1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 12 20 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 FABRIC, INFLUENCE PATTERN, WARP KNIT WSS-M1H1106-A 1. SCOPE The material defined by this specification is a INFLUENCE
2、PATTERN, 3 bars, 56 Gauge, Single Needle bar, body cloth of good quality and uniform composition. The base fabric is embossed to create the pattern. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for 2008 D219 seat insert. 3. REQUIREMENTS In ad
3、dition, to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3
4、.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Wales 146 wales/10 cm Courses 181 courses/10 cm 3.2.2 Fabric Weight, +/- 5%, g/m2(FLTM BN 106-01) Face w/no Backcoat 344 Laminated to 3 mm foam 463 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric
5、100% Polyester Backcoat No backcoat ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1106-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Face 11.1 tex f34 (textured yarn) Middle 11.1 tex f34 (textured yarn) Back 7.77 tex f36 (wd yarn) 3.5 METHOD OF DYEING Piece Dye 3.6 FINISHING OPERATIONS Knit, Heat set, Setmake, Dye, Dry, Emboss, Inspect