1、CARBON FIBER TAPE AND SHEETPolysulfone Resin ImpregnatedC PS 140 (965) Tensile, 27 (186) Modulus, 120 (248)SAESAEAMS 3899/2BIssued 15 APR 1980Revised 1 OCT 1993Superseding AMS 3899/2AAEROSPACEMATERIALSPECIFICATIONSAESAEThe Engineering SocietyFor Advancing MobilityLand Sea Air and Space400 Commonweal
2、th Drive, Warrendale, PA 15096-0001INTERNATIONALSubmitted for recognition as an American National StandardSAE Technical Board Rules provide that: “This report is published by SAE to advance the state of technical and engineeringsciences. The use of this report is entirely voluntary, and its applicab
3、ility and suitability for any particular use, including any patent infringementarising therefrom, is the sole responsibility of the user.”SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your writtencomments and sugges
4、tions.Copyright 1993 Society of Automotive Engineers, Inc.All rights reserved. PrintedinU.S.A.1. SCOPE:1.1 Form:This specification covers one type of thermoplastic,polysulfone-resin-impregnated carbon fibers in the form of tape or sheet.1.2 Application:These products have been used typically in stru
5、ctural composites requiringhigh modulus of elasticity in tension up to 120 C (248 F), but usage is notlimited to such applications.1.3 Classification:C PS 140 ksi (965 MPa) tensile strength, 27 Msi (186 GPa) tensile moduluscarbon fiber impregnated with polysulfone resin for service up to 120 C(248 F
6、).2. APPLICABLE DOCUMENTS:See AMS 3899.3. TECHNICAL REQUIREMENTS:3.1 Basic Specification:The complete requirements for producing the product described herein shallconsist of this document and the latest issue of the basic specification,AMS 3899.Copyright SAE International Provided by IHS under licen
7、se with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-SAE AMS 3899/2BAMS 3899/2B3.2 Material:The product shall be AMS 3892/2 high-modulus carbon fibers impregnated withheat-reactive, thermoplastic, polysulfone resin formulated to meet therequirements specified h
8、erein.3.2.1 Storage Life: The product shall meet the requirements of thisspecification when tested at any time up to one year from date of receiptby purchaser, provided it has been stored at room temperature in theoriginal containers.3.3 Properties:The product shall conform to the following requirem
9、ents:3.3.1 Resin-Impregnated Fiber Tape and Sheet: Shall be as specified below; testshall be performed on the as-supplied product and in accordance with testmethods listed in the basic specification, AMS 3899.3.3.1.1 Volatile Content by Weight: Shall be 5% maximum when tested at260 C 5 (500 F 9) for
10、 30 minutes 5.3.3.1.2 Total Resin Solids Content by Weight: Shall be 34% 3.3.3.1.3 Resin Flow by Weight: Shall be 4.0% maximum.3.3.2 Molded Laminates: Shall be determined on specimens cut from a test panelprepared as specified in the basic specification and tested in accordancewith test methods spec
11、ified therein.3.3.2.1 Mechanical Properties: Shall be as specified in Table 1.3.3.2.2 Density: Shall be determined on each test panel used to determinemechanical properties; values shall be reported. Fiber density and resindensity shall also be reported.3.3.2.3 Void Content: Shall be not greater tha
12、n 4%.4. QUALITY ASSURANCE PROVISIONS:See AMS 3899.5. PREPARATION FOR DELIVERY:See AMS 3899.6. ACKNOWLEDGMENT:See AMS 3899.- 2 -Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-SAE AMS 3899/2BAMS 3899/2B
13、7. REJECTIONS:See AMS 3899.8. NOTES:See AMS 3899.- 3 -Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-SAEAMS3899/2BAMS3899/2BValue(A)TestTemperature(B)120 C 5(248 F 9)MPa896TBR158,579TBR414172,36968914
14、4,79034.5Value(A)TestTemperature(B)120 C 5(248 F 9)psi130,000TBR23.0 x 106TBR60,00025 x 106100,00021 x 1065,000Value(A)TestTemperature(B)20 to 30 C(68 to 86 F)MPa965TBR186,158TBR621186,158862151,68548.3Value(A)TestTemperature(B)20 to 30 C(68 to 86 F)psi140,000TBR27.0 x 106TBR90,00027 x 106125,00022.
15、0 x1067,000Value(A)TestTemperature(B)-55 C 5(-67 F 9)MPaTBRTBRTBRTBRTBRTBRNANATBRValue (A)TestTemperature(B)-55 C 5(-67 F 9)psiTBR(D)TBRTBRTBRTBRTBRNA(E)NATBRTABLE 1 - Minimum Mechanical Properties of Prepared LaminatesPropertyTensile Strength, (C)LongitudinalTransverseTensile Modulus, (C)Longitudin
16、alTransverseCompressive Strength,(C)LongitudinalCompressive Modulus, (C)LongitudinalFlexural Strength, (C)LongitudinalFlexural Modulus, (C)LongitudinalShort Beam ShearStrengthNOTES: A. Average of four determinations per test. No individual value shall be less than 90% of the average valuespecified.B
17、. Test after 30 minutes 1 exposure at the test temperature.C. Property values are based on a test laminate with a fiber volume of 57% 3. Certain property values may beadjusted for other fiber volumes of the test laminate by multiplying the listed requirement by the ratio:Actual Fiber Volume, %/57. W
18、hen such adjustment is used, report the actual fiber volume of the test laminate.D. TBR - To be reported in preproduction test report.E. NA - Not applicable.- 4 -Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-