1、MIL-P-L7L7LE 73 R 7779706 0433747 3 R 25 Mav 1990 SUPERSEDING 13 December 1977 (See 6.6) MIL-P-17171D(SH) MILITARY SPECIFICATION PLASTIC, LAMINATE, DECORATIVE, HIGH PRESSURE This specification is approved for use by the Naval Sea Systems Command, Department of the Navy, and is available for use by a
2、ll Departments and Agencies of the Department of Defense. 1. SCOPE 1.1 ScoDe. This specification establishes the requirements for protective, high pressure, decorative plastic laminates used to cover furniture and bulkhead surfaces, and for high pressure, decorative plastic laminates factory bonded
3、by the laminate manufacturer to aluminum panels used for non-structural bulkheads and overheads. 1.2 Classification. grades, as specified (see 6.2). The sheet material shall be of the following types and Type I - General purpose. Type IV - Fire retardant. Grade 1 - Nominal thickness 0.050 inch. Grad
4、e 2 - Nominal thickness 0.062 inch. Grade 1 - Laminate plus 0.045 inch aluminum sheathing. Grade 2 - Laminate plus 0.050 inch aluminum sheathing. Grade 3 - Laminate plus 0.060 inch aluminum sheathing, Type V - Fire retardant composite. 2. APPLICABLE DOCUMENTS 2.1 Government documents. I Beneficial c
5、omments (recommendations, additions, deletions) and any pertinent data which may be of use in improving this document should be addressed to: Commander, Naval Sea Systems Command, SEA 5523, Department of the Navy, Washington, DC 20362-5101 by using the self-addressed Standardization Document Improve
6、ment Proposal (DD Form 1426) appearing at the end of this document or by letter. AMSC N/A FSC 9330 DISTRIBUTION STATEMENT A. Approved for public release; distribution is unlimited. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-_. _ MIL-P-LIJLE 73 7
7、779906 0433750 T W MIL-P-l7171E(SH) 2.1.1 SDecification. standards. and.handbooks. The following specifica- tions, standards, and handbooks form a part of this document to the extent specified herein. those listed in the issue of the Department of Defense Index of Specifications and Standards (DODIS
8、S) and supplement thereto, cited in the solicitation (see 6.2). Unless otherwise specified, the issues of these documents are SPECIFICATION MI LI TARY MIL-L-19140 - Lumber and Plywood, Fire-Retardant Treated. STANDARDS MILITARY MIL- STD- 1186 - Cushioning, Anchoring, Bracing, Blocking and MIL-STD-16
9、23 - Fire Performance Requirements and Approved Waterproofing; With Appropriate Test Methods. Specifications for Interior Finish Materials and Furnishings (Naval Shipboard Use). Application of Packaging Requirements. MIL-STD-2073-1 - DoD Materiel Procedures for Development and (Unless otherwise indi
10、cated, copies of federal and military specificationc, standards, and handbooks are available from the Standardization Documents Order Desk, BLDG. 4D, 700 Robbins Avenue, Philadelphia, PA 19111-5094.) 2.2 Non-Government Dubiications. The following documents form a part of this document to the extent
11、specified herein. Unless otherwise specified, the issues of the documents which are DOD adopted are those listed in the issue of the DODISS cited in the solicitation. documents not listed in the DODISS are the issues of the documents cited in the solicitation (see 6.2). Unless otherwise specified, t
12、he issues of AMERICAN SOCIETY FOR TESTING AND MATERIALS (ASTM) D 3951 - Standard Practice for Commercial Packaging. (DoD adopted) E 84 - Standard Test Method for Surface Burning.Characteristics of Building Materials, (DoD adopted) (Application for copies should be addressed to the American Society f
13、or Testing and Materials, 1916 Race Street, Philadelphia, PA 19103.) NATIONAL ELECTRICAL MANUFACTURERS ASSOCIATION (NEMA) LD 3 - High-pressure Decorative Laminates. (DoD adopted) (Application for copies should be addressed to the National Electrical Manufacturers Association, 2101 L Street, NW, Wash
14、ington, DC 20037.) UNDERWRITERS LABORATORIES INC. (UL) UL 723 - Test for Surface Burning Characteristics of Building Materials. (Application for copies should be addressed to the Underwriters Laboratories Inc., 333 Pfingston Road, Northbrook, IL 60062.) 2 Provided by IHSNot for ResaleNo reproduction
15、 or networking permitted without license from IHS-,-,-MIL-P-L7L7LE 73 M 7779706 OLI33752 L . (Non-Government standards and other publications are normally available from These documents also the organizations that prepare or distribute the documents. may be available in or through libraries or other
16、 informational services.) 2.3 Order of Drecedence. In the event of a conflict between the text of this document and the references cited herein, the text of this document takes precedence. Nothing in this document, however, supersedes applicable laws and regulations unless a specific exemption has b
17、een obtained. 3. REQUIREMENTS 3.1 Material. - - - Type I and IV material shall consist of layers of fibrous sheet material, such as paper impregnated-with thermosetting resins and consoli- dated under heat and pressure to form a rigid, cured material. consist of high pressure plastic laminates facto
18、ry bonded to aluminum sheathing. Asbestos and components containing asbestos are prohibited. Type V shall 3.2 Form, The material shall be in the form of rectangular laminated/ composite sheets. 3.3 Color and Dattern. The color and decorative pattern of the laminate material shall be as specified (se
19、e 6.2). 3.4 Surface finish. The surface finish of the laminate material shall be as specified (see 6.2). 3.5 Dimensions and tolerances. Size of the laminate/composite sheets shall be as specified (see 6.2). length and width dimensions shall be minus O plus 1/2 inch, conform to table I, The maximum s
20、ize shall be 5 by 12 feet. Tolerances in Thickness shall TABLE I. Thickness. 3.6 Physical DroDerties. Physical properties shall conform to the requirements of table II. 3 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,- _- MIL-P-17171E 73 B 7977706 0
21、433752 3 a MIL-P-l717lE(SH) TABLE II. Phvsical DroDertv reauirements. Requirement Impact resistance Evidence of surface damage or break, height of drop, minimum Dimensional change, percent, maximum Machine direction Cross machine direction Resistance of surface to boiling water Blistering of surface
22、 Impairment of finish Wear resistance, number of cycles, minimum Radiant heat resistance, exposure time without permanent discoloration, crazing, seconds, minim- Test 4.4.1 4.4.2 4.4.3 4.4.4 4.4.5 50 inches 1.5 percent 1.9 percent no effect no effect 400 125 Type IV Grade 1 2J 45 inches 1.5 percent
23、1.9 percent no effect no effect 400 75 Grade 2 u 55 inches 0.5 percent 0.9 percent no effect no effect 400 125 (all grades) 45 inches D.5 percent D.9 percent no effect no effect 400 125 lJ Corresponds to NEMA type GP 50. 2J Corresponds to NEMA type FX 50. 3J Corresponds to NEMA type FR 62. 3.7 Light
24、 resistance. The decorative surface of the laminate material shall show not more than a slight change in color (see 4.4.6). 3.8 High temperature resistance. The decorative surface of the laminate material shall show not more than a slight change (see 4.4.7). 3.9 Conductive heat resistance (tvDe I an
25、d tvDe V only). The decorative The decorative surface of type V composite material surface of type I laminate material shall show not more than a slight change in color or surface texture. shall be unaffected (see 4.4.8). 4 Provided by IHSNot for ResaleNo reproduction or networking permitted without
26、 license from IHS-,-,-MIL-P-17171E 73 m 7777906 0133753 5 m MIL-P-l7171E(SH) 3.10 Stain resistance. The decorative surface of the laminate material shall be unaffected from reagents (test materials) 1 through 23 and shall have not more than a moderate effect from reagents (test materials) 24 through
27、 29 (see 4.4.9). 3.11 Machinabilitv. The laminate material shall not crack, chip, or delami- nate when drilled, countersunk, tapped, sawed, or machined (see 4.4.10). 3.12 Fire performance. The material shall meet the fire performance requirements specified in MIL-STD-1623 (see 4.4.11). 3.13 Workmans
28、hip. The decorative surface of the material shall contain no defects such as scratches, dents, heat marks, blisters, and wrinkles. The material shall be uniform in quality and appearance. 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibilitv for inspection. Unless otherwise specified in the contract or
29、 purchase order, the contractor is responsible for the performance of all inspection requirements (examinations and tests) as speciied herein. Except as otherwise specified in the contract or purchase order, the contractor may use his own or any other facilities suitable for the performance of the i
30、nspection requirements specified herein, unless disapproved by the Government. The Government reserves the right to perform any of the inspections set forth in the specification where such inspections are deemed necessary to ensure supplies and services conform to prescribed requirements. 4.1.1 Resp
31、onsibilitv for compliance. All ftems shall meet all requirements of sections 3 and 5. The inspection set forth in this Specification shall become a part of the contractors overall inspection system or quality program. absence of any inspection requirements in the specification shall not relieve the
32、contractor of the responsibility of ensuring that all products or supplies submitted to the Government for acceptance comply with all requirements of the contract. Sampling inspection, as part of the manufacturing operations, is an acceptable practice to ascertain conformance to requirements, howeve
33、r, this does not authorize submission of known defective material, either indicated or actual, nor does it commit the Government to accept defective material. The 4.2 Oualitv conformance inspection. Quality conformance shall consist of the examination and tests specified in table III (see 6.3). 5 Pr
34、ovided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-P-IILIE 73 m 7797706 0433754 7 m Number of sheets in lot 1 to 25 26 to 90 91 to 150. 151 to 280 . . 281 to 500 501 to 1800 1801 and over MIL-P-l7171E(SH) TABLE III, Oualitv conformance inspection. Num
35、ber of sheets to be examined 6 13 20 32 50 80 125 Impact resistance Dimensional change Resistance of surface to boiling water Wear resistance Radiant heat resistance Light resistance High temperature resistance Conductive heat resistance Stain resistance Machinab il i ty Fire performance Workmanship
36、 Requirement I Test -I table II table II table II table II table II 3.7 3.8 3.9 3.10 3.11 3.12 3.13 4.4.1 4.4.2 4.4.3 4.4.4 4.4.5 4.4.6 4.4.7 4.4.8 4.4.9 4.4.10 4.4.11 4.3 4.2.1.3 SamDlinrr for tests, Unless otherwise specified (see 4.4.1, 4.4.9, and 4.4.11), tests shall be conducted on samples from
37、 the first lot of sheets and on samples from every tenth lot thereafter. 4.3 Examination. Each sample sheet shall be examined for form, dimensions, tolerances, color and pattern, surface finish, and workmanship to determine and evaluate visual defects, 6 Provided by IHSNot for ResaleNo reproduction
38、or networking permitted without license from IHS-,-,-MIL-P-LIJLE 93 m 9999906 0433755 9 MIL-P-I7171E(SH) . 4.4 Tests. 4.4.1 ImDact resistance. Impact resistance tests shall be conducted in accordance with NEMA LD 3 on samples for lots not subject to other tests (see 4.2.1.3). 4.4.2 Dimensional chann
39、e. - Specimens shall be tested in accordance with NEMALD 3. 4.4.3 Boiling water resistance. Specimens shall be tested in accordance with NEMA LD 3. 4.4.4 Wear resistance. Specimens shall be tested in accordance with NEMA LD 3. 4.4.5 Radiant heat resistance. Specimens shall be tested in accordance wi
40、th NEMA LD 3, 4.4.6 Light resistance, Specimens shall be tested in accordance with NEMA LD 3. 4.4.7 Hiph temDerature resistance. Specimens shal with NEMA LD 3. 4.4.8 Conductive heat resistance. Specimens shall with NEMA LD 3. be tested in accordance be tested in accordance 4.4.9 Stain resistance. St
41、ain resistance tests shall be conducted in accordance with NEMA LD 3 on samples from lots not subject to other tests (see 4.2.1.3). 4.4.10 Machinability. Machinability of specimens shall be demonstrated when worked in accordance with NEMA LD 3. 4.4.11 Fire Derformance. Fire performance tests shall b
42、e conducted at a laboratory acceptable to the Naval Sea Systems Command (NAVSEA) at 12-month intervals in accordance with MIL-STD-1623. of ASTM E 84. and tested for flammability as required by the testing agency to retain the rating. UL 723 test method may be used in lieu When specified (see 6.2), e
43、ach type IV laminate shall be identified 4.5 Insaection of aackaging. Sample packages and packs, and the inspection of the preservation, packing, and marking for shipment, stowage, and storage shall be in accordance with the requirements of section 5 and the documents specified therein. 5. PACKAGING
44、 (The packaging requirements specified herein apply only for direct Government acquisition.) 5.1 Presswatiofi. Preservation skiall be level A or commercial, as specified (see 6.2). 7 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,- MIL-P-17171E 93 W
45、9999906 0433756 O 5.1.1 Level A. Laminated sheets (see 3.2) shall be individually wrapped or interleaved to protect them from abrasion using not less than 30 pounds basic. weight kraft paper or plastic film. 5.1.2 Commercial. Preservation shall be in accordance with ASTM D 3951. 5.2 Packing. Packing
46、 shall be level A, B, C, or commercial, as specified (see 6.2). 5.2.1 General reauirements for levels A. B. and C. Shipping containers shall contain identical quantities of identical sheets and shall be of minimum weight and of uniform size, Shipping containers shall be provided with Eiber- board pa
47、ds, liners, or other media to provide protection to all corners and edges of the packed sheets from damage during handling, shipment, storage, and stowage. 5.2.1.1 Naw fire-retardant treated lumber and Dlvwood. Unless otherwise specffied (see 6.2), all lumber and plywood (including laminated veneer
48、material used in shipping containers and pallet construction) shall be fire-retardant treated material conforming to MIL-L-19140 as follows: Levels A and B - Type II - weather resistant. Level C - Type I - non-weather resistant. Category 1 - general use. Category 1 - general use. 5.2.2 Levels A. B.
49、and C containers. Sheets preserved as specified in 5.1 shall be packed in shipping containers for the level of packing specified (see 5.2) in accordance with table VII, appendix C of MIL-STD-2073-1. Unless otherwise specified (see 6.2), container selection shall be at the contractors option. 5.2.2.1 Caseliners. closure. and eross weight. 5.2.2.1.1 Caseliners. Unless otherwise specified (see 6.2), level A shipping coneainers shal