outgassing Space and Vacuum Service 45 - 55《低除气、空间和真空使用的45-55硅酮(PVMQ)橡胶密封环》.pdf

《SAE AMS 7269B-1991 RINGS SEALING SILICONE (PVMQ) RUBBER Low Outgassing Space and Vacuum Service 45 - 55《低除气、空间和真空使用的45-55硅酮(PVMQ)橡胶密封环》.pdf》由会员分享，可在线阅读，更多相关《SAE AMS 7269B-1991 RINGS SEALING SILICONE (PVMQ) RUBBER Low Outgassing Space and Vacuum Service 45 - 55《低除气、空间和真空使用的45-55硅酮(PVMQ)橡胶密封环》.pdf（11页珍藏版）》请在麦多课文档分享上搜索。

1、 AEROSPACE MATERIAL SPECIFICATION RINGS, SEALING, SILICONE (PVMQ) RUBBER Low Outgassing, Space and Vacuum Service 45 - 55 SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely

2、voluntary, and its applicability and suitability for any particular use, including any patent infringement arising therefrom, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites yo

3、ur written comments and suggestions. Copyright 2003 SAE International All rights reserved. No part of this publication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written

4、 permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: 724-776-4970 (outside USA) Fax: 724-776-0790 Email: custsvcsae.org SAE WEB ADDRESS: http:/www.sae.org AMS 7269B Issued DEC 1974 Revised APR 1991 Reaffirmed NOV 2003 Superseding AMS 7269B 1. SCOPE: 1.1 Form:

5、 This specification covers a low-outgassing silicone (PVMQ) rubber compound in the form of molded rings. 1.2 Application: Primarily for use in interplanetary space and other hard vacuums from -75 to +150C (-103 to +302F), with a minimum of condensable outgassing products. While within the earths atm

6、osphere, the silicone rubber compound is resistant to deterioration by ozone, smog, and weathering. 1.2.1 Seals conforming to this specification are intended for use in electrical connectors, components, assemblies, and vehicle segments on the external configuration of spacecraft, where no condensat

7、ion can be tolerated on critical surfaces (windows, optics, thermal control coatings, etc) when 0such critical surfaces may be as cold as 23C (73F) and the seal may be as hot as 150C (302F). Seals for man-inhabited areas of spacecraft may require additional testing and approval. 1.3 Safety - Hazardo

8、us Materials: While the materials, methods, applications, and processes described or referenced in this specification may involve the use of hazardous materials, this specification does not address the hazards which may be involved in such use. It is the sole responsibility of the user to ensure fam

9、iliarity with the safe and proper use of any hazardous materials and to take necessary precautionary measures to ensure the health and safety of all personnel involved. AMS 7269B SAE AMS 7269B - 2 - 2. APPLICABLE DOCUMENTS: The following publications form a part of this specification to the extent s

10、pecified herein. The latest issue of SAE publications shall apply. The applicable issue of other publications shall be the issue in effect on the date of the purchase order. 2.1 SAE Publications: Available from SAE, 400 Commonwealth Drive, Warrendale, PA 15096-0001. 2.1.1 Aerospace Material Specific

11、ations: AMS 2817 Packaging and Identification, Preformed Packings 2.1.2 Aerospace Standards: AS568 Aerospace Size Standard for O-Rings AS871 Manufacturing and Inspection Standards for Preformed Packings (O-Rings) 2.1.3 Aerospace Information Report: AIR851 O-Ring Tension Testing Calculations 2.2 ASTM

12、 Publications: Available from ASTM, 1916 Race Street, Philadelphia, PA 19103-1187. ASTM D 624 Rubber Property - Tear Resistance ASTM D 1329 Evaluating Rubber Property - Retraction at Low Temperature (TR Test) ASTM D 1414 Testing Rubber O-Rings ASTM D 3182 Rubber - Materials, Equipment, and Procedure

13、s for Mixing Standard Compounds and Preparing Standard Vulcanized Sheets 2.3 U.S. Government Publications: Available from Standardization Documents Order Desk, Building 4D, 700 Robbins Avenue, Philadelphia, PA 19111-5094 except as shown in 2.3.2. 2.3.1 Military Standards: MIL-STD-413 Visual Inspecti

14、on Guide for Elastomeric O-Rings AMS 7269B SAE AMS 7269B - 3 - 2.3.2 National Aeronautics and Space Administration (NASA) Publications: 2.3.2.1 NASA Johnson Space Center Publication: Available from Lyndon B. Johnson Space Center, Houston, TX 77058. SP-R-0022 Vacuum Stability Requirements of Polymeri

15、c Material for Spacecraft Application 2.3.2.2 NASA Goddard Space Flight Center (GSFC) Publication: Available from Goddard Space Flight Center, Greenbelt, MD 20771. GSFC X-735-69-471 Micro-Volatile Condensable Materials System for Polymer Outgassing Studies 3. TECHNICAL REQUIREMENTS: 3.1 Material: Sh

16、all be a compound, based on methyl-phenyl-vinyl silicone (PVMQ) rubber, selected, formulated, cured, postcured, and otherwise processed to outgas a minimal amount of condensable material in hard vacuum (below 1 x 10-6 torr) when heated to any temperature up to 150C (302F) and meeting the requirement

17、s of 3.2 (See 8.3). 3.2 Properties: The product shall conform to the following requirements; tests shall be performed on the product supplied, except for the tests of 3.2.1.4 and 3.2.5, and in accordance with ASTM D 1414 except as specified in 4.5, insofar as practicable: 3.2.1 As Received: 3.2.1.1

18、Hardness, Durometer “A“ or equivalent 50 5 3.2.1.2 Tensile Strength, 900 psi 4.5.1 minimum (6.21 MPa) 3.2.1.3 Elongation, minimum 400% 4.5.1 3.2.1.4 Tear Resistance, minimum 100 pounds force/ 4.5.2 inch (17.5 kN/m) 3.2.1.5 Corrosion None 3.2.1.6 Specific Gravity Preproduction Value 0.03 AMS 7269B SA

19、E AMS 7269B - 4 - 3.2.2 Dry Heat Resistance: Temperature: 225C 2 (437F 4) 3.2.2.1 Hardness Change Time: 70 hours 0.5 Durometer “A” or equivalent -10 to +10 3.2.2.2 Tensile Strength Change, maximum -20% 3.2.2.3 Elongation Change, maximum -35% 3.2.3 Compression Set: Temperature: 175C 2 Percent of Orig

20、inal (347F 4) Deflection, maximum Time: 22 hours 0.3 Ring Cross Section Diameter 0.066 to 0.110 inch (1.68 to 2.79 mm), incl 25 Over 0.110 inch (2.79 mm) 20 3.2.4 Low-Temperature Resistance: 4.5.3 Temperature Retraction, TR10 point, maximum -73C (-99F) 3.2.5 Outgassing Hard Vacuum: 4.5.4 3.2.5.1 Tot

21、al Mass Loss, GSFC X-735-69-471 or maximum 1% JSC SP-R-0022 3.2.5.2 Collected Volatile GSFC X-735-69-471 or Condensable Material, JSC SP-R-0022 maximum 0.1% 3.2.5.3 Visible Condensable 4.5.5 Material None 3.3 Quality: Rings, as received by purchaser, shall be uniform in quality and condition, smooth

22、, as free from foreign material as commercially practicable, and free from internal imperfections detrimental to usage of the rings. Surface imperfections shall be no greater than permitted by MIL-STD-413. AMS 7269B SAE AMS 7269B - 5 - 3.4 Sizes and Tolerances: Shall be as specified on the drawing.

23、Standard size O-rings, as shown in AS568, may be described by a part number composed of this specification number followed by a dash and three digits indicating the desired AS568 size. Inspection for conformance to dimensional requirements shall be made in accordance with AS871. 4. QUALITY ASSURANCE

24、 ROVISIONS: 4.1 Responsibility for Inspection: The vendor of rings shall supply all samples for vendors tests and shall be responsible for performing all required tests except for outgassing in hard vacuum (3.2.5). The outgassing in hard vacuum tests shall be the responsibility of the purchaser. Pur

25、chaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the rings conform to the requirements of this specification. 4.2 Classification of Tests: 4.2.1 Acceptance Tests: Tests for the following requirements are acceptance tests and shall be perform

26、ed on each lot: Requirement Paragraph Reference Hardness, as-received 3.2.1.1 Tensile Strength, as-received 3.2.1.2 Elongation, as-received 3.2.1.3 Specific Gravity 3.2.1.6 Compression Set 3.2.3 Quality 3.3 Sizes and Tolerances 3.4 4.2.2 Periodic Tests: Tests for the following requirements are perio

27、dic tests and shall be performed at a frequency selected by the vendor unless frequency of testing is specified by purchaser: Requirement Paragraph Reference Tear Resistance, Die “B“ 3.2.1.4 Corrosion 3.2.1.5 Dry Heat Resistance 3.2.2 Low-Temperature Resistance 3.2.4 AMS 7269B SAE AMS 7269B - 6 - 4.

28、2.3 Preproduction Tests: Tests for all technical requirements are preproduction tests and shall be performed prior to or on the first-article shipment of rings to a purchaser, when a change in ingredients and/or processing requires reapproval as in 4.4.2, and when purchaser deems confirmatory testin

29、g to be required. 4.2.3.1 For direct U.S. Military procurement, substantiating test data and, when requested, preproduction test material shall be submitted to the cognizant agency as directed by the procuring activity, contracting officer, or request for procurement. 4.3 Sampling and Testing: Shall

30、 be as follows: 4.3.1 For Acceptance Tests: Sufficient rings shall be taken at random from each lot to perform all required tests; the number of tests for each requirement shall be as specified in the applicable test procedure or, if not specified therein, not less than three. 4.3.1.1 A lot shall be

31、 all rings of the same size from the same batch of compound processed in one continuous run and presented for vendors inspection at one time. A lot shall not exceed 1000 rings or 300 pounds (136 kg), whichever is the lesser mass, and may be packaged in smaller quantities and delivered under the basi

32、c lot approval provided lot identification is maintained. 4.3.1.2 A batch shall be the quantity of compound run through a mill or mixer at one time. 4.3.1.3 When a statistical sampling plan has been agreed upon by purchaser and vendor, sampling shall be in accordance with such plan in lieu of sampli

33、ng as in 4.3.1 and the report of 4.6 shall state that such plan was used. 4.3.1.4 If rings smaller than AS568-010 are ordered, seven rings of -214 or -218 size shall be provided for determining tensile strength and elongation; such rings shall be from the same batch of compound cured in the same pre

34、ss and under the same conditions as the rings they represent and postcured with those rings. 4.3.1.5 Not less than two rings for compression set tests. 4.3.2 For Periodic Tests: As in 4.3.1 for the batch from which the samples are taken. 4.3.2.1 One ASTM D 3182 test sheet for tear resistance tests.

35、4.3.2.2 Not less than one ring for corrosion tests. 4.3.2.3 Not less than seven rings for dry heat resistance tests. 4.3.2.4 Not less than one ring for low-temperature resistance tests. AMS 7269B SAE AMS 7269B - 7 - 4.3.3 For Preproduction Tests: As agreed upon by purchaser and vendor and as follows

36、: 4.3.3.1 Tests for resistance to outgassing in hard vacuum shall be performed on specimens cut from ASTM D 3182 test sheets. 4.4 Approval: 4.4.1 Sample rings and test sheets shall be approved by purchaser before rings for production use are supplied, unless such approval be waived by purchaser. Res

37、ults of tests on production rings shall be essentially equivalent to those on the approved sample rings. 4.4.2 Vendor shall establish, for each size of ring, parameters for the process control factors which will produce rings meeting the technical requirements; these shall constitute the approved pr

38、ocedures and shall be used for manufacturing production rings. If necessary to make any change in parameters for the process control factors, vendor shall submit for reapproval a statement of the proposed changes in ingredients and/or processing and, when requested, sample rings and test sheets. Pro

39、duction rings incorporating the revised procedures shall not be shipped prior to receipt of reapproval. 4.4.2.1 Control factors for producing rings include, but are not limited to, the following: Base polymer, molecular weight distribution, and pretreatment Compound ingredients and proportions there

40、of within established limits Sequence of mixing compound ingredients Type of mixing equipment Method and equipment for preparing preforms Basic molding procedure (compression, transfer, injection) Curing time and temperature (must be held within plus two, minus zero half lives of the decomposition o

41、f the peroxide used) Pressure (variations of 10% are permissible) First postcure step for complete removal of curing by-products Overall postcure steps, times, and temperatures Finishing methods Methods of inspection Protection from external contamination 4.4.2.1.1 Any of the above process control f

42、actors for which parameters are considered proprietary by the vendor may be assigned a code designation. Each variation in such parameters shall be assigned a modified code designation. AMS 7269B SAE AMS 7269B - 8 - 4.5 Test Methods: 4.5.1 Tensile Strength and Elongation: For rings-smaller than can

43、be tested using 1/2 inch (12.7 mm) diameter spools, use successively smaller spools having diameters half the diameter of the next larger size, 1/4 inch (6.4 mm), 1/8 inch (3.2 mm), or 1/16 inch (1.6 mm), as required. Spool mounts shall be rotated 180 degrees relative to each other to allow closing

44、to the compound zero elongation for small O-rings. The spool center-to-center distance for zero elongation of the ring can be computed from the following formula from AIR851: d = (D S)/2. Calculations of tensile strength and elongation may be made in accordance with AIR851. 4.5.2 Tear Resistance: Sh

45、all be determined in accordance with ASTM D 624 on specimens cut from a standard sheet, using Die B. 4.5.3 Low-Temperature Resistance: May be determined in accordance with ASTM D 1329, using 1-inch (25-mm) long T-50 specimens cut from a standard test sheet in lieu of testing rings. In all cases, spe

46、cimens shall be stretched to 300% elongation and cooled to below 100 (-148F) in a bath of denatured alcohol chilled with liquid nitrogen. 4.5.4 Total Mass Loss and Collected Volatile Condensable Material: The major parameters of the mass loss and collected volatile condensable material test of both

47、GSFC X-735-69-471 and JSC SP-R-0022 are essentially as follows: A sample of not less than 100 mg is reduced to pieces less than 1/16 inch (1.6 mm) in any dimension. The sample is preconditioned at 23C 2 (73F 4) and approximately 50% relative humidity for 24 hours before being weighed to the nearest

48、microgram. The sample is placed in the outgassing equipment described in the applicable specification and the equipment evacuated to 1 x 10-6 torr or less. The specimen temperature is raised to 125C 1 (257F 2) and held at temperature for 24 hours 0.5. Volatile material is allowed to condense on a guarded collector plate of 1.5 inches (38 mm) diameter maintained at 25C 2 (77F 4). The vacuum source and heater current are cut off and clean, dry nitrog