1、105 Decker Court, Suite 825, Irving, TX 75062 P: 469-499-1044 F: 469-499-1063 www.plasticpipe.org Mechanical Couplings for Joining Polyethylene Pipe TN-45/2012 Foreword This report was developed and published with the technical help and financial support of the members of the PPI (Plastics Pipe Inst
2、itute, Inc.). The members have shown their interest in quality products by assisting independent standards-making and user organizations in the development of standards, and also by developing reports on an industry-wide basis to help engineers, code officials, specifying groups, and users. The purp
3、ose of this technical report is to provide important information available to PPI on a particular aspect of polyethylene pipe butt fusion to engineers, users, contractors, code officials, and other interested parties. More detailed information on its purpose and use is provided in the document itsel
4、f. This report has been prepared by PPI as a service of the industry. The information in this report is offered in good faith and believed to be accurate at the time of its preparation, but is offered “as is” without any express or implied warranty, including WARRANTIES OF MERCHANTABILITY AND FITNES
5、S FOR A PARTICULAR PURPOSE. Consult the manufacturer for more detailed information about the particular joining procedures to be used with its piping products. Any reference to or testing of a particular proprietary product should not be construed as an endorsement by PPI, which does not endorse the
6、 proprietary products or processes of any manufacturer. The information in this report is offered for consideration by industry members in fulfilling their own compliance responsibilities. PPI assumes no responsibility for compliance with applicable laws and regulations. PPI intends to revise this r
7、eport from time to time, in response to comments and suggestions from users of the report. Please send suggestions of improvements to the address below. Information on other publications can be obtained by contacting PPI directly or visiting the web site. The Plastics Pipe Institute, Inc. www.plasti
8、cpipe.org October 2012 105 Decker Court, Suite 825, Irving, TX 75062 P: 469-499-1044 F: 469-499-1063 www.plasticpipe.org MECHANICAL COUPLINGS FOR JOINING POLYETHYLENE PIPE 1.0 Introduction The use of polyethylene piping material has steadily increased over the past half century and today its the mat
9、erial of choice for natural gas piping systems up to 12” size. Mechanical couplings and fittings played a vital part in this evolution, especially in the earlier years, when distribution service line installations were the most common application. Many of these mechanical fittings were metallic and
10、connected to steel or cast iron main piping with a PE outlet connection for the service line. Both plastic and metallic mechanical fittings have provided the industry with fast and easy pipe joining, and repair and transition techniques. Their nearly 50 years of performance history is testimonial to
11、 the safe and reliable service these fittings provide. This document will provide a historical time line to assist material engineers, when assessing older PE systems, and to determine what the governing requirements were for mechanical fittings at the time of their installations. It will also revie
12、w the specified regulatory requirements for mechanical pipe joints, both in general terms and how they should be interpreted for mechanical joints for PE piping. An outline of recommended mechanical fitting performance capabilities will be provided to assist material engineers in product selection.
13、It includes any ASTM Test Methods or Standard Specifications available to provide guidance in how to evaluate the performance capability of mechanical fittings. Some of the most common types of mechanical fittings will generically be described. Some mechanical fitting designs are proprietary to a sp
14、ecific manufacturer. Use recommendations and compliance to regulations should be reviewed with the fitting manufacturer prior to installation. Mechanical fittings do not require highly skilled laborers and typically do not require special equipment to be installed. With each design, it is essential
15、that the manufacturers installation instructions are followed to obtain optimum performance. 2.0 Definition/Designs There are primarily five different mechanical coupling designs or technologies for joining PE currently in use in North America. All require the use of an internal stiffener when used
16、with PE pipe to prevent long-term creep of the pipe away from the compression forces. These designs can be classified by the method used for completion. These are: Tightening of bolts and nuts Tightening of compression nut (also referred to as “nut follower”). Stab or insertion style Hydraulic press
17、ure Use of an external compression or “completion” ring Tightening of Bolts This design is characterized by the use of multiple bolts and nuts being tightened to grip and seal on the polyethylene (figures 1a, 1b). These types of mechanical couplings can also be used to join polyethylene to steel or
18、cast iron gas piping, or ductile iron water piping. The tightening of the bolts brings together internal gripping rings and a sealing element. As the bolts are tightened, the outer ring, commonly called the retaining ring, forces the gripping mechanism or ring and sealing gasket into a state of comp
19、ression onto the polyethylene, thus creating restraint and a gas tight seal. The tightening of nuts and bolts is to a specified torque value prescribed by the manufacturers installation instructions. Tightening of Compression Nut (Nut Follower) With this design, the operator is required to tighten a
20、 nut to a stop or prescribed torque value. As with the “bolt” design fitting, as the operator tightens the nut down, the internal gripping ring and sealing gasket are brought down onto the polyethylene pipe to restrain and seal. In some designs, there is a prescribed torque value, however in others;
21、 the operator is required to tighten the fitting to a stop point located on the coupling body. The gas seal and restraint (grip) are dependent upon the amount of tightness the operator applies to the compression nut. Examples of compression nut style couplings are depicted in figures 2a and 2b below
22、. Figure 1a Steel body, bolt together coupling Figure 2b Nylon body compression coupling Figure 2a Cast body compression coupling Figure 1b Plastic body, bolt together coupling Stab or Insertion The “stab” or insertion style coupling requires no tightening of bolts or compression nut. With the stab
23、type, the seal and restraint are accomplished through independent components. The coupling contains either single or multiple rubber orings that provide a seal on the outside diameter, inside diameter or both diameters of the polyethylene tubing which has been inserted into the fitting. In the case
24、of an outside diameter seal fitting, the inside diameter of oring is smaller than that of the outside diameter of the polyethylene tubing, thus compressing the rubber oring onto the PE tubing surface and coupling body surface creating a gas tight seal. Likewise, for the inside diameter sealing coupl
25、ing version, the sealing oring would have a larger diameter than the inside diameter of the tubing, again, compressing the tubing wall to the oring creating a gas seal. Hydraulic Pressure This type of joining method is no longer commonly used on polyethylene, however because there may exist product
26、in the operators system we review the technology here. This type of coupling involves a steel body product with two hydraulic port holes. Internally, there are gripping plates and seals that are forced onto the piping via hydraulic fluid pressure. Use of this fitting requires that the operator use a
27、nd maintain a hydraulic pump. The hydraulic hose is attached to the fitting body and hydraulic fluid is pumped into the fitting body thus forcing the gripper and sealing mechanisms onto the pipe. Fluid pressure is measured on a pressure gauge attached to the pump. Installation pressure is predetermi
28、ned by the manufacturer and detailed in the installation instructions. Figure 3 Polyethylene stab type coupling Figure 4 Hydraulic style coupling External Compression Ring For the mechanical coupling using an external compression or “completion” ring, the operator inserts the polyethylene over an in
29、sert stiffener. The insert stiffener may or may not be integral to the fitting body and can be smooth or serrated. Prior to this step, the operator slides the compression ring over the outside of the polyethylene tubing. After the polyethylene has been inserted, the compression ring is brought over
30、the coupling body and/or polyethylene. This interference fit creates a compressive force between the polyethylene and the insert stiffener. The assembly typically requires the use of a special tool to bring the compression ring onto the fitting body. This design may or may not contain an elastomeric
31、 sealing element, in some designs the compression of the PE onto the griping element and/or internal stiffener also creates the seal. Assembly is complete when the compression ring has been brought into contact with a stop on the coupling. 3.0 Compression Couplings Background When plastic pipe was f
32、irst designed and developed for the natural gas distribution industry in the 1960s, the dimensions were called IPS and CTS or Iron Pipe Size and Copper Tubing Size. The outside diameter (OD) of IPS pipe was based on the corresponding iron pipe outside diameter so that the same fittings that were use
33、d for metal pipe could also be used for plastic pipe. For example, nominal 2” IPS PE pipe has an outside diameter of 2.375”, which is the OD of metal pipe. When mechanical compression couplings were first used for plastic gas pipe in the early 1960s they provided a leak-tight seal only, and this sea
34、l was based on the OD dimensions. These first compression couplings, which were originally designed for metal pipe, provided the necessary gas-tight seal, but did not provide resistance (restraint) to pull out. As the use of plastic pipe and particularly PE pipe, increased, the compression coupling
35、manufacturers began to design their couplings specifically for plastic pipe. In the case of PE pipe, this included an insert stiffener to provide the needed rigidity to the PE to improve the required seal. By the late 1960s, some compression coupling manufacturers also began to design their fittings
36、 with pullout Figure 5 External Compression Ring style coupling resistance in addition to leak-tight seals. By 1980, there were several manufacturers that sold compression couplings that provided both a leak-tight seal and gripping mechanisms that provided pullout restraint. In their 1972 report, “C
37、omparison of Long-Term Sealing Characteristics of Compression Type Couplings on Steel & Polyethylene Pipe” Dresser Manufacturing stated, “A new mechanical design was initiated to develop a mechanical joint for PE. Requirements were obviously long-term reliable sealing ability and a joint locking str
38、ength equal to the longitudinal strength of the plastic pipe being joined, as required by (our interpretation) the DOT regulations Volume 35, number 61, paragraph 192.273 (a)”. This statement indicates that Dresser Manufacturing interpreted the code as meaning that a compression coupling needed to h
39、ave restraint to pullout and they were manufacturing couplings to meet that requirement. The mechanical couplings manufactured by Dresser in sizes 2” IPS and below had a locking feature to prevent pullout. This had been the industry standard since the late 1960s. In the late 1970s as a result of two
40、 compression fitting pullout failures in Fremont, Nebraska and Lawrence, Kansas, the DuPont Company published an article, “Pull Out Forces on Joints in PE (Polyethylene) Pipe Systems”, in which the joint strength for compression fittings ” to 1” was deemed “equal or greater” than pipe strength. DuPo
41、nt deemed compression fittings larger than 1” to have joint strength “less” than pipe strength. As a result of several more industry gas pipeline failures due to PE pipe pulling out of a non-restraint compression coupling, some manufacturers now include caution statements in their literature, such a
42、s, “When pipe pullout could occur as a result of forces other than that caused by internal line pressure of 150 psig maximum, pipe joint MUST be anchored. Failure to anchor pipe joint could result in escaping line content and cause property damage, serious injury or death”. 4.0 Industry Codes/Standa
43、rds for Mechanical Couplings I. DOT Part 192 The key section dealing with compression couplings in the original DOT Part 192 was Part 192.273, which required that “the pipeline must be designed and installed so that each joint will sustain the longitudinal pullout or thrust forces caused by contract
44、ion or expansion of the piping or by anticipated external or internal loading.” Other sections of Part 192 that affect compression coupling design and installation are 192.143, 192.161, and 192.321. Also, DOT Part 192.703 requires that each segment of pipeline that becomes unsafe must be replaced. I
45、n 1980, after the Fremont, Nebraska and Lawrence, Kansas compression coupling pullout incidents, Part 192 was revised to incorporate additional mechanical joint requirements in Part 192.283. These new requirements included procedures for qualifying joining procedures for mechanical joints and qualif
46、ying person to make such joints, including a pullout test that requires the pipe to neck down with at least 25% elongation to qualify the joining procedure. II. AGA Plastic Pipe Manual The industry document that the gas companies rely on the most for general guidelines on installing plastic pipe is
47、the AGA Plastic Pipe Manual. This manual is prepared by plastics piping experts in the AGA Plastic Materials Committee, both gas companies and manufacturers, to assist the users with proper installation and maintenance of plastic pipe. The original 1977 AGA Manual references DOT Part 192.273 and sta
48、tes, “The installed joint must effectively sustain longitudinal pullout or thrust forces caused by contraction or expansion of the piping or by anticipated external or internal loading. Such provision may be made in the design of the joint or in the installation or a combination of both”. The 1977 A
49、GA Manual also states, “Earth movement, ground movement and third party construction activity can impose stresses on the pipe which can be transmitted to joints. In most situations it is desirable to have pipe joints which are as strong as the pipe itself in the axial (longitudinal) direction. Mechanical joints not specifically designed for use with plastic pipe may not provide complete resistance to pullout.” Later versions of the AGA Plastic Pipe Manual were updated to reflect the new mechanical joint requirements in DOT Part 192.283. III. ASTM F17 The in