1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 09 21 Revised Inserted 3.0; Deleted 3.1, 3.11, 4 1978 11 10 Metricated & Retyped CAH1-RD572066-175 1963 10 31 Released AS1 #1135 Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 1 of 2 TAPE, POLYURETHANE
2、FOAM - DOUBLE COATED ESB-M3G55-A 1. SCOPE The material defined by this specification is a pressure sensitive polyurethane foam tape coated on both sides, protected with release paper. 2. APPLICATION This specification was released originally for material used to retain emblems and/or moldings in the
3、 recessed areas in the console glove box door. Metal bonded parts are chrome plated CR steel (Falcon) and chrome plated zinc die castings (Comet). 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requiremen
4、ts For Production Materials (WSS-M99P1111-A). 3.2 TENSILE STRENGTH, min 100 psi (689 kPa) (ASTM D 1564, Die “A“) Elongation, min 50% 3.3 HARDNESS, Durometer “00“, min 65 (ASTM D 2240) 3.4 TEAR RESISTANCE, min 14 lb/in (2.5 kN/m) (ASTM D 624, Die “C“) 3.5 ADHESION Adhesion shall exceed the minimum va
5、lues specified below. Foam splitting is acceptable when the force to initiate the splitting exceeds the minimum adhesion requirement. If adhesion exceeds the length of the tape, the exposed side may be reinforced with flexible tape with sufficient strength to induce an adhesive or a cohesive failure
6、. 3.5.1 Adhesion to Steel 50 oz/in (547 N/m) (ASTM D 1000) 3.5.2 Adhesion to Painted Metal 50 oz/in (547 N/m) (ASTM D 1000: Test panels are prepared per FLTM BI 103-02, using ESB-M50J100). ENGINEERING MATERIAL SPECIFICATIONESB-M3G55-APrinted copies are uncontrolled Copyright 2005, Ford Global Techno
7、logies, LLC Page 2 of 2 3.5.3 Aged Adhesion (Painted Metal) Failure shall be cohesive or tensile (not adhesive). The forces to initiate failure shall not be less than the values obtained in 3.5.2. Test Method: Prepare bonded samples as described in ASTM D 1000 using test panels prepared per FLTM BI
8、103-02 with ESB-M50J100 enamel. Expose the samples at 70 +/- 1 C for 72 h. Permit samples to cool at 23 +/- 2 C for 2 h minimum prior to test. 3.6 LOW TEMPERATURE FLEXIBILITY Shall not crack nor show any evidence of failure. Test Method: Samples approximately 6 in (150 mm) in length shall be conditi
9、oned for 16 h at -29 C and shall then be bent 180 around a 1.0 in (25 mm) diameter temperature conditioned mandrel. 3.7 MIGRATION STAIN None Test Method: The material shall be placed in intimate contact with a freshly painted light colored (white or blue) enameled panel and also light colored vinyl
10、trim material, ESB-M2F76, and subjected to 200 h in the Westinghouse fluorescent sunlight cabinet described in FLTM BO 115-01. 3.8 RESISTANCE TO HUMIDITY DETERIORATION No evidence of foam breakdown in the form of cracking or crumbling. Test Method: Samples approximately 6 in (150 mm) in length shall
11、 be subjected to humidity aging outlined under FLTM BO 012-01 and subsequently bent 180 around a 1/4 in (6.4 mm) diameter mandrel. 3.9 ODOR No offensive odor in the “as received“ condition or after the deterioration test in para 3.10. 3.10 CELL STRUCTURE Homogeneous, medium sized cell structure with no large voids or hard spots.