1、Designation: B 709 04 (Reapproved 2009)Standard Specification forIron-Nickel-Chromium-Molybdenum Alloy (UNS N08028)*Plate, Sheet, and Strip1This standard is issued under the fixed designation B 709; the number immediately following the designation indicates the year oforiginal adoption or, in the ca
2、se of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers iron-nickel-chromium-molybdenum alloy (UNS N08028)* plate, sheet
3、, and strip inthe solution-annealed condition.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.3 This standard does not purport to a
4、ddress all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas provided by the manufacturer, to estab
5、lish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2B 880 Specification for General Requirements for ChemicalCheck Analysis Limits for Nickel, Nickel Alloys andCobalt AlloysB 906 Specification f
6、or General Requirements for Flat-Rolled Nickel and Nickel Alloys Plate, Sheet, and StripE 8/E 8M Test Methods for Tension Testing of MetallicMaterials3. Ordering Information3.1 It is the responsibility of the purchaser to specify allrequirements that are necessary for material ordered under thisspec
7、ification. Examples of such requirements include, but arenot limited to those specified in Ordering Information Sectionin Specification B 906.4. General Requirements4.1 Material furnished under this specification shall con-form to the applicable requirements of the current edition ofSpecification B
8、906, unless otherwise specified herein.5. Materials and Manufacture5.1 Heat TreatmentThe final heat treatment shall be asolution-anneal. Minor cold working such as flattening ortemper rolling may be performed after the final solutionannealing treatment.NOTE 1This recommended solution-anneal consists
9、 of heating to aminimum temperature of 1975F (1080C) and cooling rapidly to roomtemperature.6. Chemical Composition6.1 The material sampled in accordance with 10.2 shallconform to the composition limits prescribed in Table 1.6.2 If a product analysis is subsequently made, the materialshall conform t
10、o the composition limits with the productanalysis variation prescribed Specification B 880.7. Mechanical Properties7.1 The material shall conform to the requirements as to themechanical property prescribed in Table 2.8. Dimensions and Permissible Variations8.1 SheetMaterial furnished under this spec
11、ification shallconform to the applicable requirements of the current edition ofSpecification B 906, except as specified in Table 3 and Table 4.1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on
12、Refined Nickel and Cobalt and Their Alloys.Current edition approved April 15, 2009. Published April 2009. Originallyapproved in 1982. Last previous edition approved in 2004 as B 709 98 (2004).2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at ser
13、viceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.TABLE 1 Chemical RequirementsElement Composition, %Ni 29.5 to 32.5Fe remainderACr 26.0 to 28.0Mo 3.0 to 4.0C, max 0.030Si, max 1.00Mn, max 2.50P, max 0.030S, max 0.030Cu
14、 0.6 to 1.4ADetermined arithmetically by difference.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.8.2 Cold-Rolled StripMaterial furnished under this speci-fication shall conform to the applicable requirements of thecurrent edition
15、of Specification B 906, except as specified inTables 5-7.8.3 PlateMaterial furnished under this specification shallconform to the applicable requirements of the current edition ofSpecification B 906.9. Sampling9.1 Sampling for Chemical Analysis, Mechanical Testing,and Corrosion Testing shall be perf
16、ormed in accordance withSpecification B 906, except as specified herein:9.1.1 PlateA lot of plate for testing and inspection pur-poses shall consist of the products resulting from the rolling ofone heat of material in the same condition and specifiedthickness, solution annealed by the same practice,
17、 but in nocase more than 25 000 lb (11 340 kg).9.1.2 Sheet and StripA lot of sheet or strip for testing andinspection purposes shall consist of material from one heat inthe same form (sheet or strip), condition, finish, and specifiedthickness, solution-annealed by the same practice but in nocase mor
18、e than 25 000 lb (11 340 kg).9.2 Sampling for Mechanical Tests:9.2.1 When samples are to be taken after delivery, thepurchaser of material ordered to cut lengths may request on thepurchase order additional material of adequate size to providesample coupons for inspection purposes.10. Number of Tests
19、 and Retests10.1 In the case of sheet or strip supplied in coil form, twoor more tension tests (one from each end of each coil), and oneor more hardness tests shall be made on specimens taken fromeach end of the coil. When material is supplied in flatsheet, flatstrip, or plate, one tension and one o
20、r more hardness tests shallbe made on each 100 or less sheets, strips, or plates of the samelot. When specified, one corrosion test shall be conducted foreach lot.10.2 If any specimens selected to represent any lot fail tomeet any of the test requirements, the material represented bysuch specimens m
21、ay be retested. If there is valid reason tobelieve the result is not representative, the material may bere-reannealed and retested.11. Specimen Preparation11.1 Tension test specimens from material under12 in. (12.7mm) in thickness shall be of the full thickness of the materialand machined to the for
22、m and dimensions shown for thesheet-type specimen in Test Methods E 8/E 8M. Tension testspecimens from material12 in. (12.7 mm) and over shall be ofthe full thickness of the material, machined to the form andTABLE 2 Mechanical Property RequirementsFormTensileStrength,min, ksi(MPa)YieldStrength(0.2 %
23、 off-set), min,ksi (MPa)Elonga-tionin2in.or50mm, or4D, min,%RockwellHardness (orequivalent)ASheet 73 (500) 31 (214) 40 7090 HRBStrip 73 (500) 31 (214) 40 7090 HRBPlate 73 (500) 31 (214) 40 7090 HRBAHardness values are shown for information only and shall not constitute a basis for acceptance or reje
24、ction as long as the other mechanical properties are met.TABLE 3 Flatness Tolerances for Hot-Rolled and Cold-Rolled SheetsSheets not Specified to Stretcher Leveled Standard of FlatnessSpecified Thickness, in. (mm) Width, in. (mm)Flatness Tolerance (maxDeviation from a Horizon-tal Flat Surface), in.
25、(mm)0.062 (1.57) and over to 60 (1524), inclover 60 to 72 (1524 to 1829), incl12 (12.7)34 (19.1)over 72 (1829) 1 (25.4)Under 0.062 (1.57) to 36 (914), inclover 36 to 60 (914 to 1524), incl12 (12.7)34 (19.1)over 60 (1524) 1 (25.4)TABLE 4 Weight Tolerances for Hot-Rolled and Cold-Rolled SheetsIt is no
26、t practicable to produce hot-rolled and cold-rolled sheets to exact theoretical weight. Sheets of any one item of a specified thicknessand size in any finish may be overweight to the following extent:(1) An item of five sheets or less, or an item estimated to weigh 200 lb (90.7 kg) or less, may actu
27、ally weigh as much as 10 % over thetheoretical weight.(2) An item of more than five sheets and estimated to weigh more than 200 lb (90.7 kg) may actually weigh as much as 712 % over thetheoretical weight.(3) The underweight variations for sheets are limited by the under thickness tolerances shown in
28、 Table 3 of Specification B 906.For determining theoretical weight, the factor 42 lb/ft2in. (0.0008 kg/cm2mm) thickness may be used.B 709 04 (2009)2dimensions shown for the plate-type specimen in Test MethodsE 8/E 8M. Tension test specimens shall be taken from materialafter final heat treatment and
29、shall be selected in the transversedirection unless prohibited by width.12. Keywords12.1 N08028; plate; sheet; stripTABLE 5 Thickness ToleranceA,B,Cfor Cold-Rolled Strip for the Thicknesses and Widths Given, Over and UnderSpecified ThicknessWidth, in.0.187 to 1,inclOver 1 to3, inclOver 3 to6, inclOv
30、er 6 to9, inclOver 9 to12, inclOver 12 to16, inclOver 16 to20, inclOver 20 to24, inclThickness Tolerance, in.Over 0.160 to less than 0.002 0.003 0.004 0.004 0.004 0.005 0.006 0.0060.187Over 0.099 to 0.160, incl 0.002 0.002 0.003 0.003 0.004 0.004 0.005 0.005Over 0.068 to 0.099, incl 0.002 0.002 0.00
31、3 0.003 0.003 0.004 0.004 0.004Over 0.049 to 0.068, incl 0.002 0.002 0.003 0.003 0.003 0.003 0.004 0.004Over 0.039 to 0.049, incl 0.002 0.002 0.0025 0.003 0.003 0.003 0.004 0.004Over 0.034 to 0.039, incl 0.002 0.002 0.0025 0.0025 0.003 0.003 0.003 0.003Over 0.028 to 0.034, incl 0.0015 0.0015 0.002 0
32、.002 0.0025 0.0025 0.003 0.003Over 0.025 to 0.028, incl 0.001 0.0015 0.0015 0.002 0.002 0.002 0.0025 0.003Over 0.019 to 0.025, incl 0.001 0.001 0.0015 0.0015 0.002 0.002 0.0025 0.0025Over 0.016 to 0.019, incl 0.001 0.001 0.001 0.0015 0.0015 0.002 0.002 0.002Over 0.012 to 0.016, incl 0.001 0.001 0.00
33、1 0.001 0.0015 0.0015 0.002 0.002Over 0.011 to 0.012, incl 0.001 0.001 0.001 0.001 0.0015 0.0015 0.0015 0.0015Over 0.010 to 0.011, incl 0.001 0.001 0.001 0.001 0.001 0.0015 0.0015 0.00150.010 0.001 0.001 0.001 0.001 0.001 0.001 0.0015 0.0015Specified Thickness, mmWidth, mm4.76 to25.4, inclOver25.4to
34、 76.2,inclOver 76.2to 152.4,inclOver152.4 to228.6,inclOver228.6 to304.8, inclOver304.8 to406.4,inclOver406.4 to508, inclOver 508to 609.6,inclThickness Tolerance, mmOver 4.06 to less than 0.05 0.08 0.10 0.10 0.10 0.13 0.15 0.154.76Over 2.51 to 4.06, incl 0.05 0.05 0.08 0.08 0.10 0.10 0.13 0.13Over 1.
35、73 to 2.51, incl 0.05 0.05 0.08 0.08 0.08 0.10 0.10 0.10Over 1.25 to 1.73, incl 0.05 0.05 0.08 0.08 0.08 0.08 0.10 0.10Over 0.99 to 1.24, incl 0.05 0.05 0.06 0.08 0.08 0.08 0.10 0.10Over 0.86 to 0.99, incl 0.05 0.05 0.06 0.06 0.08 0.08 0.08 0.08Over 0.71 to 0.86, incl 0.04 0.04 0.05 0.05 0.06 0.06 0
36、.08 0.08Over 0.64 to 0.71, incl 0.02 0.04 0.04 0.05 0.05 0.05 0.06 0.08Over 0.48 to 0.64, incl 0.02 0.02 0.04 0.04 0.05 0.05 0.06 0.06Over 0.41 to 0.48, incl 0.02 0.02 0.02 0.04 0.04 0.05 0.05 0.05Over 0.38 to 0.41, incl 0.02 0.02 0.02 0.02 0.04 0.04 0.05 0.05Over 0.28 to 0.30, incl 0.02 0.02 0.02 0
37、.02 0.04 0.04 0.04 0.04Over 0.25 to 0.28, incl 0.02 0.02 0.02 0.02 0.02 0.04 0.04 0.040.25 0.02 0.02 0.02 0.02 0.02 0.02 0.04 0.04AFor thickness under 0.010 to 0.005 in. (0.254 to 0.127 mm), inclusive, in widths up to and including 16 in. (406 mm), a tolerance of 610 % of the thickness applies.For t
38、hicknesses under 0.010 to 0.005 in. (0.254 to 0.127 mm), inclusive, in widths over 16 to 24 in. (406 to 610 mm), exclusive, a tolerance of 615 % of the thicknessapplies. For thickness tolerances on thicknesses under 0.005 in. (0.127 mm) in widths up to 24 in. (610 mm), exclusive, the producer should
39、 be consulted.BThickness measurements are taken38 in. (9.5 mm) in from the edge of the strip, except that on widths less than 1 in. (25.4 mm) the tolerances are applicable formeasurements at all locations.CThe tolerances in this table do not include crown tolerances.TABLE 6 Crown Tolerances for Cold
40、-Rolled StripSpecified Thickness, in. (mm)Additional Thickness, at Middle of Strip over That Shown in Table 5 forEdge Measurement, for Widths and Thicknesses Given, in. (mm)Width, in. (mm)To 5 (127), inclOver 5 to 12 (127 to305), inclOver 12 to 24 (305 to610), excl0.005 to 0.010 (0.127 to 0.254), in
41、cl 0.0075 (0.19) 0.001 (0.02) 0.0015 (0.04)Over 0.010 to 0.025 (0.254 to 0.635), incl 0.001 (0.02) 0.0015 (0.04) 0.002 (0.05)Over 0.025 to 0.065 (0.635 to 1.65), incl 0.0015 (0.04) 0.002 (0.05) 0.0025 (0.06)Over 0.065 to 0.187 (1.65 to 4.76), excl 0.002 (0.05) 0.0025 (0.06) 0.003 (0.08)TABLE 7 Lengt
42、h and Camber Tolerances for Cold-Rolled StripLength TolerancesSpecified Length, ft (mm)Tolerance Over Speci-fied Length (No UnderTolerance), in. (mm)To 5 (1524), incl38 (9.5)Over 5 to 10 (1520 to 3050), incl12 (12.7)Over 10 to 20 (3050 to 6100), incl58 (15.9)B 709 04 (2009)3ASTM International takes
43、no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own respo
44、nsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed
45、 to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the a
46、ddress shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).B 709 04 (2009)4