1、BS EN ISO26985:2012ICS 97.150NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBRITISHSTANDARDResilientfloorcoveringsIdentificationoflinoleumanddeterminationofcementcontentandashresidueCopyright European Committee for Standardization Provided by IHS under license with CENNot for
2、ResaleNo reproduction or networking permitted without license from IHS-,-,-National forewordThis British Standard is the UK implementation of EN ISO 26985:2012. It is identical to ISO 26985:2008. It supersedes BS ISO 26985:2008 and BS EN 670:1998, which are withdrawn.The UK participation in its prep
3、aration was entrusted to Technical Committee PRI/60, Resilient floor coverings.A list of organizations represented on this committee can be obtained on request to its secretary.This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its corr
4、ect application.Compliance with a British Standard cannot confer immunity from legal obligations.BS EN ISO 26985:2012This British Standardwas published under theauthority of the StandardsPolicy and StrategyCommittee on 31 May2009. The British Standards Institution 2012. Published by BSI Standards Li
5、mited 2012.Amendments/corrigenda issued since publicationDate Comments 30 April 2012 This corrigendum renumbers BS ISO 26985:2008 as BS EN ISO 26985:2012ISBN 978 0 580 75246 9Copyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or netwo
6、rking permitted without license from IHS-,-,-EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN ISO 26985 February 2012 ICS 97.150 Supersedes EN 670:1997English Version Resilient floor coverings - Identification of linoleum and determination of cement content and ash residue (ISO 26985:2008) Revte
7、ments de sol rsilients - Identification du linolum et dtermination de la teneur en ciment et du taux de cendres (ISO 26985:2008) Elastische Bodenbelge - Erkennung von Linoleum und Bestimmung des Gehaltes an Bindemittel und anorganischen Fllstoffen (ISO 26985:2008) This European Standard was approved
8、 by CEN on 31 December 2011. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national s
9、tandards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language an
10、d notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Li
11、thuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brus
12、sels 2012 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN ISO 26985:2012: ECopyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license
13、 from IHS-,-,-Foreword The text of ISO 26985:2008 has been prepared by Technical Committee ISO/TC 219 “Floor coverings” of the International Organization for Standardization (ISO) and has been taken over as EN ISO 26985:2012 by Technical Committee CEN/TC 134 “Resilient, textile and laminate floor co
14、verings” the secretariat of which is held by BSI. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by August 2012, and conflicting national standards shall be withdrawn at the latest by August 2012. A
15、ttention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 670:1997. According to the CEN/CENELEC Internal Regulations
16、, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Ne
17、therlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. Endorsement notice The text of ISO 26985:2008 has been approved by CEN as a EN ISO 26985:2012 without any modification. BS EN ISO 26985:2012 EN ISO 26985:2012 (E)Copyright Eur
18、opean Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-INTERNATIONAL STANDARD1Resilient floor coverings Identification of linoleum and determination of cement content and ash residue1ScopeThisIntern
19、ationalStandard s pecifies methods for identifying linoleumand determining the cement content andash residue of linoleum floor coverings.2Terms and definitionsFor the purposes of this document, the following terms and definitions apply.2.1ash residueresidue that remains following incineration at for
20、2.2linoleum cementbinder in linoleum, consisting of a mixture of linseed oil and/or vegetable drying oils, rosin and drying oilcatalysts, which is converted to a semi-elastic mass b yan oxidative curing process3Principles3.1 IdentificationA small specimen issaponified in a solution of potassium hydr
21、oxide inmethanol to identify linoleum from otherfloor coverings.3.2 Composition3.2.1 Cement contentA specimen without the backing material is crumbled and mixed with a mixture of potassium hydroxide inmethanol. After intensive stirring at to , the mixture is filtered and carefully dried. The differe
22、ncebetween the initial mass and the massof the residue is the defined mass of linoleum cement.3.2.2 Ash residueTo determine the amount of ash residue, a specimen without the backing material is incinerated and the massof the residual ash is measured.500 C3h20 C25 CEN ISO 26985:2012 (E)BS EN ISO 2698
23、5:2012 ISO 2012Copyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-24Apparatus andmaterials4.1Apparatus4.1.1 Grater.4.1.2 Tared beakers .4.1.3 Porcelain crucibles.4.1.4 Desiccator (v
24、acuum type), containing a suitable desiccant, e.g. silica gel.4.1.5 Furnace, capable of being controlled at .4.1.6 Balance, having an accuracy of.4.1.7 Laboratory sieve, with a nominal aperture size of .4.1.8 Ultrasonic bath , or equivalent device.4.1.9 Centrifuge or vacuum filter (type A2) andsucti
25、on device, e.g. a water-jet pump.4.1.10 Bunsen burner .4.2Materials4.2.1 Methanol (methyl alcohol), analyticalgrade.4.2.2 Potassium hydroxide (analytical grade)in methanol solution , with a concentration of .5Sampling and preparation of specimens5.1SamplingTake a representative sample from the avail
26、able material. Takefivespecimens, each with a minimum area of, from across the width of the sample, or from individual tiles, the distance between the edge of thesample and the nearest edge of the specimen being at least .Cut a square of approximately from a specimen.5.2Determination of cement conte
27、ntRemove the backing material and grate the specimen. Use that part which passes through a sieve.5.3Determination of ash residueRemove the backing material and cut the specimen into small pieces of approximately .6Atmosphere for conditioning and testingCondition the specimen, at a temperature of and
28、 a relativehumidity of , fora minimum of. Maintain these conditions during the test.500 C 10 C0,1mg0,5mm0,5mol/l50cm2100mm20mm 20mm0,5mm5mm 5mm23 2 C50 5%24hBS EN ISO 26985:2012 EN ISO 26985:2012 (E) ISO 2012Copyright European Committee for Standardization Provided by IHS under license with CENNot f
29、or ResaleNo reproduction or networking permitted without license from IHS-,-,-37Test procedure7.1 IdentificationSaponify the specimen in excess potassium hydroxide/methanol solution without stirring. After , recordwhether complete disintegration of the linoleum has taken place. If disintegration has
30、 not taken place, thesample is not identified as linoleum, so do not carry out the tests described in 7.2 and 7.3.7.2 Determination of cement contentWeigh approximately of the grated specimen, with particle size , in a tared beaker.Add approximately ofthe potassium hydroxide/methanol solutionand sti
31、r for . Ensure thatthe temperature does not exceed , because wood- and/or cork-flour can be affected.Weigh the typeA2 filter (if used) and record the mass to the nearest .Centrifuge or vacuum filter the mixture using the typeA2 filter and rinse the residue at a temperature of .Condition thedryresidu
32、e in the filter or centrifuge, asdescribedin Clause6,for a minim um of , andrecordthe mass (including the A2 filter, if used)to the nearest .7.3 Determination of ash residueDetermine the tared mass of aporcelain crucible as follows. Prepare acruciblebyheating in the furnace atfor at least . Allow co
33、oling in the desiccator for at least and weigh the crucible. Repeat theprocessof heating,cooling and weighing untilthe resultsoftwo consecutive weighings donot differ from eachotherbymore than , i.e. the mass isvirtually constant.Weigh approximately of the crumbled specimen in the tared porcelain cr
34、ucible. Heat the crucible using aBunsen burner, in a way that allows the specimen to burn in a controlled manner. Place the crucible andcontents in a furnace at , forat least , to allow incineration to proceed to completion, i.e. whenno carbonaceous matterremains in the crucible.Transfer thecrucible
35、and contents to the desiccatorand allow tocool fo r at least . Determinethe mass of thecrucible and residue to the nearest . Repeat the process of incineration, cooling and weighting until theresults of two consecutive weightings do not differ from eachother bymore than ,i.e. the mass is virtuallyco
36、nstant.8Calculation and expression ofresults8.1 IdentificationRecord whether complete disintegration takes place.24h1g null 0,5mm10ml 10 0,5min25 C0,01g40 C24h0,01g500 C3h1h0,5mg2g500 10 C3h1h0,01g0,5mgBS EN ISO 26985:2012 EN ISO 26985:2012 (E) ISO 2012Copyright European Committee for Standardizatio
37、n Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-48.2Determination of cement contentCalculate the linoleum cement content, as a percentage by mass, using the following fomula:whereis the initial mass of the specimen;is the mas
38、s of the dry residue (excluding the A2 filter if used).Express the linoleum cement content as the average of the results for the number of specimens tested, andrecord these to the nearest .8.3Determination of ash residueCalculate the ash residue, as a percentage bymass, using the following fomula:wh
39、ereis the initial mass of the specimen;is the mass of the ash residue.Expressthe inorganic filler content as theaverage of the results for the number of specimenstested, andrecordthese to the nearest .9Precision statementA round-robin test will be conducted to determine the precision of this test me
40、thod.10 Test reportThe test report shall contain the following information:a) a statement that the tests were performed in accordance withthis International Standard (ISO26985:2008);b) a complete identification of the product tested, including type, source, colour, and manufacturers referencenumbers
41、;c) previous history of the sample;d) a statement as to whether the sample has been identified as linoleum;e) the average cement content and the average ash residue, as a percentage, if relevant;f) any deviation from this International Standard which could have affected the results;g) the date of th
42、e test.m 1 m 2m 1 100m 1m 20,5%m 3m 1 100m 1m 30,5%BS EN ISO 26985:2012 EN ISO 26985:2012 (E) ISO 2012Copyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-5Bibliography1EN670, Resilie
43、nt floor coverings Identification of linoleum and determ ination of cement content andash residueBS EN ISO 26985:2012 EN ISO 26985:2012 (E) ISO 2012Copyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without lic
44、ense from IHS-,-,-ICS97.150Price based on 5 pagesBS EN ISO 26985:2012 EN ISO 26985:2012 (E) ISO 2012Copyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-This page has been intentional
45、ly left blankBS EN ISO 26985:2012 EN ISO 26985:2012 (E)Copyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-BSI is the independent national body responsible for preparing British Stan
46、dards and other standards-related publications, information and services. It presents the UK view on standards in Europe and at the international level. BSI is incorporated by Royal Charter . British Standards and other standardizationproducts are published by BSI Standards Limited.British Standards
47、 Institution (BSI)raising standards worldwideBSI389 Chiswick High Road London W4 4AL UKTel +44 (0)20 8996 9001Fax +44 (0)20 8996 Standards and PASs are periodically updated by amendment or revision. Users of British Standards and PASs should make sure that they possess the latest amendments or edit
48、ions.It is the constant aim of BSI to improve the quality of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using British Standards would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside frontcover. Similary for PASs, please notify BSI Customer Services.Tel: +44 (0)20 8996 9001 Fax: +44 (0)20 8996 7001BSI offers BSI Subscribing Members an individual updating se