1、Designation: B570 06 (Reapproved 2010)Standard Specification forCopper-Beryllium Alloy (UNS Nos. C17000 and C17200)Forgings and Extrusions1This standard is issued under the fixed designation B570; the number immediately following the designation indicates the year oforiginal adoption or, in the case
2、 of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification establishes the requirements forcopper-beryllium alloy forgings and extr
3、usions produced fromthe following alloys.Copper Alloy UNS No.Nominal % CompositionBerylliumC17000C172001.71.9NOTE 1Requirements for copper-beryllium alloy rod and bar appearin Specification B196/B196M (Section 2).1.2 Unless otherwise specified, Copper Alloy UNS No.C17200 shall be the alloy furnished
4、 whenever SpecificationB570 is specified without any alloy designation.1.3 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.4 The follow
5、ing hazard statement pertains only to the testmethod portions of the specification: This standard does notpurport to address all of the safety concerns, if any, associatedwith its use. It is the responsibility of the user of this standardto establish appropriate safety and health practices anddeterm
6、ine the applicability of regulatory limitations prior touse.2. Referenced Documents2.1 ASTM Standards:2B194 Specification for Copper-Beryllium Alloy Plate,Sheet, Strip, and Rolled BarB196/B196M Specification for Copper-Beryllium AlloyRod and BarB249/B249M Specification for General Requirements forWr
7、ought Copper and Copper-Alloy Rod, Bar, Shapes andForgingsB601 Classification for Temper Designations for Copperand Copper AlloysWrought and CastB846 Terminology for Copper and Copper AlloysE8 Test Methods for Tension Testing of Metallic MaterialsE18 Test Methods for Rockwell Hardness of Metallic Ma
8、-terialsE112 Test Methods for Determining Average Grain Size3. General Requirements3.1 The following sections of Specification B249/B249Mform a part of this specification.3.1.1 Terminology,3.1.2 Materials and Manufacture,3.1.3 Sampling,3.1.4 Number of Tests and Retests,3.1.5 Sample Preparation,3.1.6
9、 Test Methods,3.1.7 Significance of Numerical Limits,3.1.8 Inspection,3.1.9 Rejection and Rehearing,3.1.10 Certification,3.1.11 Mill Test Report,3.1.12 Packaging, Marking, Shipping and Preservation.3.2 In addition, when a section with a title identical to thatreferenced in 3.1, appears in this speci
10、fication, it containsadditional requirements that supplement those appearing inSpecification B249/B249M.4. Terminology4.1 Definitions:1This specification is under the jurisdiction ofASTM Committee B05 on Copperand Copper Alloys and is the direct responsibility of Subcommittee B05.02 on Rod,Bar, Wire
11、, Shapes and Forgings.Current edition approved Oct. 1, 2010. Published December 2010. Originallyapproved in 1972. Last previous edition approved in 2006 as B570 06. DOI:10.1520/B0570-06R10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at servic
12、eastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, Unite
13、d States.4.1.1 For definitions of terms related to copper and copperalloys, refer to Terminology B846.4.1.2 extrusion, na uniform metal shape, long in relationto its cross-sectional dimensions, produced by forcing a suit-ably preheated billet or preformed piece through an orifice(die) of the desired
14、 cross section.4.1.3 forging, na metal part worked to a predeterminedshape by one or more such processes as hammering, upsetting,pressing, rolling, and so forth.5. Ordering Information5.1 Include the following information in orders for prod-ucts:5.1.1 ASTM designation and year of issue,5.1.2 Quantit
15、y: number of pieces or pounds,5.1.3 Copper Alloy UNS No. (Section 1),5.1.4 Temper (Section 8) or condition (Section 12),5.1.5 Drawing showing the shape, dimensions, and toler-ances, if required,5.1.6 If an extrusion: the length (or mass) required, straight-ness as required,5.2 The following are opti
16、ons and should be included in thecontract or purchase order, when required:5.2.1 Tension tests (Section 11),5.2.2 Special tests such as grain size,5.2.3 Finish (see Section 15),5.2.4 Grain size (see Section 9), and5.2.5 When material is ordered for agencies of the U.S.government.6. Material and Manu
17、facture6.1 Material:6.1.1 The material of manufacture shall be cast or wroughtbillet of C17000 or C17200 of such purity and soundness as tobe suitable for processing into the products prescribed herein.6.1.2 The product heat number shall appear on the certifi-cation or test report.6.2 ManufactureThe
18、 product shall be manufactured byhot working and heat treating as may be necessary to meet theproperties specified herein.7. Chemical Composition7.1 The product composition shall conform to the chemicalrequirements shown in Table 1.7.2 These composition limits do not preclude the presenceof other el
19、ements. Limits may be established and analysisrequired for unnamed elements by agreement between themanufacturer and the purchaser.7.3 Copper, given as remainder, is the difference betweenthe sum of all elements analyzed and 100 %. When all theelements given in Table 1 are analyzed, the sum of the r
20、esultsshall be 99.5 % minimum.8. Temper8.1 The standard temper designations available under thisspecification and as prescribed in Classification B601 aresolution heat-treated TB00 (A) and precipitation heat-treatedTF00 (AT).9. Grain Size9.1 The grain size, if required, shall be as agreed uponbetwee
21、n the purchaser and the manufacturer and shall bedetermined in accordance with Test Methods E112.10. Physical Property Requirements10.1 Microstructure:10.1.1 The product in the TF00 (precipitation-hardened(AT) condition shall have a microstructure with a minimum ofsecond phase (beta) constituents. W
22、hen present, beta shall befine and well dispersed.11. Mechanical Property Requirements11.1 HardnessThe product furnished under this specifica-tion shall conform to the hardness requirements prescribed inTable 2 for the solution heat-treated condition and Table 3 afterprecipitation heat treatment, un
23、less tensile properties are re-quired by the purchase order. Rockwell hardness shall bedetermined in accordance with Test Method E18.11.2 TensileWhen specified in the contract or purchaseorder, the tensile properties of the product furnished shallconform to the properties in Table 2 or Table 3 depen
24、ding upontemper required. Tensile properties shall be determined inaccordance with Test Methods E8.12. Heat Treatment12.1 Solution Heat TreatmentTemper TB00 (A)Theproduct shall be heated to a uniform temperature, nominally1450F (788C) and quenched commensurate with the requiredproperty and structura
25、l integrity of the configuration.12.2 Precipitation Heat TreatmentTemper TF00 (AT)The product shall be heat treated to a uniform temperature inthe range from 600 to 700F (316 to 370C) for a minimum of2 to 3 h and then air cooled. This is the heat treatment for theacceptance tests shown in Table 3.12
26、.3 Special combinations of properties may be obtained byspecial precipitation heat treatments. The requirements forthese special heat treatments shall be agreed upon by themanufacturer or supplier and purchaser.13. Purchases for the U.S. Government13.1 When specified in the contract or purchase orde
27、r,product purchased for agencies of the U.S. government shallconform to the special government regulations specified in theSupplementary Requirements section.TABLE 1 Chemical RequirementsComposition, %ElementCopper AlloyUNS No.C17000Copper AlloyUNS No.C17200Beryllium 1.601.85 1.802.00Additive elemen
28、ts:Nickel + cobalt, min 0.20 0.20Nickel + cobalt + iron, max 0.6 0.6Aluminum, max 0.20 0.20Silicon, max 0.20 0.20Copper remainder remainderB570 06 (2010)214. Dimensions and Permissible Variations14.1 The dimensions and tolerances for these product formsshall be those shown on the drawing that forms
29、a part of eachorder or as agreed upon between the manufacturer and thepurchaser.15. Workmanship, Finish, and Appearance15.1 The product shall be free of defects; however, blem-ishes that do not interfere with the intended application areacceptable.15.2 The purchaser shall specify in the order the co
30、nditionor finish required, such as, hot-worked, hot-worked andcleaned by blasting, pickling, or machining.16. Test Methods16.1 Chemical Composition:16.2 The chemical composition shall, in case of disagree-ment, be determined in accordance with the applicable methodin the Annex of Specification B194.
31、16.3 Test method(s) for the determination of element(s)required by contractual agreement shall be as agreed uponbetween the manufacturer and the purchaser.17. Keywords17.1 copper beryllium; extrusions; forgings; UNS C17000;UNS C17200SUPPLEMENTARY REQUIREMENTSThe following supplementary requirements
32、shall apply only when specified by the purchaser in theinquiry, contract, or order, for agencies of the U.S. government.S1. Referenced DocumentsS1.1 The following documents of the issue in effect on dateof material purchase form a part of this specification to theextent referenced herein:S1.1.1 ASTM
33、 Standard:B900 Practice for Packaging of Copper and Copper-AlloyMill-Products for U.S. Government AgenciesS1.1.2 Federal Standards:3Fed. Std. No. 102 Preservation, Packaging and PackingLevelsFed. Std. No. 123 Marking for Shipment (Civil Agencies)Fed. Std. No. 185 Identification Marking of Copper and
34、Copper-Base Alloy Mill ProductsS1.1.3 Military Standards:3MIL-STD-105 Sampling Procedures and Tables for Inspec-tion by AttributesMIL-STD-129 Marking for Shipment and StorageS2. Quality AssuranceS2.1 Responsibility for Inspection:S2.1.1 Unless otherwise specified in the contract or pur-chase order,
35、the manufacturer is responsible for the perfor-mance of all inspection and test requirements specified. Exceptas otherwise specified in the contract or purchase order, the3Available from Standardization Documents Order Desk, Bldg. 4 Section D, 700Robbins Ave., Philadelphia, PA 19111-5094, Attn: NPOD
36、S.TABLE 2 Mechanical Properties as Solution Heat TreatedTemper DesignationDiameter orThickness, in.(mm)Copper Alloy UNS No.C17000 C17200 C17000 C17200Standard Former Tensile Strength, ksi (MPa)A,B, max Rockwell Hardness, maxB ScaleTB00 solution heat-treated (A) all sizes 85 (590) 85 (590) 85 85Aksi
37、= 1000 psi.BSee Appendix X1.TABLE 3 Mechanical Properties After Precipitation Heat TreatmentTemper DesignationStandard Former In. mmCopper Alloy UNSNo.Tensile Strength,ksiA(MPa)B,CYield Strength, ksi(MPa), 0.2 % Offset,minElongation in43DD,min,%RockwellC ScaleTF00 precipitationhardened(AT)UNS C17000
38、 150190 (10301310) 120 (820) 3 32Up to 8, incl up to 200; 165200 (11401380) 130 (890) 3 36TF00 precipitationhardened(AT)Over 8 to 12, incl., over 200 to 300; UNS C17200 155190 (10701310) 130 (890) 3 34Over 12 over 300 145180 (10001240) 125 (860) 3 34Aksi = 1000 psi.BSee Appendix X1.CThe upper limits
39、 in the tensile strength column are for design guidance only.D43D=43Diameter.B570 06 (2010)3manufacturer may use his own or any other suitable facilitiesfor the performance of the inspection and test requirements,unless disapproved by the purchaser at the time the order isplaced. The purchaser shall
40、 have the right to perform any of theinspections or tests set forth, when such inspections and testsare deemed necessary to assure that the material conforms toprescribed requirements.S3. Identification MarkingS3.1 All material shall be properly marked for identificationin accordance with Fed. Std.
41、No. 185 except that the ASTMspecification number and the alloy number shall be used.S4. Preparation for DeliveryS4.1 Preservation, Packaging, Packing:S4.1.1 Military AgenciesThe material shall be separatedby size, composition, grade or class, and shall be preserved andpackaged, Level A or C, packed
42、Level A, B, or C as specifiedin the contract or purchase order, in accordance with therequirements of Practice B900.S4.1.2 Civil AgenciesThe requirements of Fed. Std. No.102 shall be referenced for definitions of the various levels ofpackaging protection.S4.2 Marking:S4.2.1 Military AgenciesIn addit
43、ion to any special mark-ing required by the contract or purchase order, marking forshipment shall be in accordance with MIL-STD-129.S4.2.2 Civil AgenciesIn addition to any special markingrequired by the contract or purchase order, marking forshipment shall be in accordance with Fed. Std. No. 123.APP
44、ENDIX(Nonmandatory Information)X1. METRIC EQUIVALENTSX1.1 The SI unit for strength properties now shown is inaccordance with the International System of Units (SI). Thederived SI unit for force is the newton (N), which is defined asthat force which when applied to a body having a mass of 1 kggives i
45、t an acceleration of 1 m/s2(N = kgm/s2). The derived SIunit for pressure or stress is the newton per square metre(N/m2), which has been named the pascal (Pa) by the GeneralConference on Weights and Measures. Since 1 ksi = 6 894 757Pa, the metric equivalents are expressed as megapascal (MPa),which is
46、 the same as MN/m2and N/mm2.SUMMARY OF CHANGESCommittee B05 has identified the location of selected changes to this standard since the last issue (B570 05a)that may impact the use of this standard. (Approved Oct. 1, 2006.)(1) Table 3 was revised.Committee B05 has identified the location of selected
47、changes to this standard since the last issue (B570 05)that may impact the use of this standard. (Approved Oct. 1, 2005.)(1) Table 3 was revised.Committee B05 has identified the location of selected changes to this standard since the last issue (B570 01)that may impact the use of this standard. (App
48、roved March 1, 2005.)(1) Document was revised to change Elongation in 2 in. toElongation in 43D. (See Table 3.)B570 06 (2010)4ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are e
49、xpressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a me