1、Designation: D5636/D5636M 94 (Reapproved 2011)1Standard Test Method forLow Temperature Unrolling of Felt or Sheet Roofing andWaterproofing Materials1This standard is issued under the fixed designation D5636/D5636M; the number immediately following the designation indicates theyear of original adopti
2、on or, in the case of revision, the year of last revision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.1NOTEUnits information was editorially revised in February 2011.1. Scope1.1 This test
3、method covers the procedure for the physicaltesting and analysis of surface cracking due to low temperatureunrolling of roofing composed of bituminous impregnated feltsand reinforced polymer modified bituminous sheet materials.These products may employ various surfacing materials on oneside.1.2 The
4、values stated in either SI units or inch-pound unitsare to be regarded separately as standard. The values stated ineach system may not be exact equivalents; therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result in non-conformancewith the stan
5、dard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referen
6、ced Documents2.1 ASTM Standards:2D1079 Terminology Relating to Roofing and Waterproofing3. Terminology3.1 DefinitionsFor definitions of terms used in this testmethod, see Terminology D1079.4. Summary of Test Method4.1 The felt or sheet roofing or waterproofing material roll istemperature conditioned
7、. Specimens are then taken from theroll, wrapped around a mandrel, temperature conditioned,unrolled, and inspected for cracking.5. Significance and Use5.1 Since felts or sheet roofing or waterproofing materialsare brought to the roof in a roll and unrolled, this test methodsimulates felt or membrane
8、 behavior under actual field condi-tions during the unrolling process.5.2 This test method is designed to aid those interested inthe physical properties of roofing and waterproofing felts andsheet materials.5.3 This test method enables a researcher to measure therelative behavior of low temperature
9、unrolling of roofing andwaterproofing felt or sheet materials under laboratory condi-tions.5.4 The data obtained from this test method will not permitservice life prediction or the ability of the material to beinstalled at the tested temperature. Unrolling capabilities areimportant during applicatio
10、n, and the temperature at the time ofunrolling is believed to affect the performance of roofing andwaterproofing membranes. However, the actual link betweenthe test data and performance is unknown and is dependent onthe materials and exposure.6. Apparatus6.1 The mandrel for the test procedure is a 6
11、80 mm 3.125in. outer diameter (Schedule 30) PVC pipe, a minimum 6250mm 10.0 in. in length.7. Test Method7.1 Unrolling at Low TemperaturesThis test method de-termines the temperature at which no cracking is observed inthe felt or sheet roofing or waterproofing materials afterunrolling at the test tem
12、perature from a 680 mm 3.125 in.diameter mandrel.7.2 Sampling:7.2.1 The specimens are to be taken from a roll of roofing orwaterproofing materials conditioned at 23 6 3C73.6 6 3.4F and 50 6 5 % relative humidity for 24 h. No1This test method is under the jurisdiction ofASTM Committee D08 on Roofinga
13、nd Waterproofing and is the direct responsibility of Subcommittee D08.20 onRoofing Membrane Systems.Current edition approved Jan. 1, 2011. Published February 2011. Originallyapproved in 1994. Last previous edition approved in 2005 as D5636 94 (2005).DOI: 10.1520/D5636_D5636M94R11E01.2For referenced
14、ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Consh
15、ohocken, PA 19428-2959, United States.specimens are to be taken closer than 61.22 m 4 ft. from theleading edge or closer than 6150 mm 6 in. from the side ofthe roll.7.2.2 Cut four specimens from the roll in the longitudinaldirection. The specimens shall be 6250 mm (63 mm) 10 in.6 18 in. wide by 6450
16、 mm (63 mm) 18 in. 618 in. long.8. Procedure8.1 Secure the specimen to the mandrel, weather sideagainst mandrel, with polyethylene tape. Wrap the temperatureconditioned specimen evenly and firmly around the mandrel.Secure the specimen to the mandrel, wrapping sufficiently withclear plastic wrap, and
17、 maintain the specimen on the mandrelat 23 6 3C 73 6 3.4F and 50 6 5 % relative humidity for24 h.8.2 Place the specimen assembly in a refrigeration unit at atemperature where the felt or sheet is presumed to be capableof passing. If this information is not available, make apreliminary screening test
18、 at 0 6 1C 32 6 2F. Maintain thetemperature in the refrigeration unit at desired temperature0.5C 61F for a minimum of 2 h. Change the temperatureintervals in preceding tests at 62C 64F. Allow therefrigerated unit and mandrel to equilibrate before proceedingwith subsequent testing.8.3 Remove the spec
19、imen assembly from the refrigerationunit. Remove the plastic wrap. Carefully and evenly clamp theexposed end of the specimen to a clip board. Unroll thespecimen onto a horizontal surface, keeping the material flatagainst the surface. Time allowance for removal from refrig-erated unit to unrolling is
20、 30 s, and time allowance of unrollingis between 4 and 6 s. Inspect for signs of cracking. Record thelocation and length of any cracks. Consider any visible surfaceruptures as a failure.8.4 Repeat the procedure until the lowest temperature atwhich none of the specimens show cracking is achieved.Allo
21、wthe refrigeration unit to equilibrate before testing subsequentspecimens at different temperatures.9. Report9.1 Report complete specimen identification and the lowesttemperature where cracking is not evident to the unaided eye.Tested specimens may not be reused for successive testing atlower or hig
22、her temperatures. For the purposes of this testmethod, any surface crack is considered a failure at the testedtemperature where the crack appears.10. Precision and Bias10.1 No statement is made about either the precision or biasof Test Method D5636 for measuring low temperature unroll-ing since the
23、result merely states whether there is conformanceto the criteria for success specified in the procedure.11. Keywords11.1 cracking; felt; low temperature; sheet roofing; unroll-ing; waterproofingASTM International takes no position respecting the validity of any patent rights asserted in connection w
24、ith any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible tec
25、hnical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful considera
26、tion at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr H
27、arbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).D5636/D5636M 94 (2011)12