1、 AEROSPACE STANDARD INSULATION SLEEVING, ELECTRICAL, SHRINKABLE WITHOUT HEAT, POLYURETHANE FLEXIBLE AS85080/3Copyright 2012 SAE International All rights reserved. No part of this publication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mech
2、anical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-4970 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org ISSUED 2004-04STABILI
3、ZED 2012-03 THIRD ANGLE PROJECTION CUSTODIAN: AE-8/AE-8D REV.A FEDERAL SUPPLY CLASS 5970 AS85080/3REV. A PROCUREMENT SPECIFICATION: MIL-I-85080SAE Technical Standards Board Rules provide that: “This report ispublishedby SAE toadvance thestate of technicalandengineering sciences. Theuse ofthis report
4、 is entirely voluntary, andits applicability and suitability forany particular use,including any patent infringement arising therefrom, isthe soleresponsibilityofthe user.”SAE reviews eachtechnicalreport at least every five years at which time itmay berevised, reaffirmed, stabilized, orcancelled. SA
5、E invites yourwrittencomments andsuggestions. SAE values your input. To provide feedbackon this Technical Report, please visit http:/www.sae.org/technical/standards/AS85080/3A RATIONALE THIS DOCUMENT HAS BEEN DETERMINED TO CONTAIN BASIC AND STABLE TECHNOLOGY WHICH IS NOT DYNAMIC IN NATURE. DESIGN AU
6、THORITIES MAY DETERMINE THAT THIS DOCUMENT IS NO LONGER TO BE USED FOR NEW DESIGN. THE PRODUCT IS NOT RECOMMENDED FOR AIRCRAFT APPLICATIONS (SEE AS50881). STABILIZED NOTICE THIS DOCUMENT HAS BEEN DECLARED “STABILIZED” BY THE AE-8D COMMITTEE AND WILL NO LONGER BE SUBJECTED TO PERIODIC REVIEWS FOR CUR
7、RENCY. USERS ARE RESPONSIBLE FOR VERIFYING REFERENCES AND CONTINUED SUITABILITY OF TECHNICAL REQUIREMENTS. NEWER TECHNOLOGY MAY EXIST. Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-NOTICE THIS DOCU
8、MENT HAS BEEN TAKEN DIRECTLY FROM U.S. MILITARY SPECIFICATION MIL-I-85080/3(AS), NOTICE 1 AND CONTAINS ONLY MINOR EDITORIAL AND FORMAT CHANGES REQUIRED TO BRING IT INTO CONFORMANCE WITH THE PUBLISHING REQUIREMENTS OF SAE TECHNICAL STANDARDS. THE INITIAL RELEASE OF THIS DOCUMENT IS INTENDED TO REPLAC
9、E MIL-I-85080/3(AS), NOTICE 1. ANY PART NUMBERS ESTABLISHED BY THE ORIGINAL SPECIFICATION REMAIN UNCHANGED. THE ORIGINAL MILITARY SPECIFICATION WAS ADOPTED AS AN SAE STANDARD UNDER THE PROVISIONS OF THE SAE TECHNICAL STANDARDS BOARD (TSB) RULES AND REGULATIONS (TSB 001) PERTAINING TO ACCELERATED ADO
10、PTION OF GOVERNMENT SPECIFICATIONS AND STANDARDS. TSB RULES PROVIDE FOR (A) THE PUBLICATION OF PORTIONS OF UNREVISED GOVERNMENT SPECIFICATIONS AND STANDARDS WITHOUT CONSENSUS VOTING AT THE SAE COMMITTEE LEVEL, AND (B) THE USE OF THE EXISTING GOVERNMENT SPECIFICATION OR STANDARD FORMAT. UNDER DEPARTM
11、ENT OF DEFENSE POLICIES AND PROCEDURES, ANY QUALIFICATION REQUIREMENTS AND ASSOCIATED QUALIFIED PRODUCTS LISTS ARE MANDATORY FOR DOD CONTRACTS. ANY REQUIREMENT RELATING TO QUALIFIED PRODUCTS LISTS (QPLS) HAS NOT BEEN ADOPTED BY SAE AND IS NOT PART OF THIS TECHNICAL REPORT. AEROSPACE STANDARD AS85080
12、/3SHEET OF 3 REV. A INSULATION SLEEVING, ELECTRICAL, SHRINKABLE WITHOUT HEAT, POLYURETHANE FLEXIBLE 1Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-AEROSPACE STANDARD AS85080/3SHEET 2 OF 3 REV. A IN
13、SULATION SLEEVING, ELECTRICAL, SHRINKABLE WITHOUT HEAT, POLYURETHANE FLEXIBLE REQUIREMENTS: CONTINUOUS OPERATING TEMPERATURE RANGE: -55C (-67F) TO +125C (+257F). MODE OF SHRINKAGE: THE HEATLESS SHRINK TUBING SHALL RECOVER TO A PREDETERMINED DIAMETER UPON EXPOSURE TO THE ATMOSPHERE. NO EXTERNAL SOURC
14、ES OF HEAT ARE REQUIRED. COLOR: THE TUBING SHALL BE FURNISHED IN BLACK, WHITE OR CLEAR AS STANDARD COLORS. COLORS SHALL CONFORM TO THE REQUIREMENTS OF CLASS II OF MIL-STD-104. LONGITUDINAL CHANGE: 10 PERCENT. MILITARY PART NUMBER: THE MILITARY PART NUMBER SHALL CONSIST OF THE BASIC NUMBER OF THIS SP
15、ECIFICATION SHEET AND DASH NUMBERS AS SHOWN BELOW: M85080/3 - X XX - X | | | | _ COLOR CODE DESIGNATOR (SEE 1.2.2) | | | | | | _ SIZE IDENTIFIER (TABLE I) | | | |_ CLASS (WHERE NO CLASSES ARE | SPECIFIED, THE NUMERIC “0“ | SHALL BE USED) | |_ SPECIFICATION SHEET EXAMPLE: WHITE, 0.506 INCH AS SUPPLIE
16、D I.D. SLEEVING SHALL BE IDENTIFIED AS M85080/3-007-9. TABLE I. DIMENSIONS (INCHES) 1/ AFTER UNRESTRICTED SHRINKAGE MILITARY PART NUMBER 2/ AS SUPPLIED I.D. MIN 3/ I.D. MAX WALL THICKNESS 4/ M85080/3-001-X M85080/3-002-X M85080/3-003-X M85080/3-004-X M85080/3-005-X M85080/3-006-X M85080/3-007-X M850
17、80/3-008-X M85080/3-009-X M85080/3-010-X M85080/3-011-X 0.042 0.084 0.126 0.170 0.252 0.338 0.506 0.675 0.843 1.012 1.350 0.031 0.062 0.093 0.125 0.187 0.250 0.375 0.500 0.625 0.750 1.000 0.015 0.020 0.020 0.020 0.020 0.025 0.025 0.030 0.030 0.035 0.040 1/ DIAMETER LIMITS FOR OBJECT TO BE ENCLOSED S
18、HOULD BE IN ACCORDANCE WITH THE RECOMMENDATIONS OF THE MANUFACTURER. 2/ THE COLOR CODE IDENTIFIED SHALL BE REPLACED BY THE COLOR CODE FROM 1.2.2. 3/ THE INNER DIAMETER OF THE SLEEVE MAY BE MECHANICALLY EXPANDED 2X THE RECOVERED INSIDE DIAMETER WHEN IN THE AS-SUPPLIED CONDITION. THE MANUFACTURER SHOU
19、LD BE CONSULTED FOR SPECIAL APPLICATIONS AND RECOMMENDATIONS. 4/ WALL SHRINKAGE WILL BE LESS IF SHRINKAGE IS RESTRICTED. UNRESTRICTED SHRINKAGE: 4.6.3.12; 23 1C (73.4 2F) FOR 24 HOURS. Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permi
20、tted without license from IHS-,-,-AEROSPACE STANDARD AS85080/3SHEET 3 OF 3REV. AINSULATION SLEEVING, ELECTRICAL, SHRINKABLE WITHOUT HEAT, POLYURETHANE FLEXIBLE TABLE II. PROPERTIES AFTER UNRESTRICTED SHRINKAGE. PROPERTY REQUIREMENT TEST CONDITION RESTRICTED SHRINKAGE VOLTAGE WITHSTAND DIELECTRIC STR
21、ENGTH, VOLTS PER MIL MIN VOLUME RESISTIVITY, OHM-CM, MIN WATER ABSORPTION, % MAX FUNGUS RESISTANCE LOW TEMPERATURE FLEX HEAT SHOCK PROPERTIES AFTER HEAT RESISTANCE TEST: TENSILE STRENGTH, PSI, MIN ULTIMATE ELONGATION, %, MIN CORROSION PROPERTIES AFTER FLUID RESISTANCE TEST: TENSILE STRENGTH, PSI, MI
22、N ULTIMATE ELONGATION, %, MIN ODOR TENSILE STRESS, AT 200% ELONGATION, PSI, MAX TENSILE STRENGTH, PSI, MIN ULTIMATE ELONGATION, %, MIN FLAMMABILITY NO CRACKS PASS50010111.0NON NUTRIENT NO CRACKING NO CRACKS, FLOWING OR DRIPPING 800400NO CORROSION OR PITTING 2000300NO OBJECTION- ABLE ODOR 10001000300
23、SELF EXTINGUISHING; ONE MINUTE MAX. NO MORE THAN 25% OF IN- DICATOR FLAG BURNED. 4.6.3.24.6.64.6.2; ASTM D 876 4.6.2; ASTM D 876 4.6.2; ASTM D 570, PAR 6.1 4.6.2; ASTM G 21 4.6.6; -55 2C (-67 5F) 4.6.7; 160 1C (320 2F) 4.6.8; 125 1C (258 2F) FOR 96 HOURS. 4.6.94.6.104.6.114.6.2 ASTM D 412 4.6.13 AST
24、M D 638 SPEED D 4.6.13 ASTM D 638 SPEED D 4.6.14.1SHELF LIFE (AS SUPPLIED): TEST METHOD 4.6.16. MIL-I-85080/3(AS) IS INACTIVE FOR NEW DESIGN AND IS NO LONGER USED, EXCEPT FOR REPLACEMENT PURPOSES. Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-