SAE AMS 3197L-2009 Sponge Chloroprene (CR) Rubber Soft《氯丁(CR)橡胶软海绵》.pdf

《SAE AMS 3197L-2009 Sponge Chloroprene (CR) Rubber Soft《氯丁(CR)橡胶软海绵》.pdf》由会员分享，可在线阅读，更多相关《SAE AMS 3197L-2009 Sponge Chloroprene (CR) Rubber Soft《氯丁(CR)橡胶软海绵》.pdf（7页珍藏版）》请在麦多课文档分享上搜索。

1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions. Copyright 2009 SAE International All rights reserved. No part of this publication m

3、ay be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: 724-776-4970 (outside USA)

4、 Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS3197L AEROSPACE MATERIAL SPECIFICATION AMS3197L Issued 1942-12 Reaffirmed 2007-03 Revised 200

5、9-07 Superseding AMS3197K Sponge, Chloroprene (CR) Rubber Soft RATIONALE AMS3197L results from a Five Year Review and update of this specification. 1. SCOPE 1.1 Form This specification covers a chloroprene (CR) rubber sponge in the form of sheet, strip, molded shapes, or other forms, as ordered. 1.2

6、 Application These products have been used typically for general applications requiring the use of open-cell, soft rubber sponge pads and seals operating from -40 to +176 F (-40 to +80 C), but usage is not limited to such applications. 1.3 Safety - Hazardous Materials While the materials, methods, a

7、pplications, and processes described or referenced in this specification may involve the use of hazardous materials, this specification does not address the hazards which may be involved in such use. It is the sole responsibility of the user to ensure familiarity with the safe and proper use of any

8、hazardous materials and to take necessary precautionary measures to ensure the health and safety of all personnel involved. 2. APPLICABLE DOCUMENTS The issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The

9、supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the last published issue of that document shall apply. 2.1 SAE Publications Available from SAE Inter

10、national, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA), www.sae.org. AMS2810 Identification and Packaging, Elastomeric Products Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproductio

11、n or networking permitted without license from IHS-,-,-SAE AMS3197L Page 2 of 7 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org. ASTM D 1056 Flexible Cellular Materials Sponge or Expanded

12、 Rubber 3. TECHNICAL REQUIREMENTS 3.1 Material Shall be a compound, based on a chloroprene (CR) elastomer with agents to form an open-cell sponge, suitably cured to produce a product meeting the technical requirements of this specification. 3.1.1 Color Shall be black. 3.1.2 Finish The top and bottom

13、 surfaces of sheet and strip and the exterior surfaces of molded parts shall have a natural skin finish. Fabric or wire mesh type of surface impressions are not objectionable. 3.1.3 Vulcanized Joints Vulcanized joints are permissible in molded products where the finished product is larger than is us

14、ual industry practice to mold in one section. If a vulcanized joint is necessary, the joint shall have the same strength, size, and color as the parent material. 3.2 Properties Sponge shall conform to the following requirements; tests shall be performed on the sponge supplied and in accordance with

15、ASTM D 1056 except as otherwise specified herein. 3.2.1 Compression Deflection Shall be 1 to 4 psi (6.9 to 27.6 kPa) at 68 to 86 F (20 to 30 C). 3.2.2 Specific Volume Shall be as shown in Table 1 for each nominal thickness; a tolerance of 10% will be allowed. 3.2.3 Hydrogen Ion Concentration (pH) Sh

16、all be 7.0 1.0, determined in accordance with 4.5.1. 3.2.4 Dry Heat Resistance Shall be as follows, determined in accordance with 4.5.2. Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-SAE AMS3197L P

17、age 3 of 7 TABLE 1 - SPECIFIC VOLUME Nominal Thickness Inches Nominal Thickness Millimeters Specific Volume Cubic Inches per Pound Specific Volume cm3/gram 1/32 0.8 26 0.92 1/16 1.6 36 1.30 3/32 2.4 42 1.52 1/8 3.2 48 1.73 3/16 4.8 55 1.99 1/4 6.4 58 2.10 5/16 7.9 61 2.20 3/8 9.5 63 2.28 1/2 12.7 66

18、 2.38 5/8 15.9 70 2.53 3/4 19.0 73 2.64 7/8 22.2 77 2.78 1 25.4 80 2.89 1- 1/2 38.1 87 3.14 3.2.4.1 Compression Deflection Change -5 to +30% 3.2.4.2 Specific Volume Change -10 to +10% 3.2.4.3 Bend (Flat) No cracking or checking. 3.2.5 Compression Set Shall be as follows, determined at 158 F 2 (70 C

19、1) for 22 hours 0.2. 3.2.5.1 Percent of Original Deflection Not higher than 40. 3.2.5.2 Percent of Original Thickness Not higher than 20. 3.2.6 Low-Temperature Flexibility When specified, the product shall have low-temperature flexibility acceptable to purchaser, determined by a procedure agreed upo

20、n by purchaser and vendor. 3.2.7 Weather Resistance When specified, the product shall have weather resistance acceptable to purchaser, determined by a procedure agreed upon by purchaser and vendor. Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or net

21、working permitted without license from IHS-,-,-SAE AMS3197L Page 4 of 7 3.3 Quality The product, as received by purchaser, shall be uniform in quality and condition, smooth, as free from foreign materials as commercially practicable, and free from imperfections detrimental to usage of the product. 3

22、.4 Dimensions and Tolerances Dimensions and tolerances shall be as specified in the parts standard, drawing or purchase document. If not specified, shall conform to the following values; measurements shall be made in accordance with ASTM D 1056. 3.4.1 Sheet and Strip 3.4.1.1 Thickness Shall be speci

23、fied in Table 2: TABLE 2A - THICKNESS TOLERANCE, INCH/POUND UNITS Nominal Thickness Inches Tolerance, Inch plus and minus Up to 1/8, incl 1/64 Over 1/8 to 1/2, incl 1/32 Over 1/2 3/64 TABLE 2B - THICKNESS TOLERANCE, SI UNITS Nominal Thickness Millimeters Tolerance, Millimeters plus and minus Up to 3

24、.2, incl 0.4 Over 3.2 to 12.7, incl 0.8 Over 12.7 1.2 3.4.1.2 Width Shall be specified in Table 3: TABLE 3A - WIDTH TOLERANCE, INCH/POUND UNITS Nominal Width Inches Tolerance, Inch plus and minus Up to 6, incl 1/16 Over 6 to 18, incl 1/8 Over 18 1/4 TABLE 3B - WIDTH TOLERANCE, SI UNITS Nominal Width

25、 Millimeters Tolerance, Millimeters plus and minus Up to 152, incl 1.6 Over 152 to 457, incl 3.2 Over 457 6.4 Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-SAE AMS3197L Page 5 of 7 3.5 Toxicologica

26、l Formulations The material shall have no adverse effects on the health of personnel when used for its intended purpose in accordance with manufacturers instructions and with appropriate handling procedures. 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The vendor of sponge shall

27、 supply all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the sponge conforms to specified requirements . 4.2 Classification of Tests All tec

28、hnical requirements are acceptance tests and preproduction tests and shall be performed prior to or on the initial shipment of sponge to a purchaser, on each lot, when a change in ingredients and/or processing requires reapproval as in 4.4.2, and when purchaser deems confirmatory testing to be requi

29、red. 4.3 Sampling and Testing Shall be as follows: 4.3.1 For Acceptance Tests Sufficient sponge shall be taken at random from each lot to perform all required tests. The number of determinations for each requirement shall be as specified in the applicable test procedure or, if not specified therein,

30、 not less than three. 4.3.1.1 A batch shall be all material run through a mixer at one time. 4.3.1.2 A lot shall be not more than 2500 pounds (1134 kg) of sponge from one batch. 4.3.1.3 When a statistical sampling plan has been agreed upon by purchaser and vendor, sampling shall be in accordance wit

31、h such plan in lieu of sampling as in 4.3.1 and the report of 4.6 shall state that such plan was used. 4.3.2 For Preproduction Tests As agreed upon by purchaser and vendor. 4.4 Approval 4.4.1 Sponge shall be approved by purchaser before sponge for production use is supplied, unless such approval be

32、waived by purchaser. Results of tests on production sponge shall be essentially equivalent to those on the approved sample. 4.4.2 Vendor shall use ingredients, manufacturing procedures, processes, and methods of inspection on production sponge which are essentially the same as those used on the appr

33、oved sample. If necessary to make any change in ingredients, in type of equipment for processing, or in manufacturing procedures, vendor shall submit for reapproval a statement of the proposed changes in ingredients and/or processing and, when requested, sample sponge. Production sponge made by the

34、revised procedure shall not be shipped prior to receipt of reapproval. Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-SAE AMS3197L Page 6 of 7 4.5 Test Methods 4.5.1 Hydrogen Ion Concentration (pH)

35、Dice approximately 1 cubic inch (16 cm3) of sponge to approximately 1/8 inch (3.2 mm) or smaller cubes and extract with continuous agitation for 60 minutes 6 with 100 mL of freshly distilled water. Determine pH of the extract by chemical means or pH meter. 4.5.2 Dry Heat Aging A sample of sponge 4 i

36、nches (102 mm) square shall be suspended for 22 hours 0.2 by a wire attached to one corner of the sample in a circulating-air convection oven operating at 212 F 2 (100 C 1). The sample shall be removed from the oven and trimmed to 2 inches (51 mm) square by removing 1 inch (25 mm) from each side pri

37、or to testing. Standard specimens shall be cut from the sample and tested by the procedure used for the sponge as received. Bend test specimens shall be the 1 inch (25 mm) wide strips produced in trimming the 4-inch (102-mm) square sample to a 2-inch (51-mm) square. 4.6 Reports The vendor of sponge

38、shall furnish with each shipment a report showing the results of tests to determine the conformance to the technical requirements. This report shall include the purchase order number, lot number, AMS3197L, vendors compound number, form or part number, and quantity. 4.7 Resampling and Retesting If an

39、y specimen fails, a retesting of three additional specimens for each nonconforming specimen shall be necessary for product acceptance. The same batch/lot of product used for the failed test shall be used for retesting. Failure of any retest specimen shall be cause for rejection. Results of all tests

40、 shall be reported. 5. PREPARATION FOR DELIVERY 5.1 Identification and Packaging Shall be as specified in the parts standard, drawing or purchase document. If not specified, shall be as follows: packaging shall be in accordance with AMS2810. A lot may be packaged in small quantities and delivered un

41、der the basic lot approval provided lot information is maintained. 5.1.1 Each package, box, and shipping container shall be permanently and legibly marked with the following when pertinent: Specification number AMS number with revision, class, grade, and type Manufacturers identification Manufacture

42、rs product designation Batch/lot number Date of manufacturing/packaging Shelf life expiration date Storage conditions 6. ACKNOWLEDGMENT A vendor shall mention this specification number and its revision letter in all quotations and when acknowledging purchase orders. 7. REJECTIONS Sponge not conformi

43、ng to this specification, or to modifications authorized by purchaser, will be subject to rejection. Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-SAE AMS3197L Page 7 of 7 8. NOTES 8.1 A change bar

44、 (|) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the previous issue of this document. An (R) symbol to the left of the document title indicates a complete revision of the document, including techn

45、ical revisions. Change bars and (R) are not used in original publications, nor in documents that contain editorial changes only. 8.2 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary; dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of the primary units and are presented only for information. PREPARED BY AMS COMMITTEE “CE“ Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-